Comparative analysis of the retention force and deformation of PEEK and PEKK removable partial denture clasps with different thicknesses and undercut depths.

STATEMENT OF PROBLEM: The retentive force and deformation of milled polyetheretherketone (PEEK) and polyetherketoneketone (PEKK) removable partial denture (RPD) frameworks are not well understood. PURPOSE: The purpose of this in vitro study was to assess the retentive force and deformation of PEEK and PEKK Akers clasps with different designs and undercut depths. MATERIAL AND METHODS: A master model containing the first and second molar abutments was used to design Akers clasps of different cross-sectional dimensions, undercut depths (0.5 and 0.75 mm), and materials. The components of the removable partial denture framework also included an occlusal rest and were manufactured using a milling machine (n=5). The fatigue resistance of the Akers clasps was measured before and after deformation regarding the retentive forces. RESULTS: The PEEK2-U50 clasp had the largest retentive force with no significant difference among all groups before and after the insertion and removal cycle. In addition, the increased cross-sectional dimensions of the design resulted in significant differences in retentive forces between the PEEK1 and PEEK2 groups and between the PEEK and PEKK materials. CONCLUSIONS: Increasing the clasp's cross-sectional dimensions significantly impacted retentive forces, especially between different PEEK groups and between PEEK and PEKK materials.

Effect of thickness of externally characterized stains on optical properties of high-translucency zirconia.

OBJECTIVES: There is insufficient information about the effects of the thickness of externally characterized stains or glazes on CIELAB color parameters and the translucency parameter (TP) of 5 mol% yttria partially stabilized zirconia (5Y-PSZ). The present study evaluated the effect of a thickness reduction of the externally characterized or glazed layer on its CIE2000 color parameters and TP00 of 5Y-PSZ. MATERIALS AND METHODS: Twenty-eight specimens were sectioned from 5Y-PSZ blanks. Three brands of powdered stains (namely VI, SH, and IV) and a glaze (GL) were used to extrinsically stain the specimen surfaces (n = 7 per group). After measuring the final thickness and color, specimens of each group were carefully ground and finally polished. The reduced thickness was carefully controlled in decrements of 0.02 mm on the characterized stains or glazed layers at each reduction cycle until the surface of the un-stained zirconia was exposed. The CIELAB color parameters of specimens were measured using a spectrophotometer. Subsequently, differences in lightness (∆L'), chroma (∆C'), and hue (∆H'), and TP00 values and color differences (ΔE00) were calculated using the CIEDE2000 formula to determine differences between the specimen and the un-stained zirconia at each reduction cycle. A paired-samples t-test, two-way mixed-design analysis of variance, and Pearson correlation coefficient were used to analyze the data (α = 0.05). RESULTS: There were no significant differences in lightness, chroma, hue, or TP00 values before or after glazing or after each reduction cycle of the glazed layer. Mean ΔE00 values ranged between 20.94 and 33.55 after applying the externally characterized stains. With a decreased thickness of the characterized stain layer, there were observed that significant decreases in ∆L', ∆H', ∆C', and ΔE00, and significant increases in TP00. CONCLUSIONS: Increasing the thickness of externally characterized stains decreased the lightness and caused the alternation of chroma and hue, whereas these phenomena were not observed in the glazed group. There was a slight change of CIE2000 color parameters and TP00 when the thickness of the characterized layer exceeded 0.06 mm. CLINICAL RELEVANCE: The application and thickness of externally characterized stains can sensitively affect CIE2000 color parameters and translucency of 5Y-PSZ.

Effect of toothbrushing on the optical properties and surface roughness of extrinsically stained high-translucency zirconia.

