RESUMO
OBJECTIVES: To evaluate the anti-demineralizing effect of a mouthwash comprising pomegranate peel extract (PPE 3%), sodium trimetaphosphate (TMP 0.3%), and fluoride (F 225 ppm) in an in situ study, and to assess its irritation potential in an ex vivo study. METHODS: This double-blind crossover study was conducted in four phases with 7 days each. Twelve volunteers used palatal appliances containing enamel blocks, which were subjected to cariogenic challenges. The ETF formulation (PPE + TMP + F, pH 7.0), TF formulation (TMP + F, pH 7.0), deionized water (W, pH 7.0), and essential oil commercial mouthwash (CM, 220 ppm F, pH 4.3) were dropped onto the enamel twice daily. The percentage of surface hardness loss, integrated loss of subsurface hardness, calcium, phosphorus, and fluoride in enamel and biofilms were determined. In addition, alkali-soluble extracellular polysaccharide concentrations were analyzed in the biofilms. The irritation potential was evaluated using the hen's egg chorioallantoic membrane test through the vascular effect produced during 300-s of exposure. RESULTS: ETF was the most efficacious in preventing demineralization. It also showed the highest concentrations of calcium and phosphorus in the enamel and in the biofilm, as well as the lowest amount of extracellular polysaccharides in the biofilm. In the eggs, ETF produced light reddening, whereas CM led to hyperemia and hemorrhage. CONCLUSIONS: The addition of PPE to formulations containing TMP and F increased its anti-demineralizing property, and this formulation presented a lower irritation potential than the CM. CLINICAL RELEVANCE: ETF can be a promising alternative alcohol-free mouthwash in patients at high risk of caries.
Assuntos
Antissépticos Bucais , Extratos Vegetais , Punica granatum , Desmineralização do Dente , Humanos , Cálcio/análise , Estudos Cross-Over , Esmalte Dentário , Fluoretos , Dureza , Antissépticos Bucais/química , Antissépticos Bucais/farmacologia , Fósforo , Polifosfatos , Desmineralização do Dente/prevenção & controle , Extratos Vegetais/farmacologiaRESUMO
To evaluate the effect of 1100 ppm F toothpastes supplemented with micrometric or nanosized ß-CaGP (ß-CaGPm/ß-CaGPn) on artificial enamel remineralization, using a pH cycling model. Enamel blocks with artificial caries were randomly allocated into ten groups (n = 10), according to the toothpastes: without fluoride/ß-CaGPm/ß-CaGPn (negative control); 1100 ppm F (1100F); 1100F plus 0.125%, 0.25%, 0.5%, and 1.0% of ß-CaGPm or ß-CaGPn. The blocks were treated 2×/day with slurries of toothpastes. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); integrated mineral loss (ΔIMR); fluoride (F), calcium (Ca), and phosphorus (P) concentrations in the enamel; polydispersity index (PdI); and zeta potential (Zp) were determined. The data were analyzed by ANOVA (p < 0.001). For Zp/PdI, no significance was observed when comparing the means (p > 0.001). The treatment with 1100F-0.25%ß-CaGPn led to %SHR â¼57 higher when compared to the 1100F group (p < 0.001). The lowest ΔKHN was observed for the 1100F-0.25%ß-CaGPn group (p < 0.001). The ΔIMR was lower (â¼201%) for the 1100F-0.25%ß-CaGPn when compared to 1100F (p < 0.001). The association of ß-CaGPm and ß-CaGPn to 1100F did not influence its F concentration (p > 0.001). The highest increase in Ca and P was observed for 1100F-0.25%ß-CaGPn (p < 0.001). The addition of 0.25%ß-CaGPn to 1100F toothpaste was able to promote an additional remineralizing effect of artificial caries lesions.
RESUMO
OBJECTIVES: This study investigates the dentin permeability (by hydraulic conductance) and tubule occlusion (by confocal and scanning electron microscopies) of in-office desensitizing materials. MATERIALS AND METHODS: Bovine dentin blocks were immersed in EDTA to open dentinal tubules. Placebo varnish (PLA), fluoride varnish (FLU), NaF 5% + 5% nanoparticulate sodium trimetaphosphate varnish (TMP), universal adhesive system (SBU), S-PRG filler varnish (SPRG), Biosilicate (BIOS), and amelotin (AMTN) solution were the materials tested. After application, the specimens underwent an erosive-abrasive challenge. Dentin permeability was evaluated at T0 (initial), T1 (after treatment), and T2 (after challenge). Confocal and scanning electron microscopy (SEM) were used to evaluate, respectively, length and number of dentinal tubule occlusions and opened dentinal tubules, after challenge. Permeability and SEM data were analyzed by two-way repeated measures ANOVA and Tukey's tests. Confocal data were analyzed by one-way ANOVA, Tukey's test, and Kruskal-Wallis and Dunn's tests. Spearman and Pearson's correlation tests were also used. Significance level was set at 5%. RESULTS: At T1, the AMTN group showed the lowest permeability value, following the increasing order at T2: AMTN = SBU < BIOS = SPRG < TMP < FLU < PLA. The SBU group had the highest value of occluded dentinal tubule length. The AMTN group presented more occluded dentinal tubules compared to PLA and FLU. AMTN and SBU had the lowest values of opened dentin tubules. Results showed a negative correlation between the analyses. CONCLUSION: The SBU and AMTN solution were more effective in reducing dentin permeability by occluding dentin tubules. CLINICAL RELEVANCE: All materials reduced permeability after challenge, except fluoride varnish.
