MDP-based universal adhesive system irradiated with Er,CR:YSGG: Analysis of its performance up to 6 months.

This study aimed to analyze the interaction of a MDP-based universal dentin bonding system (DBS) with Er, Cr: YSGG laser irradiation, measuring the microtensile bond strength to dentin over a six-month period. The experimental design involved three factors: DBS (Adper Scotchbond Universal; Clearfil SE Bond, Adper Scotchbond Multipurpose and Adper Single Bond 2), laser (Control and Er, Cr: YSGG), and time (initial- 7 days and 6 months). Eighty dentin samples from molars were prepared (n=10) with laser irradiation after primer and DBS application. After 7 days, were subjected to micro tensile bond strength test. The data were analyzed by three-way ANOVA and Tukey tests (p<0.05). Both DBS and laser significantly affected the bonding performance and their interaction was statistically significant (p=0.0194). The self-etching mode of the MDP-based universal DBS maintained the bond strength on dentin irradiated with ER, Cr: YSGG after 6 months, while bonding with all other DBS deteriorated.

The influence of fillers and protease inhibitors in experimental resins in the protein profile of the acquired pellicle formed in situ on enamel-resin specimens.

OBJECTIVE: This study evaluated the influence of the addition of fillers and/or protease inhibitors [(epigallocatechin gallate - EGCG) or (chlorhexidine - CHX)] in experimental resins in the protein profile of the acquired pellicle (AP) formed in situ on enamel-resin specimens. DESIGN: 324 samples of bovine enamel were prepared (6 × 6 × 2 mm). The center of each sample was added with one of the following experimental resins (Bis-GMA+TEGDMA): no filler, no inhibitor (NF-NI); filler no inhibitor (F-NI); no filler plus CHX (NF-CHX); filler plus CHX (F-CHX); no filler plus EGCG (NF-EGCG); filler plus EGCG (F-EGCG). Nine subjects used a removable jaw appliance (BISPM - Bauru in situ pellicle model) with 2 slabs from each group. The AP was formed for 120 min, in 9 days and collected with electrode filter paper soaked in 3% citric acid. The pellicles collected were processed for analysis by LC-ESI-MS/MS. RESULTS: A total of 140 proteins were found in the AP collected from all the substrates. Among them, 16 proteins were found in common in all the groups: 2 isoforms of Basic salivary proline-rich protein, Cystatin-S, Cystatin-AS, Cystatin-SN, Histatin-1, Ig alpha-1 chain C region, Lysozyme C, Mucin-7, Proline-rich protein 4, Protein S100-A9, Salivary acidic proline-rich phosphoprotein ½ and Statherin. Proteins with other functions, such as metabolism and transport, were also identified. CONCLUSION: The composition of the experimental resins influenced the protein profile of the AP. This opens a new avenue for the development of new materials able to guide for AP engineering, thus conferring protection to the adjacent teeth.

Effect of diode laser irradiation on the bond strength of polymerized non-simplified adhesive systems after 12 months of water storage.

OBJECTIVES: The aim of this in vitro study was to evaluate the bonding strength of non-simplified dentin bonding systems (DBS) to dentin irradiated with a diode laser (970 nm) immediately and after 12 months of water storage following either primer or bond application. MATERIAL AND METHODS: The experimental design included three different factors: DBS type [AdperTM Scotchbond Multipurpose (MP) and Clearfil™ SE Bond (CSE)], irradiation [without irradiation - control (C), irradiation after primer application (AP), and irradiation after bond application (AB)], and time [initial (I) and after 12 months of water storage (12 m)]. Sixty sound human third molars (n = 10) were obtained, and their flat occlusal dentin areas were prepared and standardized. Laser irradiation was performed in the contact mode perpendicular to the dental surface over an automatically selected scanning area at a pulse energy of 0.8 W, frequency of 10 Hz, and energy density of 66.67 J/cm2. After 7 days of treatment, the specimens were cut, and half of them were subjected to microtensile testing (500 N/0.05 mm/min), whereas the remaining sticks were examined after 12 months of water storage. The obtained data were analyzed by three-way analysis of variance (ANOVA) followed by a Tukey test (p<0.05). The observed fracture modes were investigated using a portable digital microscope with a magnification of 40x. RESULTS: Among the utilized DBS, MP generally exhibited higher bond strengths, but did not always differ from CSE under similar conditions. The irradiation factor was statistically significant only for the MP/AB groups. After 12 months of storage, all groups demonstrated a significant reduction in the bond strength, whereas the results of fracture analysis showed a predominance of the adhesive type. CONCLUSIONS: The laser treatment of non-simplified DBS was not able to stabilize their bonding characteristics after 12 months.