OBJECTIVES: The effect of toothbrushing on the color, relative translucency, and surface roughness of extrinsically stained zirconia dental restorations is still unclear. The purpose of the present study was to evaluate the optical properties and surface textures of extrinsically stained or glazed partially stabilized zirconia with 5 mol% yttria (5Y-PSZ) after toothbrushing by determining changes in the color, translucency parameter (TP), and surface roughness. MATERIALS AND METHODS: Specimens (2 mm thick; n = 50) were sectioned from 5Y-PSZ blanks. Three brands of powdered stains (namely VI, SH, IV) and a glaze (GL) were used to extrinsically stain the specimen surfaces (n = 10 per group). The specimens were subjected to 10,000-50,000 simulated toothbrushing strokes using a toothpaste slurry (Ora2 PREMIUM Stain clear paste). The color parameters were measured before staining or glazing and before and after simulated brushing. The color changes and TP values can be calculated before and after simulated brushing. The surface roughness was also evaluated. RESULTS: Significant changes were found in the shade and TP values of 5Y-PSZ after extrinsic staining, but no significant changes were found after toothbrushing, irrespective of the staining brand (p > 0.05). The surface roughness of the characterized 5Y-PSZ specimens decreased after toothbrushing, whereas that of the non-characterized 5Y-PSZ group increased. CONCLUSIONS: Toothbrushing markedly affects the surface roughness of extrinsically stained or glazed 5Y-PSZ specimens, whereas no impacts on the color or translucency were observed. CLINICAL RELEVANCE: For esthetic reasons, clinicians and dental technicians prefer to apply extrinsic stains to zirconia restorations, which profoundly affects its appearance. The limited influence of toothbrushing on color and translucency of 5Y-PSZ is promising for clinical applications.

Microstructure, mechanical properties, and retentive forces of cobalt-chromium removable partial denture frameworks fabricated by selective laser melting followed by heat treatment.

STATEMENT OF PROBLEM: The effect of heat treatment on the microstructure and mechanical properties of cobalt-chromium (Co-Cr) removable partial denture (RPD) frameworks fabricated by selective laser melting (SLM) is not well understood. PURPOSE: The purpose of this in vitro study was to evaluate the suitability of SLM-fabricated Co-Cr alloys followed by heat treatment as a framework for RPDs by determining the microstructure and mechanical properties. MATERIAL AND METHODS: Dumbbell specimens and RPD frameworks were fabricated by using SLM followed by heat treatment. The effects of the heat treatment on the microstructure were studied by using optical microscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD). Tensile and insertion and removal tests were performed to study the mechanical responses of selective laser melting followed by heat treatment specimens, including the ultimate tensile strength (UTS), 0.2% yield strength (0.2% YS), elongation (E), and retentive forces. Specimens fabricated by using the traditional lost-wax process were used as a control (casting) group. RESULTS: X-ray diffraction indicated that the γ-face-centered cubic phase dominated SLM and selective laser melting followed by heat treatment specimens. Results from optical microscopy and SEM showed microstructural changes under different fabrication and postprocessing heat treatments; it was difficult to observe the grain boundary in the SLM group, whereas submicrometer-scale grains had formed in the selective laser melting followed by heat treatment group. The selective laser melting followed by heat treatment group exhibited the highest elongation and retentive forces compared with the casting and SLM groups. CONCLUSIONS: SLM increased the mechanical properties of Co-Cr alloys. Postprocessing heat treatment further enhanced the tensile ductility. It is suggested that SLM followed by heat treatment is an efficient strategy for fabricating RPD frameworks.

Trueness of removable partial denture frameworks additively manufactured with selective laser melting.

STATEMENT OF PROBLEM: Although studies have reported on selective laser melting (SLM)-fabricated removable partial dentures (RPDs), research addressing the trueness of SLM-fabricated RPD metal frameworks is sparse. PURPOSE: The purpose of this in vitro study was to evaluate the trueness of powdered cobalt-chromium (Co-Cr) or titanium-6 aluminum-4 vanadium (Ti-6Al-4V) alloy frameworks for RPDs fabricated by SLM. MATERIAL AND METHODS: A digital scan of a Kennedy class II mandible typodont was obtained to design an RPD framework by using a computer-aided design (CAD) software program (denoted as CRF). Two experimental groups of frameworks were fabricated from the CRF by using SLM in alloys of Co-Cr (SLM-Co-Cr, n=6) and in Ti-6Al-4V (SLM-Ti-6Al-4V, n=6) while a control group was fabricated by using traditional lost-wax casting following stereolithography (CA-Co-Cr, n=6). In total, 18 RPD frameworks were digitally scanned (denoted as CRF), with each scan then superimposed on the CRF and evaluated for discrepancies by using a 3D analysis software program. A nonparametric Kruskal-Wallis test was performed to determine differences in trueness among groups (α=.05). RESULTS: The CA-Co-Cr group showed the highest discrepancy between CEF and CRF. Statistically significant differences were found between the CA-Co-Cr and SLM-fabricated groups (P=.03 for Co-Cr, and P=.016 for Ti-6Al-4V). However, no significant difference was found between the SLM-Co-Cr and SLM-Ti-6Al-4V groups (P=.787). CONCLUSIONS: SLM-fabricated RPD frameworks exhibited higher trueness than CA-Co-Cr fabricated ones, indicating the potential of selective laser melting to produce the geometric shapes required for accurate dental restorations.