Assuntos
Dessensibilizantes Dentinários , Sensibilidade da Dentina , Animais , Bovinos , Dentina , Dessensibilizantes Dentinários/uso terapêutico , Permeabilidade da Dentina , Sensibilidade da Dentina/tratamento farmacológico , Fluoretos/farmacologia , Fluoretos Tópicos/farmacologia , Microscopia Eletrônica de Varredura , PoliésteresRESUMO
Although the association of polyols/polyphosphates/fluoride has been demonstrated to promote remarkable effects on dental enamel, little is known on their combined effects on biofilms. This study assessed the effects of solutions containing fluoride/sodium trimetaphosphate (TMP)/xylitol/erythritol on dual-species biofilms of Streptococcus mutans and Candida albicans. Biofilms were grown in the continuous presence of these actives alone or in different associations. Quantification of viable plate counts, metabolic activity, biofilm biomass, and extracellular matrix components were evaluated. Overall, fluoride and TMP were the main actives that significantly influenced most of the variables analyzed, with a synergistic effect between them for S. mutans CFUs, biofilm biomass, and protein content of the extracellular matrix (p < 0.05). A similar trend was observed for biofilm metabolic activity and carbohydrate concentrations of the extracellular matrix, although without statistical significance. Regarding the polyols, despite their modest effects on most of the parameters analyzed when administered alone, their co-administration with fluoride and TMP led to a greater reduction in S. mutans CFUs and biofilm biomass compared with fluoride alone at the same concentration. It can be concluded that fluoride and TMP act synergistically on important biofilm parameters, and their co-administration with xylitol/erythritol significantly impacts S. mutans CFUs and biomass reduction.
Assuntos
Fluoretos , Xilitol , Fluoretos/farmacologia , Xilitol/farmacologia , Polifosfatos/farmacologia , Biofilmes , Eritritol/farmacologiaRESUMO
It has been stated that sodium trimetaphosphate (TMP) promotes a more anionic dentin surface inducing greater calcium (Ca) and phosphate precipitation. The aim of the present study was to evaluate in vitro the surface free energy (γs) of dentin after treatment with TMP associated or not with fluoride (F), exposed or not to Ca, as well as the adsorption of TMP, F, and Ca by dentin. Bovine dentin blocks (n = 12 blocks/group) were treated with solutions containing TMP at 0, 1, 3, or 9 (w/v) followed or not by the application of Ca. These solutions were or were not associated to 1,100 ppm F. F, Ca, and TMP were determined in the solutions before and after the treatment to calculate the adsorption by dentin. To analyze the γs of dentin, the apolar (γsLW), and polar (γsAB), components were determined by contact angle measurement. Data were submitted to 2-way ANOVA followed by the Student-Newman-Keuls test (p < 0.05). TMP reduces γs of dentin and increases electron donor sites (γs-). Higher values of γs- led to higher adsorption of Ca (p < 0.001). The F/TMP association did not change γs or γsLW and reduced the values of γs-, but the adsorption of Ca was higher. There was correlation between the adsorption of TMP and γs- (Pearson's r = 0.801; p < 0.001) and F (Pearson's r = 0.871, p < 0.001). It is possible to conclude that TMP increased γs- and Ca adsorption, and reduced γs. The association with F increased the adsorption of TMP without rising γs-; however, there was higher adsorption of Ca.
