Injectable Hybrid-Crosslinked Hydrogels as Fatigue-Resistant and Shape-Stable Skin Depots.

Injectable hydrogels have gained considerable attention, but they are typically mechanically weak and subject to repeated physiological stresses in the body. Herein, we prepared polyurethane diacrylate (EPC-DA) hydrogels, which are injectable and can be photocrosslinked into fatigue-resistant implants. The mechanical properties can be tuned by changing photocrosslinking conditions, and the hybrid-crosslinked EPC-DA hydrogels exhibited high stability and sustained release properties. In contrast to common injectable hydrogels, EPC-DA hydrogels exhibited excellent antifatigue properties with >90% recovery during cyclic compression tests and showed shape stability after application of force and immersion in an aqueous buffer for 35 days. The EPC-DA hydrogel formed a shape-stable hydrogel depot in an ex vivo porcine skin model, with establishment of a temporary soft gel before in situ fixing by UV crosslinking. Hybrid crosslinking using injectable polymeric micelles or nanoparticles may be a general strategy for producing hydrogel implants resistant to physiological stresses.

High molecular weight hyper-branched PCL-based thermogelling vitreous endotamponades.

Vitreous endotamponades play essential roles in facilitating retina recovery following vitreoretinal surgery, yet existing clinically standards are suboptimal as they can cause elevated intra-ocular pressure, temporary loss of vision, and cataracts while also requiring prolonged face-down positioning and removal surgery. These drawbacks have spurred the development of next-generation vitreous endotamponades, of which supramolecular hydrogels capable of in-situ gelation have emerged as top contenders. Herein, we demonstrate thermogels formed from hyper-branched amphiphilic copolymers as effective transparent and biodegradable vitreous endotamponades for the first time. These hyper-branched copolymers are synthesised via polyaddition of polyethylene glycol, polypropylene glycol, poly(ε-caprolactone)-diol, and glycerol (branch inducing moiety) with hexamethylene diisocyanate. The hyper-branched thermogels are injected as sols and undergo spontaneous gelation when warmed to physiological temperatures in rabbit eyes. We found that polymers with an optimal degree of hyper-branching showed excellent biocompatibility and was able to maintain retinal function with minimal atrophy and inflammation, even at absolute molecular weights high enough to cause undesirable in-vivo effects for their linear counterparts. The hyper-branched thermogel is cleared naturally from the vitreous through surface hydrogel erosion and negates surgical removal. Our findings expand the scope of polymer architectures suitable for in-vivo intraocular therapeutic applications beyond linear constructs.