Mesoporous layer-by-layer ordered nanohybrids of layered double hydroxide and layered metal oxide: highly active visible light photocatalysts with improved chemical stability.

Mesoporous layer-by-layer ordered nanohybrids highly active for visible light-induced O(2) generation are synthesized by self-assembly between oppositely charged 2D nanosheets of Zn-Cr-layered double hydroxide (Zn-Cr-LDH) and layered titanium oxide. The layer-by-layer ordering of two kinds of 2D nanosheets is evidenced by powder X-ray diffraction and cross-sectional high resolution-transmission electron microscopy. Upon the interstratification process, the original in-plane atomic arrangements and electronic structures of the component nanosheets remain intact. The obtained heterolayered nanohybrids show a strong absorption of visible light and a remarkably depressed photoluminescence signal, indicating an effective electronic coupling between the two component nanosheets. The self-assembly between 2D inorganic nanosheets leads to the formation of highly porous stacking structure, whose porosity is controllable by changing the ratio of layered titanate/Zn-Cr-LDH. The resultant heterolayered nanohybrids are fairly active for visible light-induced O(2) generation with a rate of ∼1.18 mmol h(-1) g(-1), which is higher than the O(2) production rate (∼0.67 mmol h(-1) g(-1)) by the pristine Zn-Cr-LDH material, that is, one of the most effective visible light photocatalysts for O(2) production, under the same experimental condition. This result highlights an excellent functionality of the Zn-Cr-LDH-layered titanate nanohybrids as efficient visible light active photocatalysts. Of prime interest is that the chemical stability of the Zn-Cr-LDH is significantly improved upon the hybridization, a result of the protection of the LDH lattice by highly stable titanate layer. The present findings clearly demonstrate that the layer-by-layer-ordered assembly between inorganic 2D nanosheets is quite effective not only in improving the photocatalytic activity of the component semiconductors but also in synthesizing novel porous LDH-based hybrid materials with improved chemical stability.

Controlled release of donepezil intercalated in smectite clays.

The inorganic-organic hybrid for a drug delivery system was successfully realized by intercalating donepezil molecules into smectite clays (laponite XLG, saponite, and montmorillonite). According to the powder XRD patterns, TG profiles, and FT-IR spectra, it was confirmed that donepezil molecules were well stabilized in the interlayer space of clay via mono or double layer stacking. The adsorption amount and molecular structure of donepezil appeared to depend on the cation exchange capacity of the clay, which in turn, tailored the drug release patterns. Especially in the presence of a bulky cationic polymer (Eudragit E-100) in the release media, the release rate was found to be improved due to its effective replacement with intercalated donepezil molecules. Therefore, to formulate a complete drug delivery system, the hybrids were coated with Eudragit E-100 using a spray dryer, which also showed great enhancement in the release rate during a short period of time (180min).

Enhanced contrast of electrochromic full cell systems with nanocrystalline PEDOT-prussian blue.

Poly-(3,4-ethylenedioxythiophene) (PEDOT) is an ideal polymer for electrochromic (EC) devices due to its fast response time, high conductivity, and facile fabrication in a doped form except its demerit like an optical contrast limitation. In this study, we developed a simple way to overcome low coloration efficiency of PEDOT through fabricating a complementary PEDOT and prussian blue full cell system. Fundamental properties of EC displays, such as optical contrast, coloration efficiency, and switching speed, could be successfully optimized by controlling the deposition time and applied voltage during EDOT polymerization. In particular, UV transmittance spectra indicated that the optical contrast was enhanced up to 31 approximately 99% at the wavelength of 600 nm. Scanning electron microscopy images showed that the optimized PEDOT and prussian blue films were deposited on ITO glass substrate with an uniform thickness of approximately 180 nm and approximately 190 nm, respectively. Moreover, according to the circuit analysis, the average response time of electric current for the optimized full cell system was about 400 ms. It is, therefore, concluded that such a full cell system could have high potential applications as smart windows and/or optical devices.

A dual-polymer electrochromic device with high coloration efficiency and fast response time: poly(3,4-(1,4-butylene-(2-ene)dioxy)thiophene)-polyaniline ECD.

A new dual-polymer electrochromic device (ECD) composed of poly(3,4-(1,4-butylene-(2-ene)dioxy)thiophene) (PBueDOT) and polyaniline (PANI) with a hydrophobic molten salt electrolyte has been developed. To build this system, an alkylenedioxy ring in the BueDOT backbone was expanded to include a strongly electron-donating alkylenedioxy bridge, and the thickness and surface morphology of the corresponding PBueDOT film were controlled systematically. Not only the dual-electrochromic-polymer-electrode system, but also the expanded alkylenedioxy ring in the BueDOT backbone, synergistically improved the electrochromic performance. From the coloration efficiency (CE) value calculations, we found that the CE was enhanced up to 930 cm(2) C(-1). Furthermore, these ECDs showed an extremely fast response time of less than 80 ms.

Unilamellar nanosheet of layered manganese cobalt nickel oxide and its heterolayered film with polycations.

The exfoliation of layered Li[Mn(1/3)Co(1/3)Ni(1/3)]O(2) into individual monolayers could be achieved through the intercalation of quaternary tetramethylammonium (TMA(+)) ions into protonated metal oxide. An effective exfoliation occurred when the TMA(+)/H(+) ratio was 0.5-50. Reactions outside this range produced no colloidal suspension, but all the manganese cobalt nickel oxides precipitated. Atomic force microscopy and transmission electron microscopy clearly demonstrated that exfoliated manganese cobalt nickel oxide nanosheets have a nanometer-level thickness, underscoring the formation of unilamellar nanosheets. The maintenance of the hexagonal atomic arrangement of the manganese cobalt nickel oxide layer upon the exfoliation was confirmed by selected area electron diffraction analysis. According to diffuse reflectance ultraviolet--visible spectroscopy, the exfoliated manganese cobalt nickel oxides displayed distinct absorption peaks at approximately 354 and approximately 480 nm corresponding to the d-d transitions of octahedral metal ions, which contrasted with the featureless spectrum of the pristine metal oxide. In the light of zeta potential data showing the negative surface charge of manganese cobalt nickel oxide nanosheets, a heterolayered film of manganese cobalt nickel oxide and conductive polymers could be prepared through the successive coating process with colloidal suspension and polycations. The UV--vis and X-ray diffraction studies verified the layer-by-layer ordered structure of the obtained heterolayered film, respectively.