Assuntos
Cálcio , Fluoretos , Animais , Bovinos , Dentina , Fluoretos/farmacologia , Humanos , Polifosfatos/farmacologia , Fluoreto de Sódio/farmacologiaRESUMO
OBJECTIVES: This in vitro study evaluated the efficacy of toothpaste containing fluoride (F), sodium trimetaphosphate (TMP), and xylitol and erythritol (XE) to inhibit or repair initial enamel erosion lesions. MATERIALS AND METHODS: Bovine enamel blocks (n = 120) were selected according to surface hardness (SH) and randomly divided into 5 experimental groups (n = 24 blocks/group): Placebo (no F, TMP, XE); 1100 ppm F; 16% xylitol + 4% erythritol (XE); 200 ppm F + 0.2% TMP (200 ppm F/TMP); and 200 ppm F + 0.2% TMP + 16% xylitol + 4% erythritol (200 ppm F/TMP/XE). The sound and softened blocks were immersed in toothpaste slurry in human saliva for 2 min. The blocks were then submitted to 4 erosive challenges in citric acid (0.75%, pH 3.5), each challenge for 1 min, with stirring. The SH of the blocks was determined after treatment (t) and after the 4 erosive challenges. In addition, the precipitates were analyzed by scanning electron microscopy (SEM). Variables were submitted to a two-way repeated-measures analysis of variance followed by a Student-Newman-Keuls test (p < 0.05). RESULTS: Toothpaste containing 200 ppm F/TMP/XE led to the highest protective and repair effect compared to the other groups (p < 0.001). The protective and repair effect was XE > 200 ppm F/TMP > 1100 ppm F > placebo (p < 0.001). All groups produced precipitates with a thicker layer for XE and TMP groups. CONCLUSIONS: Toothpaste containing 200 ppm F, TMP, and polyols demonstrated a superior protective and repair effect in initial enamel erosive lesions in vitro. CLINICAL RELEVANCE: Toothpaste containing F and polyols could be an advantage in patients affected by dental erosion, due to its higher preventive potential, mainly in individuals who frequently drink acidic beverages. However, future studies are needed to confirm these results.
Assuntos
Fluoretos , Cremes Dentais , Animais , Bovinos , Humanos , Cariostáticos/farmacologia , Esmalte Dentário , Eritritol/farmacologia , Fluoretos/análise , Dureza , Concentração de Íons de Hidrogênio , Fluoreto de Sódio/farmacologia , Cremes Dentais/farmacologia , Cremes Dentais/uso terapêutico , Xilitol/farmacologiaRESUMO
OBJECTIVES: This study evaluated the effects of sodium hexametaphosphate microparticles (HMPmicro) or nanoparticles (HMPnano) on the growth of saliva-derived microcosm biofilms MATERIALS AND METHODS: Saliva-derived biofilms were formed on glass coverslips for 24 h. Thereafter, Streptococcus mutans (C180-2) was incorporated or not into the biofilms. From that time point onwards, solutions containing 0.2% HMPmicro or HMPnano, combined or not with 220 ppm F, were constantly present in the culture medium. In addition, 220 ppm F alone (220F) and McBain medium without any compound were also tested as positive and negative controls (CTL), respectively. After 96 h, the biofilms were plated on anaerobic blood agar or sucrose agar bacitracin for total and S. mutans CFU-counting, respectively. Biofilms' lactic acid production was analysed spectrophotometrically. Data were submitted to ANOVA or Kruskal-Wallis' tests, followed by Student-Newman-Keuls' test (p<0.05; n=12). RESULTS: HMPmicro or HMPnano led to significantly lower lactic acid production, and significant reductions in total CFU-counting in microcosm biofilms, supplemented or not with S. mutans, in comparison to both controls, with significant differences between 220F and CTL. No significant differences were observed among the groups treated with HMPmicro or HMPnano (with or without F). The same trend was seen for S. mutans CFU-counting, in biofilms supplemented with S. mutans. CONCLUSIONS: HMP significantly reduced total and S. mutans CFU counts, as well as lactic acid production by saliva-derived microcosm biofilms. CLINICAL RELEVANCE: These findings in saliva-derived microcosm biofilms suggest that HMP stands as a promising alternative for the control of cariogenic biofilms.
Assuntos
Nanopartículas , Saliva , Ágar/farmacologia , Biofilmes , Humanos , Ácido Láctico/farmacologia , Fosfatos , Streptococcus mutansRESUMO
OBJECTIVE: This study evaluated in vitro the effects of calcium gluconate (CaGlu), sodium fluoride (NaF), sodium hexametaphosphate (HMP), and NaF/TMP added to a 35% hydrogen peroxide (H2O2) bleaching gel on the color change, enamel hardness, and trans-amelodentinal diffusion. MATERIALS AND METHODS: Enamel discs/bovine dentin (n = 150) were divided according to the bleaching gel: 35% H2O2 (H2O2); 35% H2O2 + 0.1% NaF (H2O2/NaF); 35% H2O2 + 1% HMP (H2O2/HMP); 35% H2O2 + 0.1% NaF + 1% HMP (H2O2/NaF/HMP), and 35% H2O2 + 2% CaGlu (H2O2/Caglu). The bleaching gels were applied three times (40 min/session) at 7-day intervals between each application. Then, color alteration (ΔE), whitening index (ΔWID), percentage of surface hardness loss (% SH), cross-sectional hardness (ΔKHN), and trans-amelodentinal diffusion were determined. Data were submitted for analysis of variance (ANOVA), followed by the Student-Newman-Keuls test (p < 0.05). RESULTS: All bleaching gels showed significant color changes after treatment (p < 0.001). ΔE and ΔWID were similar among the evaluated gels. Mineral loss (% SH and ΔKHN) and trans-amelodentinal diffusion of hydrogen peroxide were lower for H2O2/NaF/HMP; the H2O2/CaGlu group presented the highest values about the other groups (p < 0.001). CONCLUSION: It is possible to conclude that the addition of NaF/HMP to the in-office bleaching agent did not interfere with the bleaching efficacy and reduced enamel demineralization and H2O2 diffusion. CLINICAL SIGNIFICANCE: The association of NaF/HMP to the bleaching gel can be used as a novel approach for minimizing the adverse effects of H2O2 by-products and with similar clinical efficacy.
