Clinical efficacy of simvastatin gel combined with polypropylene membrane on the healing of extraction sockets: A triple-blind, randomized clinical trial.

OBJECTIVES: This study aimed to evaluate dimensional changes, level of soft tissue healing, and pain/discomfort perception in post-extraction sockets filling with 1.2% simvastatin (SIM) gel covered with polypropylene membranes (PPPM). MATERIAL AND METHODS: Twenty-six post-extraction sockets of posterior teeth were randomly allocated in two groups: (a) socket filling with 1.2% SIM gel and covered with PPPM (n = 13) and (b) socket filling with placebo gel and covered with PPPM (n = 13). Cone-beam computed tomography (CBCT) images before and 90 days after the extraction enabled alveolar bone dimensional changes calculation using horizontal and vertical measurements. The measurements occurred at three different levels for thickness located 1, 3, and 5 mm from the top of the bone crest. The vertical (depth) measure was assessed from the most apical portion of the socket to the bone crest's most coronal portion. Seven days after the extractions, the level of soft tissue healing and pain perception were also analyzed. RESULTS: After 90 days of extractions, the dimensional changes in thickness in the test group were significantly smaller in sections A (p = .044), B (p = .036) and C (p = .048) when compared to the control group. The test group showed a significantly lower height-dimensional change than the control group (p < .0001). Soft tissue healing index (p = .63), perception of pain (p = .23), and number of analgesics consumed (p = .25) were similar between groups. CONCLUSIONS: Simvastatin at 1.2% compared with placebo effectively reduced the dimensional changes in post-extraction sockets covered with PPPM. There was no significant difference in the level of soft tissue healing and postoperative pain between the test and control groups.

Efeito da temperatura de armazenamento na resistência coesiva de um compósito / Effect of storage temperature on the composite cohesive strength

O objetivo deste estudo foi avaliar a resistência à tração diametral de um compósito fotopolimerizável em diferentes temperaturas de armazenamento. Foram confeccionados 12 espécimes cilíndricos (n = 6),que foram divididos em dois grupos: G1- resina à temperatura ambiente (25ºC) e G2- resina utilizada imediatamente após remoção do refrigerador (5ºC). Cada espécime foi confeccionado em três incrementos, cada incremento polimerizado por 40 segundos. Realizouse o teste a uma velocidade de 1.0 mm/min até a falha. Após cada teste, a resistência à tração diametral foi calculada (MPa) e os resultados submetidos à análise estatística, pelo teste t-student (p > 0,05). Não houve efeito da temperatura de armazenamento na resistência coesiva da resina utilizada neste estudo.

Efeito do fator cavitário na resistência adesiva à dentina de um sistema restaurador à base de silorano / C factor effect on bond strength of a restorative system based on silorane

O objetivo deste estudo foi avaliar o efeito do fator C na resistência adesiva à dentina humana de um compósito à base de silorano, comparando-o com um compósito à base de metacrilato. Foram utilizados 40 molares humanos hígidos. Em metade da amostra foi realizado um preparo do tipo Classe I, com dimensões de 4x4 mm e 2 mm de profundidade, enquanto na outra metade foi realizado um preparo virtual (flat) com auxílio de uma matriz de teflon branco, com as mesmas dimensões da cavidade (4x4x2 mm), apoiada na superfície de dentina exposta. Cada grupo foi divido em dois, de acordo com o sistema restaurador: Sistema Adesivo P90 e resina Filtek P90; Adper Scotchbond Multiuso e resina Filtek Z350 XT (3M ESPE). Após a aplicação do sistema adesivo segundo as especificações do fabricante, as cavidades (real e virtual) foram preenchidas com as resinas (Z350 XT e P90) em dois incrementos. Foi realizada a fotoativação de cada incremento durante 25s. Após uma semana, as coroas foram seccionadas, obtendo-se espécimes constituídos de resina/dente na forma de um paralelepípedo (palitos). Estes palitos foram utilizados para o teste de microtração (Emic), onde a resistência adesiva na unidade MPa foi calculada. Os resultados foram avaliados estatisticamente pelo teste de análise de variância ANOVA One-Way (p = 0,05), e pelo teste de múltiplas comparações Student Newman Keuls. Foi observada uma diferença estatística entre a resina P90 (flat= 16,13±7,7 MPa e Cavidade= 16,75±9,0 MPa) e a Z350 XT (flat= 25,82±11,6 MPa e Cavidade=24,47±13,5 MPa), independentemente do tipo de cavidade restaurada. E não foi possível observar diferença estatística entre os tipos de cavidades (real ou virtual) restauradas com a mesma resina. Através dos testes realizados, foi possível concluir que: o fator C não afetou a resistência adesiva dos dois sistemas restauradores utilizados, e o tipo de sistema restaurador afeta a resistência adesiva, sendo que o sistema à base de silorano apresenta ...