Effect of Different Bone Grafting Materials and Mesenchymal Stem Cells on Bone Regeneration: A Micro-Computed Tomography and Histomorphometric Study in a Rabbit Calvarial Defect Model.

This study evaluated the new bone formation potential of micro-macro biphasic calcium phosphate (MBCP) and Bio-Oss grafting materials with and without dental pulp-derived mesenchymal stem cells (DPSCs) and bone marrow-derived mesenchymal stem cells (BMSCs) in a rabbit calvarial bone defect model. The surface structure of the grafting materials was evaluated using a scanning electron microscope (SEM). The multipotent differentiation characteristics of the DPSCs and BMSCs were assessed. Four circular bone defects were created in the calvarium of 24 rabbits and randomly allocated to eight experimental groups: empty control, MBCP, MBCP+DPSCs, MBCP+BMSCs, Bio-Oss+DPSCs, Bio-Oss+BMSCs, and autogenous bone. A three-dimensional analysis of the new bone formation was performed using micro-computed tomography (micro-CT) and a histological study after 2, 4, and 8 weeks of healing. Homogenously porous structures were observed in both grafting materials. The BMSCs revealed higher osteogenic differentiation capacities, whereas the DPSCs exhibited higher colony-forming units. The micro-CT and histological analysis findings for the new bone formation were consistent. In general, the empty control showed the lowest bone regeneration capacity throughout the experimental period. By contrast, the percentage of new bone formation was the highest in the autogenous bone group after 2 (39.4% ± 4.7%) and 4 weeks (49.7% ± 1.5%) of healing (p < 0.05). MBCP and Bio-Oss could provide osteoconductive support and prevent the collapse of the defect space for new bone formation. In addition, more osteoblastic cells lining the surface of the newly formed bone and bone grafting materials were observed after incorporating the DPSCs and BMSCs. After 8 weeks of healing, the autogenous bone group (54.9% ± 6.1%) showed a higher percentage of new bone formation than the empty control (35.3% ± 0.5%), MBCP (38.3% ± 6.0%), MBCP+DPSC (39.8% ± 5.7%), Bio-Oss (41.3% ± 3.5%), and Bio-Oss+DPSC (42.1% ± 2.7%) groups. Nevertheless, the percentage of new bone formation did not significantly differ between the MBCP+BMSC (47.2% ± 8.3%) and Bio-Oss+BMSC (51.2% ± 9.9%) groups and the autogenous bone group. Our study results demonstrated that autogenous bone is the gold standard. Both the DPSCs and BMSCs enhanced the osteoconductive capacities of MBCP and Bio-Oss. In addition, the efficiency of the BMSCs combined with MBCP and Bio-Oss was comparable to that of the autogenous bone after 8 weeks of healing. These findings provide effective strategies for the improvement of biomaterials and MSC-based bone tissue regeneration.

Prophylactic supplement with melatonin successfully suppresses the pathogenesis of periodontitis through normalizing RANKL/OPG ratio and depressing the TLR4/MyD88 signaling pathway.