Assuntos
Clareadores , Clareadores Dentários , Clareamento Dental , Animais , Bovinos , Estudos Transversais , Fluoretos/farmacologia , Géis , Dureza , Humanos , Peróxido de Hidrogênio , Fosfatos , Fluoreto de Sódio/farmacologia , Clareamento Dental/efeitos adversos , Clareadores Dentários/farmacologiaRESUMO
BACKGROUND: The objective of this systematic review and meta-analysis (SRM) was to assess the evidence between the association of oral lichen planus and periodontal disease, evaluating the periodontal clinical parameters and biomarkers levels. METHODS: This systematic review and meta-analysis followed PRISMA and was registered in PROSPERO (CRD42020181513). Searches were accomplished in databases for articles published until June 2021. The meta-analysis was performed with the variables: plaque index (PI), gingival index (GI), probing depth (PD), and clinical attachment loss (CAL). The mean difference was applied with a 95% confidence interval. RESULTS: Six articles were included. Qualitative analysis showed the levels of biomarkers (matrix metalloproteinases, interleukins, and periodontal microbiological profile) are increased in subjects with periodontal disease and oral lichen planus. In the meta-analysis, these subjects also presented increases in all periodontal clinical parameters evaluated: GI-gingivitis 0.22 [0.14, 0.31] p < 0.0001 and periodontitis 0.12 [0.06, 0.19] p = 0.0003; PI-gingivitis 0.22 [0.12, 0.31] p < 0.0001 and periodontitis 0.15 [0.08, 0.23] p < 0.0001; PD-gingivitis 0.27 [0.06; 0.48] p = 0.0107 and periodontitis 0.11 [0.01; 0.21] p = 0.0299; and CA-periodontitis 0.06 [0.01, 0.12] p = 0.0176. CONCLUSIONS: Evidence suggests a significant relationship between the severity of periodontal disease and the presence of oral lichen planus. Although the association is biologically plausible, further studies are needed using populations and well-defined biochemical and clinical outcomes with consideration of potential confounding factors. CLINICAL RELEVANCE: This SRM provides information on the interaction between OLP and periodontal disease and guides clinicians to make evidence-based decisions and suggests recommendations for further high-quality studies.
Assuntos
Gengivite , Líquen Plano Bucal , Doenças Periodontais , Periodontite , Gengivite/microbiologia , Humanos , Líquen Plano Bucal/complicações , Doenças Periodontais/complicações , Índice PeriodontalRESUMO
This study aimed to evaluate the surface (γs) and interaction (ΔGiwi) free energy and calcium (Ca2+) and phosphate (PO43-) adsorption to dental enamel treated with sodium trimetaphosphate (TMP) or calcium glycerophosphate (CaGP) that had or had not been exposed to CaPO4-containing solutions. Bovine enamel blocks (n = 192; 24 blocks/group) were treated (2 mL/block; 2 min) with TMP (0%, 1%, 3%, and 9%) and CaGP (0, 0.25, 0.5, and 1%) or exposed to a CaPO4-containing solution. The adsorption of these compounds by enamel was assessed before and after treatment. γs and ΔGiwi and their apolar (γsLW and ΔGiwiLW) and polar (γsAB and ΔGiwiAB) components and acid-base interactions (γs+/γs-) were determined by the contact angles. The data were subjected to ANOVA, followed by the Student-Newman-Keuls test (p < 0.05). The adsorption of TMP was dose dependent (p < 0.001), and it reduced γs and γsAB and increased ΔGiwiAB (ΔGiwi > 0) and γs- when compared with the group without TMP (p < 0.001). The immersion in CaPO4-containing solution increased γs and γsAB and reduced ΔGiwiAB (ΔGiwi > 0) and γs- (p < 0.001). There was a correlation between the adsorption of TMP and Ca2+ (r = 0.916; p < 0.001) and PO43- (r = 0.899; p < 0.001). The adsorption of CaGP on the enamel was dose dependent (p < 0.001), reducing γs, ΔGiwiAB (ΔGiwi < 0), γsLW, and γs- when compared to the group without CaGP (p < 0.001). When exposed to the CaPO4-containing solution, there was an increase in ΔGiwiAB (ΔGiwi > 0), γsLW, and γs- and a decrease in γsAB (p < 0.001) without adsorption of Ca2+ by enamel. It may be concluded that TMP and CaGP were adsorbed onto the enamel, producing hydrophilic and hydrophobic surfaces, respectively. TMP produces electron donor sites that induce Ca2+ adsorption, while CaGP releases Ca2+ into the medium.
