Aripiprazole-montmorillonite: a new organic-inorganic nanohybrid material for biomedical applications.

Poor aqueous solubility and the unpleasant taste of aripiprazole (APZ) have been recurring problems, owing to its low bioavailability and low patient tolerance, respectively. Herein, we prepared a nanohybrid system that was based on a bentonite clay material, montmorillonite (MMT), which could both mask the taste and enhance the solubility of APZ (i.e., APZ-MMT). To further improve the efficacy of this taste masking and drug solubility, APZ-MMT was also coated with a cationic polymer, polyvinylacetal diethylamino acetate (AEA). In vitro dissolution tests at neutral pH showed that the amount of drug that was released from the AEA-coated APZ-MMT was greatly suppressed (<1%) for the first 3 min, thus suggesting that AEA-coated APZ-MMT has strong potential for the taste masking of APZ. Notably, in simulated gastric juice at pH 1.2, the total percentage of APZ that was released within the first 2 h increased up to 95% for AEA-coated APZ-MMT. Furthermore, this in vitro release profile was also similar to that of Abilify®, a commercially available medication. In vivo experiments by using Sprague-Dawley rats were also performed to compare the pharmacokinetics of AEA-coated APZ-MMT and Abilify®. AEA-coated APZ-MMT exhibited about 20% higher systemic exposure of APZ and its metabolite, dehydro-APZ, compared with Abilify®. Therefore, a new MMT-based nanovehicle, which is coated with a cationic polymer, can act as a promising delivery system for both taste masking and for enhancing the bioavailability of APZ.

A nanohybrid system for taste masking of sildenafil.

A nanohybrid was prepared with an inorganic clay material, montmorillonite (MMT), for taste masking of sildenafil (SDN). To further improve the taste-masking efficiency and enhance the drug-release rate, we coated the nanohybrid of SDN-MMT with a basic polymer, polyvinylacetal diethylaminoacetate (AEA). Powder X-ray diffraction and Fourier transform infrared experiments showed that SDN was successfully intercalated into the interlayer space of MMT. The AEA-coated SDN-MMT nanohybrid showed drug release was much suppressed at neutral pH (release rate, 4.70 ± 0.53%), suggesting a potential for drug taste masking at the buccal cavity. We also performed in vitro drug release experiments in a simulated gastric fluid (pH = 1.2) and compared the drug-release profiles of AEA-coated SDN-MMT and Viagra(®), an approved dosage form of SDN. As a result, about 90% of SDN was released from the AEA-coated SDN-MMT during the first 2 hours while almost 100% of drug was released from Viagra(®). However, an in vivo experiment showed that the AEA-coated SDN-MMT exhibited higher drug exposure than Viagra(®). For the AEA-coated SDN-MMT, the area under the plasma concentration- time curve from 0 hours to infinity (AUC(0-∞)) and maximum concentration (C(max)) were 78.8 ± 2.32 µg · hour/mL and 12.4 ± 0.673 µg/mL, respectively, both of which were larger than those obtained with Viagra(®) (AUC(0-∞) = 69.2 ± 3.19 µg · hour/mL; C(max) = 10.5 ± 0.641 µg/mL). Therefore, we concluded that the MMT-based nanohybrid is a promising delivery system for taste masking of SDN with possibly improved drug exposure.

Inorganic-polymer nanohybrid carrier for delivery of a poorly-soluble drug, ursodeoxycholic acid.

Delivery of poorly soluble drugs has been problematic due to its low absorption profile and bioavailability. In this work, ursodeoxycholic acid (UDCA), a poorly-soluble drug, was intercalated into inorganic nanovehicle, layered double hydroxides (LDHs), with a molecular level to enhance its solubility in biological fluid. The UDCA-loaded nanovehicle (i.e., UDCA-LDHs) was also coated with an anionic polymer, Eudragit(®) S100, to increase the dissolution rate of UDCA. According to the powder X-ray diffraction (PXRD) patterns of UDCA-LDHs, the gallery height of LDHs was expanded from 3.6Å to 28.3Å, indicating that the UDCA molecules were successfully intercalated into the interlayer space of LDHs. Fourier transform infrared (FT-IR) spectra also revealed that the UDCA molecules were well stabilized in the LDHs through electrostatic interaction. The in vitro dissolution test in a simulated biological fluid (pH=6.8) showed that the total dissolved fraction of UDCA for the first 2h was about 60.2% for the Eudragit(®) S100 coated UDCA-LDHs, which was a dramatic increase as compared with 19.0% dissolution from intact UDCA. It is, therefore, concluded that LDHs nanovehicle coated with an anionic polymer is a promising delivery system for improving aqueous solubility of poorly soluble drugs.