Periodontitis (PD) is an inflammatory disease characterized by gingival inflammation and resorption of alveolar bone. Impaired receptor activator of nuclear factor-kappa B ligand/osteoprotegerin (RANKL/OPG) signaling caused by enhanced production of pro-inflammatory cytokines plays an essential role in the pathogenesis of PD. Considering melatonin possesses significant anti-inflammatory property, this study aimed to determine whether prophylactic treatment with melatonin would effectively normalize RANKL/OPG signaling, depress toll-like receptor 4/myeloid differentiation factor 88 (TLR4/MyD88)-mediated pro-inflammatory cytokine activation, and successfully suppress the pathogenesis of PD. PD was induced in adult rats by placing the ligature at molar subgingival regions. Fourteen days before PD induction, 10, 50, or 100 mg/kg of melatonin was intraperitoneally injected for consecutive 28 days. Biochemical and enzyme-linked immunosorbent assay were used to detect TLR4/MyD88 activity, RANKL, OPG, interleukin 1ß, interleukin 6, and tumor necrosis factor-α levels, respectively. The extent of bone loss, bone mineral intensity, and calcium intensity was further evaluated by scanning electron microscopy, micro-computed tomography, and energy-dispersive X-ray spectroscopy. Results indicated that high RANKL/OPG ratio, TLR4/MyD88 activity, and pro-inflammatory cytokine levels were detected following PD. Impaired biochemical findings paralleled well with severe bone loss and reduced calcium intensity. However, in rats pretreated with melatonin, all above parameters were successfully returned to nearly normal levels with maximal change observed in rats receiving 100 mg/kg. As prophylactic treatment with melatonin effectively normalizes RANKL/OPG signaling by depressing TLR4/MyD88-mediated pro-inflammatory cytokine production, dietary supplement with melatonin may serve as an advanced strategy to strengthen oral health to counteract PD-induced destructive damage.

Effects of two surface finishes on the color of cemented and colored anatomic-contour zirconia crowns.

STATEMENT OF PROBLEM: The esthetic appearance of anatomic-contour zirconia restorations is influenced by the shade of the coloring liquid and the optical properties of the luting cements. However, few studies are available on the effects of surface-finishing methods and luting cements on colored anatomic-contour zirconia restorations. PURPOSE: The purpose of this in vitro study was to investigate the effects of surface finishing methods on the color distribution of colored anatomic-contour zirconia crowns before and after being cemented onto abutments. MATERIAL AND METHODS: Implant-supported anatomic-contour zirconia premolar crowns were fabricated and immersed in A3-coloring liquid for 30 seconds. The colored zirconia crowns were separated into 3 groups according to the method of surface treatment: no treatment (N), polishing (P), and glazing (G). The zirconia crowns without coloring liquid application served as the control group. CIELab color coordinates were obtained, and color differences (ΔE) between shaded crowns were calculated with a spectrophotometer. The color stability of the crown before and after cement application was also investigated. RESULTS: Before cement application, the mean color difference between groups N and P was 2.85 ΔE units, whereas the mean ΔE value between groups N and G was 3.27. Mean ΔE values with and without cement application among groups ranged from 2.75 to 3.45 ΔE units. CONCLUSIONS: The color appearance of the colored zirconia crowns was strongly influenced by the surface-finishing methods and luting cement application.

In vitro study of optimal removable partial denture clasp design made from novel high-performance polyetherketoneketone.

PURPOSE: This study aimed to investigate the retentive force and deformation of double Akers' polyetherketoneketone (PEKK) clasps on removable partial dentures (RPDs) with varying designs and undercut depths. METHODS: Thirty double Akers' PEKK clasps with two different widths and heights (Groups I and II) were fabricated using computer-aided design and computer-aided manufacturing (CAD/CAM). Each design was further subdivided (n = 5) into three undercut depths (0.25, 0.50, and 0.75 mm). The retentive force of the clasps was measured after 10 years of clinical use (15,000 insertion/removal cycles), and the deformation of the clasp tips was analyzed before and after cycling. RESULTS: Clasps with 0.50-mm and 0.75-mm undercut depths exhibited greater initial retentive forces (3.15-3.51 N) compared to those in the 0.25-mm undercut group (2.40-2.80 N). Group I maintained consistent retentive forces over the cycles (P = 0.345), whereas Group II showed declining forces after the initial use (P < 0.003). In both groups, the 0.50-mm undercut exhibited a greater retentive force than the 0.25-mm (P < 0.001 and P < 0.004, respectively), with no significant differences between the 0.50-mm and 0.75-mm undercut depths. Despite a lower initial retentive force, the 0.25-mm undercut showed less deformation and clasp tip wear. CONCLUSIONS: The PEKK clasps did not exhibit significantly reduced retentive forces or permanent deformations after 15,000 fatigue cycles. These results suggest that the PEKK polymer displays superior mechanical properties as an esthetic clasp material, and clasps with 0.50-mm and 0.75-mm undercut depths are recommended for long-term clinical use.

