Free Standing Dry and Stable Nanoporous Polymer Films Made through Mechanical Deformation.

A new straight forward approach to create nanoporous polymer membranes with well defined average pore diameters is presented. The method is based on fast mechanical deformation of highly entangled polymer films at high temperatures and a subsequent quench far below the glass transition temperature Tg . The process is first designed generally by simulation and then verified for the example of polystyrene films. The methodology does not need any chemical processing, supporting substrate, or self assembly process and is solely based on polymer inherent entanglement effects. Pore diameters are of the order of ten polymer reptation tube diameters. The resulting membranes are stable over months at ambient conditions and display remarkable elastic properties.

Elastic Modulus and Thermal Conductivity of Thiolene/TiO2 Nanocomposites.

Metal oxide based polymer nanocomposites find diverse applications as functional materials, and in particular thiol-ene/TiO2 nanocomposites are promising candidates for dental restorative materials. The important mechanical and thermal properties of the nanocomposites, however, are still not well understood. In this study, the elastic modulus and thermal conductivity of thiol-ene/TiO2 nanocomposite thin films with varying weight fractions of TiO2 nanoparticles are investigated by using Brillouin light scattering spectroscopy and 3ω measurements, respectively. As the TiO2 weight fraction increases from 0 to 90%, the effective elastic longitudinal modulus of the films increases from 6.2 to 37.5 GPa, and the effective thermal conductivity from 0.04 to 0.76 W/m K. The former increase could be attributed to the covalent cross-linking of the nanocomposite constituents. The latter one could be ascribed to the addition of high thermal conductivity TiO2 nanoparticles and the formation of possible conductive channels at high TiO2 weight fractions. The linear dependence of the thermal conductivity on the sound velocity, reported for amorphous polymers, is not observed in the present nanocomposite system.