Fabrication and characterization of Ag- and Ga-doped mesoporous glass-coated scaffolds based on natural marine sponges with improved mechanical properties.

Natural marine sponges were used as sacrificial template for the fabrication of bioactive glass-based scaffolds. After sintering at 1050°C, the resulting samples were additionally coated with a silicate solution containing biologically active ions (Ag and Ga), well-known for their antibacterial properties. The produced scaffolds were characterized by superior mechanical properties (maximum compressive strength of 4 MPa) and total porosity of ~80% in comparison to standard scaffolds made by using PU foam templates. Direct cell culture tests performed on the uncoated and coated samples showed positive results in terms of adhesion, proliferation, and differentiation of MC3T3-E1 cells. Moreover, vascular endothelial growth factor (VEGF) secretion from cells in contact with scaffold dissolution products was measured after 7 and 10 days of incubation, showing promising angiogenic results for bone tissue engineering applications. The antibacterial potential of the produced samples was assessed by performing agar diffusion tests against both Gram-positive and Gram-negative bacteria.

Chitosan/hydroxyapatite composite bone tissue engineering scaffolds with dual and decoupled therapeutic ion delivery: copper and strontium.

Therapeutic metal ions are a family of metal ions characterized by specific biological properties that could be exploited in bone tissue engineering, avoiding the use of expensive and potentially problematic growth factors and other sensitive biomolecules. In this work, we report the successful preparation and characterization of two material platforms containing therapeutic ions: a copper(ii)-chitosan derivative and a strontium-substituted hydroxyapatite. These biomaterials showed ideal ion release profiles, offering burst release of an antibacterial agent together with a more sustained release of strontium in order to achieve long-term osteogenesis. We combined copper(ii)-chitosan and strontium-hydroxyapatite into freeze-dried composite scaffolds. These scaffolds were characterized in terms of morphology, mechanical properties and bioactivity, defined here as the ability to trigger the deposition of novel calcium phosphate in contact with biological fluids. In addition, a preliminary biological characterization using cell line osteoblasts was performed. Our results highlighted that the combination of chitosan and hydroxyapatite in conjunction with copper and strontium has great potential in the design of novel scaffolds. Chitosan/HA composites can be an ideal technology for the development of tissue engineering scaffolds that deliver a complex arrays of therapeutic ions in both components of the composite, leading to tailored biological effects, from antibacterial activity, to osteogenesis and angiogenesis.

Gelatin coating increases in vivo bone formation capacity of three-dimensional 45S5 bioactive glass-based crystalline scaffolds.

Recent studies have demonstrated that surface characteristics, porosity, and mechanical strength of three-dimensional 45S5-type bioactive glass (BG)-based scaffolds are directly correlated with osteogenic properties. Three-dimensional BG-based scaffolds obtained from maritime natural sponges (MNSs) as sacrificial templates exhibit the required morphological properties; however, no in vivo data about the osteogenic features are available. In this study, uncoated (Group A) and gelatin-coated (Group B) crystalline MNS-obtained BG-based scaffolds were evaluated mechanically and seeded with human mesenchymal stem cells prior to subcutaneous implantation in immunodeficient mice. Before implantation and after explantation, micro-computed tomography scans were conducted, and scaffolds were finally subjected to histomorphometry. Scaffolds of both groups showed bone formation. However, Group B scaffolds performed distinctly better as indicated by a significant increase in scaffold volume (8.95%, p = 0.039) over the implantation period compared with a nonsignificant increase of 5.26% in Group A scaffolds in micro-computed tomography analysis. Furthermore, percentage bone area was 10.33% (±1.18%) in the Group B scaffolds, which was significantly (p = 0.007) higher compared with the 8.53% (±0.77%) in the Group A scaffolds in histomorphometry. Compressive strength was enhanced significantly by gelatin coating (9 ± 2 vs. 4 ± 1 MPa; p = 0.029). The presence of gelatin on the remnant parts was verified by scanning electron microscopy and X-ray spectroscopy, demonstrating the coatings' resilience. MNS-obtained BG-based scaffolds were thus confirmed to exhibit osteogenic properties in vivo that can significantly be enhanced by gelatin coating.

Collagen scaffolds functionalised with copper-eluting bioactive glass reduce infection and enhance osteogenesis and angiogenesis both in vitro and in vivo.

The bone infection osteomyelitis (typically by Staphylococcus aureus) usually requires a multistep procedure of surgical debridement, long-term systemic high-dose antibiotics, and - for larger defects - bone grafting. This, combined with the alarming rise in antibiotic resistance, necessitates development of alternative approaches. Herein, we describe a one-step treatment for osteomyelitis that combines local, controlled release of non-antibiotic antibacterials with a regenerative collagen-based scaffold. To maximise efficacy, we utilised bioactive glass, an established osteoconductive material with immense capacity for bone repair, as a delivery platform for copper ions (proven antibacterial, angiogenic, and osteogenic properties). Multifunctional collagen-copper-doped bioactive glass scaffolds (CuBG-CS) were fabricated with favourable microarchitectural and mechanical properties (up to 1.9-fold increase in compressive modulus over CS) within the ideal range for bone tissue engineering. Scaffolds demonstrated antibacterial activity against Staphylococcus aureus (up to 66% inhibition) whilst also enhancing osteogenesis (up to 3.6-fold increase in calcium deposition) and angiogenesis in vitro. Most significantly, when assessed in a chick embryo in vivo model, CuBG-CS not only demonstrated biocompatibility, but also a significant angiogenic and osteogenic response, consistent with in vitro studies. Collectively, these results indicate that the CuBG-CS developed here show potential as a one-step osteomyelitis treatment: reducing infection, whilst enhancing bone healing.