Establishing a novel deep learning model for detecting peri-implantitis.

BACKGROUND/PURPOSE: The diagnosis of peri-implantitis using periapical radiographs is crucial. Recently, artificial intelligence may apply in radiographic image analysis effectively. The aim of this study was to differentiate the degree of marginal bone loss of an implant, and also to classify the severity of peri-implantitis using a deep learning model. MATERIALS AND METHODS: A dataset of 800 periapical radiographic images were divided into training (n = 600), validation (n = 100), and test (n = 100) datasets with implants used for deep learning. An object detection algorithm (YOLOv7) was used to identify peri-implantitis. The classification performance of this model was evaluated using metrics, including the specificity, precision, recall, and F1 score. RESULTS: Considering the classification performance, the specificity was 100%, precision was 100%, recall was 94.44%, and F1 score was 97.10%. CONCLUSION: Results of this study suggested that implants can be identified from periapical radiographic images using deep learning-based object detection. This identification system could help dentists and patients suffering from implant problems. However, more images of other implant systems are needed to increase the learning performance to apply this system in clinical practice.

Development of a zinc chloride-based chemo-mechanical system for potential minimally invasive dental caries removal system.

Background/purpose: The chemo-mechanical caries-removal technique is known to offer advantages of selective dentin caries treatment while leaving healthy dental tissues intact. However, current sodium hypochlorite based reagents usually excessively damage dentin collagen. Therefore, the purpose of this study was to develop a novel chemo-mechanical caries-removal system to preserve the collagen network for subsequent prosthetic restorations. Materials and methods: The calfskin-derived collagen was chosen as a model system to investigate the dissolution behavior of collagen under different operating conditions of chemical-ultrasonic treatment systems. The molecular weight, triple-helix structure, the morphology, and functional group of collagen after treatment were investigated. Results: Various concentrations of sodium hypochlorite or zinc chloride together with ultrasonic machinery were chosen to investigate. The outcomes of circular dichroism (CD) spectra demonstrated stability of the triple-helix structure after treatment of a zinc chloride solution. In addition, two apparent bands at molecular weights (MWs) of 130 and 121 kDa evidenced the stability of collagen network. The positive 222 nm and 195 nm negative CD absorption band indicated the existence of a triple-helix structure for type I collagen. The preservation of the morphology and functional group of the collagen network on the etched dentin surface were investigated by in vitro dentin decalcification model. Conclusion: Unlike NaOCl, the 5 wt% zinc chloride solution combined with ultra-sonication showed dissolution rather than denature as well as degradation of the dentin collagen network. Additional in vivo evaluations are needed to verify its usefulness in clinical applications.

Characterization and Antibacterial Properties of Polyetherketoneketone Coated with a Silver Nanoparticle-in-Epoxy Lining.

Polyetherketoneketone (PEKK) is an alternative material for use in removable partial denture frameworks; these frameworks must exhibit antibacterial properties to reduce the risk of periodontal disease. In the present study, silver nanoparticles (AgNPs) were synthesized via the reduction of silver nitrate with sodium borohydride in a solution containing polyvinyl pyrrolidone (PVP). Transmission electron microscope images and dynamic light scattering confirmed that metallic nanoparticles had been created with an average size of 32 nm. Furthermore, the coating of the PEKK polymeric substrate with 0.5% AgNPs was carried out using an epoxy resin lining at room temperature. Fourier transform infrared (FTIR) spectra confirmed the successful transfer of the AgNP-in-resin lining onto the polymeric substrate. Scanning electron microscopy and atomic force microscopy confirmed that the AgNPs had been uniformly deposited onto the PEKK specimens. Finally, the antibacterial activity of the specimens was tested against Porphyromonas gingivalis. An inhibition zone of 22.5 mm and an antibacterial rate of 83.47% were found for the PEKK coated with 0.5% AgNPs (0.5% Ag-PEKK) compared to an untreated polyetheretherketone (PEEK) substrate, evidencing that 0.5% Ag-PEKK has potential antibacterial properties for implant applications.

Mechanical Properties and Biocompatibility of Urethane Acrylate-Based 3D-Printed Denture Base Resin.