Assuntos
Cálcio , Glicerofosfatos , Adsorção , Animais , Bovinos , Esmalte Dentário , Fluoretos , Humanos , PolifosfatosRESUMO
OBJECTIVES: To evaluate the hydraulic conductance of dentin after treatment with fluoride toothpastes containing sodium trimetaphosphate microparticles (TMPmicro) or nanoparticles (TMPnano). MATERIALS AND METHODS: The dentinal tubules of bovine dentin blocks (4 × 4 × 1 mm) were unobstructed for determination of the maximum hydraulic conductance of the dentin. The dentin blocks were randomized into four groups (n = 15/group) of toothpastes (placebo, 1100 ppm F, and 1100 with 3% TMPmicro or 3% TMPnano) which were applied for 7 days (2×/day) using a brushing machine. The dentin surface (5/group) was analyzed by scanning electron microscopy. The hydraulic conductance post-treatment was measured in the other ten blocks. Thereafter, the same blocks were immersed in citric acid (pH 3.2) for 1 min, and the conductance was determined again. The data were submitted to 2-way ANOVA repeated measures, followed by the Student-Newman-Keuls test (p < 0.05). RESULTS: The percentage conductance reduction post-treatment for the groups were placebo = 1100 ppm F < 1100 TMPnano < 1100 TMPmicro (p < 0.001). After acid attack, the percentage reduction was placebo < 1100 ppm F < 1100 TMPnano < 1100 TMPmicro (p < 0.001). The toothpastes containing TMP showed the highest obliteration of dentinal tubules. CONCLUSIONS: The addition of TMPmicro to fluoride toothpaste produced a greater reduction in hydraulic conductance when compared with 1100 ppm F toothpaste. CLINICAL RELEVANCE: The increased capacity of toothpastes containing TMP to reduce hydraulic conductance indicates their potential to reduce symptoms of dentinal hypersensitivity.
Assuntos
Nanopartículas , Cremes Dentais , Animais , Bovinos , Dentina , Fluoretos/farmacologia , Humanos , Polifosfatos , Fluoreto de Sódio , Cremes Dentais/farmacologiaRESUMO
BACKGROUND: The aim of this systematic review and meta-analysis (SRM) was to assess the postoperative pain (PP) after non-surgical endodontic retreatment (NSER) in a one visit compared to multiple visits. The PICO question used was "Does NSER in patients with unsatisfactory endodontic treatment in a one-visit visit have a similar PP to that of NSER in multiple visits?" MATERIALS AND METHODS: This systematic review followed PRISMA and was registered in PROSPERO (CRD42019136700). Searches were performed in the PubMed/MEDLINE, Scopus, and the Cochrane Library databases for articles published until September 2020. The eligible criteria were randomized clinical trials (RCTs). The meta-analysis was based on the Mantel-Haenszel. The PP after the retreatment was analyzed using a dichotomous outcome, measured according to risk ratio (RR) when p < 0.05. The Cochrane scale was used to assess risk of bias, and the Grading of Recommendations Assessment, Development, and Evaluation (GRADE) approach was used to assess the quality of evidence. RESULTS: Four studies were included. In general analysis without considering intensity, one-visit NSER presented lower PP than the multiple visits only for 1 and 30 days [(RR = 0.67; CI: 0.48 to 0.93; p = 0.02), and (RR = 0.09; CI: 0.01 to 0.66; p = 0.02)], respectively. Regarding sub-analysis considering the intensity, one visit present lower mild PP when compared with multiple visits [(RR = 0.54; CI: 0.30, 0.96; p = 0.04); (RR = 0.33; CI: 0.12, 0.88; p = 0.03); and (RR = 0.12; CI: 0.02, 0.86; p = 0.03)], respectively. However, sub-analysis for moderate and severe PP showed no significant difference, independently of period evaluated (p > 0.05). Regarding the risk of bias analysis, a low risk was observed for most domains, except allocation that was considered unclear, while the certainty of evidence for each analysis was considered low. CONCLUSION: Within the limitations of study, the one and multiple visit can be considered adequate, because both present a similar occurrence of PP, except for mild pain. However, due to the low number of studies, further well conducted and standardized RCTs are needed to reassess these results. CLINICAL RELEVANCE: Both therapies of endodontic retreatment can be considered in clinical practice. Therefore, the endodontist must consider the patient's individual characteristics and experience to consider the best treatment approach.
