Sulfonate-Containing Polyelectrolytes for Perovskite Modification: Chemical Configuration, Property, and Performance.

Three sulfonate-containing polyelectrolytes are elaborately designed and used to passivate perovskite film with the anti-solvent method. Under the influence of the secondary monomer, three copolymers present various chemical configurations and deliver different modification effects. Fluorene-thiophene copolymer STF has linear and highly-conjugated chain. STF-perovskite film presents large crystal grains. Fluorene-carbazole copolymer SCF has flexible chain and easily enters into grain boundary areas. SCF-perovskite film is homogenous and continuous. Fluorene-fluorene copolymer SPF agglomerates on the surface and is not applicable to the anti-solvent method. The full investigation demonstrates that STF and SCF not only conduct surface defect passivation, but also improve the film quality by being involved in the perovskite's crystallization process. Compared with the control device, the devices with STF and SCF deliver high efficiency and excellent stability. The unencapsulated devices with STF and SCT maintain ≈80% of the initial power conversion efficiency (PCE) after 40 days of storage under 30-40% relative humidity. SCF performs better and the device maintains 60% of the initial PCE after 20 days of storage under 60-80% relative humidity.

Fully bio-based intumescent flame retardant hybrid: A green strategy towards reducing fire hazard and improving degradation of polylactic acid.

Polylactic acid (PLA) is a promising renewable polymer material with excellent biodegradability and good mechanical properties. However, the easy flammability and slow natural degradation limited its further applications, especially in high-security fields. In this work, a fully bio-based intumescent flame-retardant system was designed to reduce the fire hazard of PLA. Firstly, arginine (Arg) and phytic acid (PA) were combined through electrostatic ionic interaction, followed by the introduction of starch as a carbon source, namely APS. The UL-94 grade of PLA/APS composites reached V-0 grade by adding 3 wt% of APS and exhibited excellent anti-dripping performance. With APS addition increasing to 7 wt%, LOI value increased to 26 % and total heat release decreased from 58.4 (neat PLA) to 51.1 MJ/m2. Moreover, the addition of APS increased its crystallinity up to 83.5 % and maintained the mechanical strength of pristine PLA. Noteworthy, APS accelerated the degradation rate of PLA under submerged conditions. Compared with pristine PLA, PLA/APS showed more apparent destructive network morphology and higher mass and Mn loss, suggesting effective degradation promotion. This work provides a full biomass modification strategy to construct renewable plastic with both good flame retardancy and high degradation efficiency.