In this study, five urethane acrylates (UAs), namely aliphatic urethane hexa-acrylate (87A), aromatic urethane hexa-acrylate (88A), aliphatic UA (588), aliphatic urethane triacrylate diluted in 15% HDD (594), and high-functional aliphatic UA (5812), were selected to formulate five UA-based photopolymer resins for digital light processing (DLP)-based 3D printing. Each UA (40 wt%) was added and blended homogenously with ethoxylated pentaerythritol tetraacrylate (40 wt%), isobornyl acrylate (12 wt%), diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide (3 wt%), and a pink acrylic (5 wt%). Each UA-based resin specimen was designed using CAD software and fabricated using a DLP 3D printer to specific dimensions. Characteristics, mechanical properties, and cytotoxicity levels of these designed UA-based resins were investigated and compared with a commercial 3D printing denture base acrylic resin (BB base) control group at different UV exposure times. Shore hardness-measurement data and MTT assays were analyzed using a one-way analysis of variance with Bonferroni's post hoc test, whereas viscosity, maximum strength, and modulus were analyzed using the Kruskal-Wallis test (α = 0.05). UA-based photopolymer resins with tunable mechanical properties were successfully prepared by replacing the UA materials and the UV exposure times. After 15 min of UV exposure, the 5812 and 594 groups exhibited higher viscosities, whereas the 88A and 87A groups exhibited lower viscosities compared with the BB base group. Maximum flexural strength, flexural modulus, and Shore hardness values also revealed significant differences among materials (p < 0.001). Based on MTT assay results, the UA-based photopolymer resins were nontoxic. In the present study, mechanical properties of the designed photopolymer resins could be adjusted by changing the UA or UV exposure time, suggesting that aliphatic urethane acrylate has good potential for use in the design of printable resins for DLP-type 3D printing in dental applications.

Rehardening and the Protective Effect of Gamma-Polyglutamic Acid/Nano-Hydroxyapatite Paste on Surface-Etched Enamel.

Many revolutionary approaches are on the way pertaining to the high occurrence of tooth decay, which is an enduring challenge in the field of preventive dentistry. However, an ideal dental care material has yet to be fully developed. With this aim, this research reports a dramatic enhancement in the rehardening potential of surface-etched enamels through a plausible synergistic effect of the novel combination of γ-polyglutamic acid (γ-PGA) and nano-hydroxyapatite (nano-HAp) paste, within the limitations of the study. The percentage of recovery of the surface microhardness (SMHR%) and the surface parameters for 9 wt% γ-PGA/nano-HAp paste on acid-etched enamel were investigated with a Vickers microhardness tester and an atomic force microscope, respectively. This in vitro study demonstrates that γ-PGA/nano-HAp treatment could increase the SMHR% of etched enamel to 39.59 ± 6.69% in 30 min. To test the hypothesis of the rehardening mechanism and the preventive effect of the γ-PGA/nano-HAp paste, the surface parameters of mean peak spacing (Rsm) and mean arithmetic surface roughness (Ra) were both measured and compared to the specimens subjected to demineralization and/or remineralization. After the treatment of γ-PGA/nano-HAp on the etched surface, the reduction in Rsm from 999 ± 120 nm to 700 ± 80 nm suggests the possible mechanism of void-filling within a short treatment time of 10 min. Furthermore, ΔRa-I, the roughness change due to etching before remineralization, was 23.15 ± 3.23 nm, while ΔRa-II, the roughness change after remineralization, was 11.99 ± 3.90 nm. This statistically significant reduction in roughness change (p < 0.05) implies a protective effect against the demineralization process. The as-developed novel γ-PGA/nano-HAp paste possesses a high efficacy towards tooth microhardness rehardening, and a protective effect against acid etching.

Surface Modified ß-Tricalcium phosphate enhanced stem cell osteogenic differentiation in vitro and bone regeneration in vivo.