Assuntos
Assistência Odontológica , Dor Pós-Operatória , Humanos , Ensaios Clínicos Controlados Aleatórios como Assunto , RetratamentoRESUMO
OBJECTIVE: This study evaluated the effects of calcium gluconate (CaGlu), sodium fluoride (NaF), sodium trimetaphosphate (TMP), and NaF/TMP added to a 35% hydrogen peroxide (HP) bleaching gel for the reduction in enamel demineralization in vitro, with and without the use of a fluoridated dentifrice. DESIGN: Enamel blocks (n = 100) were obtained from bovine incisors (n = 200) after flattening and subjected to initial surface hardness (SH) analysis. The blocks were divided according to the bleaching gel (35% HP; 35% HP + 0.05% NaF; 35% HP + 0.25% TMP; 35% HP + 0.05% NaF + 0.25% TMP; 35% HP + 2% CaGlu) and were treated with ether non-fluoridated or fluoridated (1100 ppm) dentifrice. The bleaching gels were applied thrice (40 min/session) at the intervals of 7 days between each application. After 21 days, the final SH for the calculation of the percentage of SH loss (%SH) and cross-sectional hardness for the evaluation of the integrated hardness area (IH) were determined. RESULTS: Bleaching containing HP + NaF + TMP presented lowest %SH (p < 0.001), regardless of the dentifrice used. HP + NaF + TMP bleaching gel led to lower subsurface enamel mineral loss (IH) compared to the other groups (p < 0.001), and these did not differ from each other (p > 0.05). Daily use of fluoride dentifrice led to higher IH values (p < 0.001), regardless of the bleaching gels. CONCLUSION: The addition of NaF/TMP to a 35% HP bleaching gel remarkably reduced the mineral loss compared to the cases of the other bleaching gels, regardless of dentifrice. CLINICAL RELEVANCE: The association of TMP/NaF can be used as a strategy for reducing mineral loss during the bleaching procedure, even without the daily use of fluoride dentifrice.
Assuntos
Dentifrícios , Desmineralização do Dente , Animais , Cálcio , Cariostáticos , Bovinos , Estudos Transversais , Esmalte Dentário , Dentifrícios/farmacologia , Fluoretos , Géis , Dureza , Fluoreto de SódioRESUMO
OBJECTIVE: To evaluate the effect of treatment with fluoridated toothpaste supplemented with a combination of sodium trimetaphosphate (TMP) and casein phosphopeptide-amorphous calcium phosphate (MI Paste Plus®) on the demineralization of dental enamel. METHODS: Bovine enamel blocks selected by initial surface hardness (SHi) were randomly allocated into six groups (n = 12), according to the test toothpastes: (1) without F-TMP-MI Paste Plus® (Placebo); (2) 1100 ppm F (1100F); (3) MI Paste Plus®; (4) 1100F + MI Paste Plus® (1100F-MI Paste Plus), (5) 1100F + 3 % TMP (1100F-TMP); and (6) 1100F-TMP + MI Paste Plus® (1100F-TMP-MI Paste Plus). Blocks were treated two times per day with slurries of toothpaste (1 min), and groups 4 and 6 received an application of MI Paste Plus (3 min). Next, the samples were subjected to five pH cycles (demineralizing/remineralizing solutions) at 37 °C, to produce subsurface enamel lesions.Thereafter, the blocks were maintained for 2 days in fresh remineralizing solution. After pH cycling, the following were obtained: percentage of surface hardness loss (%SH); integrated loss of subsurface hardness (ΔKHN); profile analysis and lesion depth subsurface through polarized light microscopy (PLM); scanning electron microscopy (SEM); and fluoride (F), calcium (Ca), and phosphorus (P) in the enamel. The data were subjected to ANOVA (1-criterion), followed by the Student-Newman-Keuls test (p < 0.001). RESULTS: The 1100F-TMP-MI Paste Plus group showed better results for SHR, ΔKHN, and PLM (p < 0.001). The F concentration was similar among all groups (p > 0.001). The 1100F-TMP-MI Paste Plus group showed the highest concentration of Ca and P in the enamel (p < 0.001). CONCLUSION: The application of 1100F-TMP-MI Paste Plus promoted a higher inhibitory effect against enamel demineralization. CLINICAL SIGNIFICANCE: The combination of treatments with F, TMP, and MI Paste Plus® can be an effective alternative to improve the oral health of individuals, especially those with high activity of dental caries and at high risk for its development.
