Improvement in mechanical strength and biological function of 3D-printed trimagnesium phosphate bioceramic scaffolds by incorporating strontium orthosilicate.

Trimagnesium phosphate (TMP) bioceramic scaffolds are deemed as promising bone grafts, but their mechanical and biological properties are yet to be improved. In the study, strontium orthosilicate (SrOS) was used to modify the TMP scaffolds, whose macroporous structure was constructed by the filament deposition-type 3D printing method. The new phases of SrMg2(PO4)2 and Sr2MgSi2O7, which showed nanocrystalline topography, were produced in the 3D-printed TMP/SrOS bioceramic composite scaffolds. The compressive strength (1.8-64.1 MPa) and porosity (39.7%-71.4%) of the TMP/SrOS scaffolds could be readily tailored by changing the amounts of SrOS additives and the sintering temperature. The TMP/SrOS scaffolds gradually degraded in the aqueous solution, consequently releasing ions of magnesium, strontium and silicon. In contrast with the TMP scaffolds, the TMP/SrOS bioceramic scaffolds had profoundly higher compressive strength, and enhanced cell proliferative and osteogenic activities. The TMP/SrOS scaffolds incorporated with 5 wt% SrOS had the highest mechanical strength and beneficial cellular function, which made them promising for treating different sites of bone defects.

Improving the osseointegration and soft tissue sealing of zirconia ceramics by the incorporation of akermanite via sol infiltration for dental implants.

Zirconia ceramics are promising dental implant materials due to their high-grade biocompatibility, high mechanical strength, and distinctive aesthetic appearance. Nevertheless, zirconia ceramics are bio-inert with a lack of osseointegration and soft tissue sealing, which limits dental implant applications. As such, the fabrication of zirconia ceramics with high mechanical strength, excellent osseointegration and soft tissue sealing performance remains a great challenge in the dental restoration field. In this article, a novel zirconia ceramic with akermanite (AKT) modification by the negative pressure infiltration method is presented. The effects of AKT sol infiltration at different times on the morphology, phase composition, mechanical properties, bioactivity, osseointegration and soft tissue sealing of the modified zirconia ceramics have been systematically investigated. The modified zirconia ceramics feature excellent mechanical properties and significantly improved surface roughness, hydrophilia, and apatite mineralization ability as compared with unmodified zirconia ceramics. Furthermore, cell-culture experiment results indicated that the surface modification of zirconia ceramics could promote adhesion, spreading, migration, proliferation and osteogenic differentiation of mouse bone marrow stromal stem cells (mBMSCs), as well as the early adhesion, spreading, proliferation and fibroblast differentiation of human gingival fibroblasts (HGFs) in vitro. The prepared bioactive zirconia distinctively enhanced the alkaline phosphate (ALP) activity, osteogenesis-related gene expression of mBMSCs and fibroblast-related-gene expression of HGFs. The in vivo evaluation confirmed that 15-TZP ceramics could promote bone-implant osseointegration to the greatest extent as compared with pure zirconia ceramics. To conclude, our research has shown that AKT-modified zirconia ceramics can achieve bone integration and soft tissue sealing, indicating that they have a lot of potential for application as a novel dental implant material in the clinical setting.

Fabrication of 3D printed Ca3Mg3(PO4)4-based bioceramic scaffolds with tailorable high mechanical strength and osteostimulation effect.

Calcium, magnesium and phosphate are predominant constituents in the human bone. In this study, magnesium-calcium phosphate composite bioceramic scaffolds were fabricated utilizing Mg3(PO4)2 and ß-Ca3(PO4)2 as starting materials, and their pore structure was constructed by 3D printing. The porosity and compressive strength of the composite bioceramic scaffolds could be adjusted by altering the sintering temperature and the formula of starting materials. The composite bioceramic scaffolds prepared from 60 wt% Mg3(PO4)2 and 40 wt% ß-Ca3(PO4)2 were dominated by the Ca3Mg3(PO4)4 phase, and this Ca3Mg3(PO4)4-based bioceramic scaffolds possessed the highest compressive strength (12.7 - 92.4 MPa). Moreover, the Ca3Mg3(PO4)4-based bioceramic scaffolds stimulated cellular growth and osteoblastic differentiation of bone marrow stromal cells. The Ca3Mg3(PO4)4-based bioceramic scaffolds as bone regenerative biomaterials are flexible to the requirement of bone defects at various sites.