A major number of studies have demonstrated Beta-tricalcium phosphate (ß-TCP) biocompatibility, bioactivity, and osteoconductivity characteristics in bone regeneration. The aim of this research was to enhance ß-TCP's biocompatibility, and evaluate its physicochemical properties by argon glow discharge plasma (GDP) plasma surface treatment without modifying its surface. Treated ß-TCP was analyzed by scanning electron microscopy (SEM), energy-dispersive spectrometry, X-ray photoelectron spectroscopy (XPS), X-ray diffraction analysis, and Fourier transform infrared spectroscopy characterization. To evaluate treated ß-TCP biocompatibility and osteoblastic differentiation, water-soluble tetrazolium salts-1 (WST-1), immunofluorescence, alkaline phosphatase (ALP) assay, and quantitative real-time polymerase chain reaction (QPCR) were done using human mesenchymal stem cells (hMSCs). The results indicated a slight enhancement of the ß-TCP by GDP sputtering, which resulted in a higher Ca/P ratio (2.05) than the control. Furthermore, when compared with control ß-TCP, we observed an improvement of WST-1 on all days (p < 0.05) as well as of ALP activity (day 7, p < 0.05), with up-regulation of ALP, osteocalcin, and Osteoprotegerin osteogenic genes in cells cultured with the treated ß-TCP. XPS and SEM results indicated that treated ß-TCP's surface was not modified. In vivo, micro-computed tomography and histomorphometric analysis indicated that the ß-TCP test managed to regenerate more new bone than the untreated ß-TCP and control defects at 8 weeks (p < 0.05). Argon GDP treatment is a viable method for removing macro and micro particles of < 7 µm in size from ß-TCP bigger particles surfaces and therefore improving its biocompatibility with slight surface roughness modification, enhancing hMSCs proliferation, osteoblastic differentiation, and stimulating more new bone formation.

Oral Microbiota Changes in Elderly Patients, an Indicator of Alzheimer's Disease.

Alzheimer's disease (AD) is a neurodegenerative disease that usually affects older individuals. Owing to the higher incidence of root caries and missing teeth in elderly individuals, the bacteria involved in these dental concerns might potentially deteriorate their cognitive function. Altered microbiota in the oral cavity may induce neuroinflammation through migration from the oral cavity to the brain. However, the correlation between the composition of the oral microbiota and neurodegenerative disease remains unclear. In this study, we evaluated sequence to determine the relative abundance and diversity of bacterial taxa in the dental plaque of elderly patients with AD and controls. Oral samples; the DMFT index; and other clinical examination data were collected from 17 patients with AD and 18 normal elderly individuals as the control group. Patients with AD had significantly more missing teeth and higher dental plaque weight but lower microbial diversity than controls. Significantly increased numbers of Lactobacillales, Streptococcaceae, and Firmicutes/Bacteroidetes and a significantly decreased number of Fusobacterium were observed in patients with AD. In conclusion, using the PacBio single-molecule real-time (SMRT) sequencing platform to survey the microbiota dysbiosis biomarkers in the oral cavity of elderly individuals could serve as a tool to identify patients with AD.

Guided Tissue Regeneration Treatment Yields Better Results in Class II Furcations in the Mandible Than in the Maxilla: A Retrospective Study.

Absorbable porcine collagen membrane with a bovine bone graft can be considered for regenerative treatment in periodontal class II furcation defects. We evaluated the clinical efficacy of guided tissue regeneration (GTR) treatment with bovine bone xenograft and a porcine collagen membrane in molars with class II furcations. Probing depth (PD), clinical attachment level (CAL), and bone level (BL) were recorded at baseline and at 3, 6, and 9 months postoperatively. Thirty class II furcation defects from the lower and upper molars were assessed. Significant improvements in PD and CAL were observed from baseline to 9 months in all groups (p < 0.01). BL improved in all groups except group A in the upper molars in radiographic assessment (p < 0.05). The lower and upper molars showed PD reduction of 50.5% ± 7.44% and 46.2% ± 11.2%, respectively, at 9 months (p = 0.044). In furcations of 1-3 mm, the lower and upper molars showed PD reductions of 51.2% ± 4.49% and 36.5% ± 16.14%, respectively (p = 0.035). The lower and upper molars showed a CAL gain of 51.1% ± 4.64% and 33.6% ± 18.8%, respectively (p = 0.037). Thus, GTR with bovine bone graft and porcine collagen membrane yielded good results in class II furcations, with better results in the lower than in the upper molars.

A Silk Fibroin Based Hydration Accelerator for Root Canal Filling Materials.

