RESUMO
We present a microfluidic chip in Polymethyl methacrylate (PMMA) for optical trapping of particles in an 80µm wide microchannel using two counterpropagating single-mode beams. The trapping fibers are separated from the sample fluid by 70µm thick polymer walls. We calculate the optical forces that act on particles flowing in the microchannel using wave optics in combination with non-sequential ray-tracing and further mathematical processing. Our results are compared with a theoretical model and the Mie theory. We use a novel fabrication process that consists of a premilling step and ultraprecision diamond tooling for the manufacturing of the molds and double-sided hot embossing for replication, resulting in a robust microfluidic chip for optical trapping. In a proof-of-concept demonstration, we show the trapping capabilities of the hot embossed chip by trapping spherical beads with a diameter of 6µm, 8µm and 10µm and use the power spectrum analysis of the trapped particle displacements to characterize the trap strength.
Assuntos
Coloides/química , Coloides/isolamento & purificação , Tecnologia de Fibra Óptica/instrumentação , Dispositivos Lab-On-A-Chip , Pinças Ópticas , Polimetil Metacrilato/química , Desenho de Equipamento , Análise de Falha de Equipamento , MicroesferasRESUMO
An experimental study of a micromachined non-porous pillar array column performance under non-retentive conditions is presented. The same pillar structure has been fabricated in cyclo-olefin polymer (COP) chips with three different depths via hot embossing and pressure-assisted thermal bonding. The influence of the depth on the band broadening along with the already known contribution arising from the top and bottom cover plates has been studied. The experimental results exhibit reduced plate heights as low as 0.2, which are in agreement with the previous experimental work. Moreover, the constant values of the reduced Van Deemter expression are also in accordance with the previous studies. A more exhaustive study of the C-term band broadening is also presented, showing that comparing the space between the pillars with different open tubular rectangular channels offers a good estimation of the C-term band broadening that is obtained experimentally. These experimental results, hence, confirm that micromachined pillar array columns fabricated in COP can achieve the same performance as the ones fabricated in silicon for the presently studied pillar channel design.
Assuntos
Cromatografia Líquida de Alta Pressão/métodos , Cicloparafinas/química , Técnicas Analíticas Microfluídicas/métodos , Polímeros/química , Microscopia Eletrônica de Varredura , MicrotecnologiaRESUMO
We report on the possibility to perform HDC in micropillar array columns and the potential advantages of such a system. The HDC performance of a pillar array column with pillar diameter = 5 microm and an interpillar distance of 2.5 microm has been characterized using both a low MW tracer (FITC) and differently sized polystyrene bead samples (100, 200 and 500 nm). The reduced plate height curves that were obtained for the different investigated markers all overlapped very well, and attained a minimum value of about h(min)=0.3 (reduction based on the pillar diameter), corresponding to 1.6 microm in absolute value and giving good prospects for high efficiency separations. The obtained reduced retention time values were in fair agreement with that predicted by the Di Marzio and Guttman model for a flow between flat plates, using the minimal interpillar distance as characteristic interplate distance.