The purpose of this study is to evaluate the effect of the C factor in the bond strength of a composite based on silorane to human dentin, comparing its results with a methacrylate-based composite. A total of 40 human molars were used. In half of this sample was used a Class I standard preparation method, comprising the dimensions of 4x4 mm and 2 mm deep, while with the other half was used a virtual preparation method (flat), being applied a white Teflon matrix, respecting the same dimensions cavity (4x4x2 mm), supported on the surface of exposed dentin. Each group was divided into two parts, in accordance with the 2 different restorative systems: P90 Adhesive System and Filtek P90; Filtek Z350 XT and Adper Scotchbond Multipurpose (3 ESPE). Based on manufacturer's specifications the adhesive system was applied , the cavities (real and virtual) were filled with the resins (Z350 XT and P90) in two increments. Polymerization was performed for each increment during 25 seconds. After one week, the crowns were sectioned, obtaining specimens made of resin / tooth in the form of a parallelepiped (stick-shaped). These sticks were used in a microtensile test (Emic), where the bond strength was calculated in Mpa unit . It was used the analysis of variance One-Way ANOVA (p = 0.05) and also, the Student Newman Keuls test for multiple comparisons to evaluate the results statistically. It was observed a statistical difference between the P90 resin (flat = 16.13±7.7 MPa and cavity = 16.75±9.0 MPa) and Z350 XT (flat = 25.82±11.6 MPa and cavity = 24.47±13.5 MPa), regardless of the cavity restored. And it was not possible to observe a statistical difference between the types of cavities (real or flat) restored with the same composite. The conclusion of the tests is: the C factor did not affect the bond strength of two restorative systems applied, and the type of restorative system affects the bond strength, and the system based on silorano presents ...

Efeito do método de fotoativação e armazenamento de um compósito na sua resistência coesiva / Efects of cohesive strength of a composite after photoactivation and storage media

A proposta deste estudo é avaliar a resistência à tração diametral após dois tipos de fotoativação e armazenamento.Foram confeccionados 24 espécimesdivididos em quatro grupos: G1- fotoativação convencional armazenado em água destilada; G2- pulso tardioarmazenado em água destilada; G3- convencional armazenado em álcool e G4- pulso tardio armazenado em álcool (n = 6). Os grupos foram armazenados a37º C por 24 horas. O foi realizado a uma velocidade de 1.0 mm/min. Os resultados (G1:130.9, G2:127.6, G3:130.8, G4:110.8 MPa) foram submetidos à análise de variância Anova (p ≥ 0,05) e apontam para uma semelhança estatística. Não foi encontrada diferençana resistência coesiva do compósito nos diferentes métodos de fotoativação e meios de armazenamento.

Doença do refluxo gastroesofágico e erosão dentária / Gastroesophageal reflux disease and dental erosion

0 objetivo do presente estudo foi abordar a erosão dentária (ED) decorrente da doença do refluxo gastroesofágico (DRCE) nas diferentes faixas etárias e sua associação com outras doenças, com particular atenção para diagnóstico, prevenção e potenciais perspectivas de tratamento. A elevada prevalência da DRGE, tanto em adulto quanto em criança, observada nas últimas duas décadas, tem sido responsável por tornar esta afecção um problema de saúde pública. Esta doença pode ainda comprometer sítios extradigestórios, como pulmão e ouvido. Ou estar associada com doenças sistêmicas, tal como a diabetes, desordens alimentares, como a bulimia, ou o consumo abusivo de álcool de forma regular. A associação entre a DRCE e o processo de ED, decorrente da acidificação do meio bucal, fragiliza os tecidos mineralizados acarretando a perda destes tecidos. Cabe ressaltar que a ED não está relacionada com o envolvimento bacteriano. Ela é um processo irreversível, que altera aparência, funcionalidade e pode levar à perda do elemento dentário.