Mineral trioxide aggregate (MTA) is widely used in various dental endodontic applications such as root-end filling, furcal perforation repair, and vital pulp therapy. In spite of many attempts to improve handling properties and reduce the discoloration of MTA, the ideal root canal filling material has yet to be fully developed. The objective of this study was to investigate the setting time, mechanical properties, and biocompatibility of MTA set by a silk fibroin solution. A 5 wt% silk fibroin (SF) solution (a novel hydration accelerant) was used to set SavDen® MTA and ProRoot® white MTA (WMTA). Changes in setting time, diametral tensile strength (DTS), material crystallization, in vitro cell viability, and cell morphology were assessed by Vicat needle measurement, a universal testing machine, scanning electron microscopy (SEM), and WST-1 assay, respectively. The initial setting time of ProRoot® MTA and SavDen® MTA experienced a drastic decrease of 83.9% and 42.1% when deionized water was replaced by 5 wt% SF solution as the liquid phase. The DTS of SavDen® MTA showed a significant increase after set by the SF solution in 24 h. A human osteoblast-like cell (MG-63)-based WST-1 assay revealed that both ProRoot® MTA and SavDen® MTA hydrated using SF solution did not significantly differ (p > 0.05) in cell viability. MG-63 cells with pseudopodia attachments and nuclear protrusions represent a healthier and more adherent status on the surface of MTA when set with SF solution. The results suggest that the 5 wt% SF solution may be used as an alternative hydration accelerant for MTA in endodontic applications.

In Vitro Analysis of Fibronectin-Modified Titanium Surfaces.

BACKGROUND: Glow discharge plasma (GDP) procedure is an effective method for grafting various proteins, including albumin, type I collagen, and fibronectin, onto a titanium surface. However, the behavior and impact of titanium (Ti) surface modification is yet to be unraveled. PURPOSE: The purpose of this study is to evaluate and analyze the biological properties of fibronectin-grafted Ti surfaces treated by GDP. MATERIALS AND METHODS: Grade II Ti discs were initially cleaned and autoclaved to obtain original specimens. Subsequently, the specimens were GDP treated and grafted with fibronectin to form Ar-GDP (Argon GDP treatment only) and GDP-fib (fibronectin coating following GDP treatment) groups. Blood coagulation test and MG-63 cell culture were performed to evaluate the biological effects on the specimen. RESULTS: There was no significant difference between Ar-GDP and GDP-fib groups in blood compatibility analysis. While in the MTT test, cellular proliferation was benefited from the presence of fibronectin coating. The numbers of cells on Ar-GDP and GDP-fib specimens were greater than those in the original specimens after 24 h of culturing. CONCLUSIONS: GDP treatment combined with fibronectin grafting favored MG-63 cell adhesion, migration, and proliferation on titanium surfaces, which could be attributed to the improved surface properties.

Chair-side quantitative oral-microflora screening for assessing familial correlation of periodontal status and caries prevalence.

AIM: Our goal was to investigate the relationship between clinical status and the presence of carious or periodontal pathogens among parent-child familial pairs. Clinical practices of risk assessment with consideration of familial pathogen interaction might reduce the need for therapy, improve patient outcomes, and ultimately reduce oral disease burden. MATERIALS AND METHODS: In this study, we enrolled 30 parent-child pairs, with the children exhibiting complete deciduous dentition or mixed dentition with only permanent first molars. Clinical statuses were evaluated using caries and periodontal disease indicators, including the sum of decay and the number of missing or filled teeth (DMFT) for adults, decay, extraction caused by dental disease, and filled teeth (deft), for children, probing depth, and plaque control record (PCR). Supra- and sub-gingival bacteria were determined based on semi-quantitative measurements of microbial infection by using data from the Dentocult(®) SM test (caries-related organisms) and the PerioCheck(®) test (periodontal disease-related organisms). RESULTS: No statistically significant relationship was detected between the prevalence of periodontal pathogens and that of cariogenic pathogens in the oral cavity. However, the clinical status of caries (DMFT) was negatively correlated with the clinical status of periodontal disease (pocket depth) in parents who were infected with dominant periodontal pathogens (r = -0.59, p<0.01). Parents' DMFT scores were positively correlated with children's deft and PCR scores. PCR and deft scores of children appeared to decrease significantly with the parent's pocket depth. CONCLUSION: The study showed that the quantity of caries pathogens were not significant related to periodontal pathogens, but the caries clinical outcome is negative related with periodontal clinical outcome between familial pairs.