Assuntos
Cárie Dentária , Desmineralização do Dente , Animais , Fosfatos de Cálcio , Cariostáticos , Caseínas/farmacologia , Bovinos , Esmalte Dentário , Fluoretos , Dureza , Humanos , Fosfopeptídeos , Polifosfatos , Remineralização Dentária , Cremes Dentais/farmacologiaRESUMO
The present study evaluated fluoride (F) concentrations in saliva of toddlers after brushing with dentifrices containing different F concentrations, applied in different quantities, and estimated F intake from toothbrushing. The study comprised a double-blind, crossover protocol, in which toddlers (n = 18, 2-3 years old) were randomly assigned into six groups, according to possible combinations of dentifrices (0/550/1,100 ppm F, as NaF) and amounts (rice grain, pea size, and transverse technique). Volunteers used a F-free dentifrice during 1 week. On the 7th day, saliva samples were collected before (baseline), and at 5/15/30/60 min after toothbrushing. All dentifrice expectorated after brushing was collected. F concentrations (saliva and expectorate) were determined with an ion-specific electrode. Data were submitted to ANOVA or Kruskal-Wallis test, followed by Fisher's LSD or Student-Newman-Keuls' tests (p <0.05). Brushing with 550 ppm F dentifrice (pea size or transversal technique) increased the area under the curve (AUC) at similar levels compared to 1,100 ppm F (rice grain). The highest AUC and salivary F at 5 min after brushing were achieved by 1,100 ppm F (pea size), followed by 550 ppm F (transversal technique). Regarding F intake, the highest values were observed for 550 ppm F (transversal technique), followed by 1,100 ppm F (pea size). It is possible to conclude that the amount of dentifrice and F concentration in the product significantly affected both salivary F concentrations and F intake during toothbrushing.
Assuntos
Dentifrícios , Cariostáticos , Pré-Escolar , Método Duplo-Cego , Fluoretos , Humanos , Saliva , Fluoreto de Sódio , Escovação DentáriaRESUMO
This in vitro study evaluated the protective effect of fluoride varnishes containing sodium trimetaphosphate (TMP) against dentin erosion and abrasion. Specimens of coronal dentin were divided into: placebo, 2.5% NaF, 5% NaF, 2.5% NaF + 5% TMP, and 5% NaF + 5% TMP groups (n =24/group). After single application of the varnishes, the samples were immersed in citric acid (0.05 mol/L, pH = 3.2, 5 min) followed or not by brushing, and the dentin wear was assessed after 5 days. Varnishes containing fluoride + TMP led to the lowest wear. TMP varnishes showed a superior effect against dentin erosive wear.
Assuntos
Dentina , Erosão Dentária , Cariostáticos , Esmalte Dentário , Fluoretos , Fluoretos Tópicos , Humanos , Fluoreto de Sódio , Erosão Dentária/prevenção & controleRESUMO
The aim of the present study was to evaluate the influence of sodium trimetaphosphate (TMP), associated or not with fluoride (F), on the concentrations of F, calcium (Ca), and phosphorus (P) and on the pH of mixed biofilms of Streptococcus mutans and Candida albicans, before and after exposure to sucrose. The biofilms received three treatments (72, 78, and 96 h after the beginning of their formation), at three TMP concentrations (0.25, 0.5, or 1%), with or without F at 500 ppm. Solutions containing 500 and 1,100 ppm F as well as artificial saliva were also tested as controls. Biofilm pH was measured and the concentrations of F, Ca, and P were determined (solid and fluid phases). In a parallel experiment, after the third treatment (96 h), the biofilms were exposed to a 20% sucrose solution to simulate a cariogenic challenge and the pH of the medium, F, Ca, P, and TMP were determined. The data were submitted by two-way ANOVA, followed by Fisher's least significant difference test (p < 0.05). Treatment with TMP and 500 ppm F led to higher F concentration in the biofilm fluid. Although TMP did not affect Ca concentrations, biofilms treated with TMP alone presented higher P concentrations. Treatment with 1% TMP and F led to the highest pH values of the biofilm, both before and after the cariogenic challenge. It was concluded that TMP increases F and P in the biofilm and that its presence promotes an increase in the pH of the medium, even after the cariogenic challenge.
Assuntos
Fluoretos , Sacarose , Biofilmes , Fluoretos/farmacologia , Humanos , Concentração de Íons de Hidrogênio , Polifosfatos , Fluoreto de Sódio/farmacologia , Streptococcus mutans , Sacarose/farmacologiaRESUMO
OBJECTIVE: To evaluate the effect of a fluoride toothpaste containing nano-sized sodium hexametaphosphate (HMPnano) on enamel demineralization on the biochemical composition and insoluble extracellular polysaccharide (EPS) in biofilm formed in situ. METHODS: This crossover double-blind study consisted of four phases (7 days each), in which 12 volunteers wore intraoral appliances containing four enamel bovine blocks. The cariogenic challenge was performed using 30% sucrose solution (6×/day). Blocks were treated 3×/day with the following toothpastes: no F/HMP/HMPnano (Placebo), conventional fluoride toothpaste, 1100 ppm F (1100F), 1100F + 0.5% micrometric HMP (1100F/HMP), and 1100F + 0.5% nano-sized HMP (1100F/HMPnano). The percentage of surface hardness loss (%SH), integrated loss of subsurface hardness (ΔKHN), and enamel calcium (Ca), phosphorus (P), and fluoride (F) were determined. Moreover, biofilms formed on the blocks were analyzed for F, Ca, P, and insoluble extracellular polysaccharide (EPS) concentrations. Data were analyzed using one-way ANOVA, followed by Student-Newman-Keuls' test (p < 0.001). RESULTS: 1100F/HMPnano promoted the lowest %SH and ΔKHN among all groups (p < 0.001). The addition of HMPnano to 1100F significantly increased Ca concentrations (p < 0.001). The 1100F/HMPnano promoted lower values of EPS when compared with 1100F (~ 70%) (p < 0.001) and higher values of fluoride and calcium in the biofilms (p < 0.001). CONCLUSION: 1100F/HMPnano demonstrated a greater protective effect against enamel demineralization and on the composition of biofilm in situ when compared to 1100F toothpaste. CLINICAL RELEVANCE: This toothpaste could be a viable alternative to patients at high risk of caries.
Assuntos
Cárie Dentária , Fosfatos , Desmineralização do Dente , Cremes Dentais , Animais , Cariostáticos , Bovinos , Estudos Cross-Over , Cárie Dentária/prevenção & controle , Esmalte Dentário , Método Duplo-Cego , Fluoretos , Dureza , Humanos , Fosfatos/uso terapêutico , Desmineralização do Dente/prevenção & controleRESUMO
OBJECTIVES: To evaluate the effects of hexametaphosphate microparticles (mHMP) or nanoparticles (nHMP) incorporated in glass ionomer cement (GIC) on antimicrobial and physico-mechanical properties, fluoride (F) release, and enamel demineralization. MATERIAL AND METHODS: HMP solutions were obtained at concentrations of 1, 3, 6, 9, and 12%, for screening of antimicrobial activity. Next, mHMP or nHMP at 6, 9, and 12% were incorporated into a resin-modified GIC and the antibacterial activity was evaluated. The resistance to diametral tensile and compressive strength, surface hardness, and degree of monomer conversion as well as F and HMP releases of GICs were determined. Furthermore, specimens were attached to enamel blocks and submitted to pH-cycling, and mineral loss was determined. Parametric and non-parametric tests were performed, after checking data homoscedasticity (p < 0.05). RESULTS: HMP solutions at 6, 9, and 12% demonstrated the best antibacterial activity. GIC containing HMP showed better antibacterial effects at 9 and 12% for nHMP. Regarding F and HMP releases, the highest levels of release occurred for groups containing 9 and 12% nHMP. With the increase in HMP concentration, there was lower mineral loss. However, the incorporation of mHMP or nHMP in GIC reduced values of physico-mechanical properties when compared to the control GIC. CONCLUSIONS: nHMP improves antimicrobial activity and fluoride release, and decreases enamel demineralization, but reduces the physico-mechanical properties of GIC. CLINICAL RELEVANCE: The association of GIC/HMP could be an alternative material for patients at high risk for dental caries and could be indicated for low-stress regions or provisional restorations.
Assuntos
Antibacterianos/química , Esmalte Dentário/efeitos dos fármacos , Cimentos de Ionômeros de Vidro/química , Fosfatos/química , Animais , Bovinos , Cárie Dentária , Fluoretos/química , Concentração de Íons de Hidrogênio , Teste de Materiais , Desmineralização do Dente/prevenção & controleRESUMO
This study aimed to synthesize and characterize materials containing silver nanoparticles (AgNP) with polyphosphates (sodium trimetaphosphate (TMP) or sodium hexametaphosphate (HMP), and evaluate their effect against Candida albicans and Streptococcus mutans. The minimum inhibitory concentration (MIC) was determined, which was followed by the quantification of the biofilm by counting colony-forming units (CFUs), the amount of metabolic activity, and the total biomass. The MICs revealed greater effectiveness of composites containing 10% Ag (TMP + Ag10% (T10) and HMP + Ag10% (H10)) against both microorganisms. It was observed that T10 and H10 reduced the formation of biofilms by 56-76% for C. albicans and by 52-94% for S. mutans for total biomass and metabolic activity. These composites promoted significant log reductions in the number of CFUs, between 0.45-1.43 log10 for C. albicans and 2.88-3.71 log10 for S. mutans (p < .001). These composites demonstrated significant antimicrobial activity, especially against S. mutans, and may be considered a potential alternative for new dental materials.