Construction of Polycarbonates with Pendant Multifunctional Groups via a One-Step CO2/ Diepoxide Copolymerization Approach.

A "one-step" strategy has been demonstrated for the tunable synthesis of multifunctional aliphatic polycarbonates (APCs) with ethylene oxide (EO), ethylene carbonate (EC), and cyclohexene oxide (CHO) side groups by the copolymerization of 4-vinyl-1-cyclohexene diepoxide with carbon dioxide under an aminotriphenolate iron/PPNBz (PPN = bis(triphenylphosphine)-iminium, Bz = benzoate) binary catalyst. By adjusting the PPNBz-to-iron complex ratio and incorporating auxiliary solvents, the content of functional side groups can be tuned within the ranges of 53-75% for EO, 18-47% for EC, and <1-7% for CHO. The yield and molecular weight distribution of the resulting multifunctional APCs are affected by the viscosity of the polymerization system. The use of tetrahydrofuran as an auxiliary solvent enables the preparation of narrow-distribution polycarbonates at high conversion. This work presents a novel perspective for the preparation of tailorable multifunctional APCs.

Synthesis of α-Diimine Complex Enabling Rapidly Covalent Attachment to Silica Supports and Application of Homo-/Heterogeneous Catalysts in Ethylene Polymerization.

For covalent attachment-supported α-diimine catalysts, on the basis of ensuring the thermal stability and activity of the catalysts, the important problem is that the active group on the catalyst can quickly react with the support, anchoring it firmly on the support, shortening the loading time, reducing the negative impact of the support on the active centers, and further improving the polymer morphology, which makes them suitable for use in industrial polymerization temperatures. Herein, we synthesized a α-diimine nickel(II) catalyst bearing four hydroxyl substituents. The hydroxyl substituents enable the catalyst to be immobilized firmly on silica support by covalent linkage in 5-10 min. Compared with the toluene solvent system, the homogeneous catalysts show high activity and thermal stability in hexane solvent at the same conditions. Compared with homogeneous catalysts, heterogeneous catalysis leads to improvements in catalyst lifetime, polymer morphology control, catalytic activity, and the molecular weight of polyethylene (up to 679 kg/mol). The silica-supported catalysts resulted in higher melting temperatures as well as lower branching densities in polyethylenes. Even at 70 °C, the polyethylene prepared by S-CatA-2 still exhibits dispersed particle morphology, and there is no phenomenon of reactor fouling, which is suitable for industrial polymerization processes.

Synthesis of High Molecular Weight Cyclic Poly(ε-caprolactone)s of Variable Ring Size Based on a Light-Induced Ring-Closure Approach.

High molecular weight cyclic poly(ε-caprolactone)s (cPCLs) with variable ring size are synthesized via light-induced ring closure of α,ω-anthracene-terminated PCL (An-PCL-An). The ring size of cPCL is tunable simply by adjusting the polymer concentration from 10 to 100 mg mL(-1) in THF. The cyclo-addition via the bimolecular cyclization of An-PC-An is well characterized by a variety of analyses such as (1) H NMR and UV-vis spectroscopies, gel-permeation chromatography, and differential scanning calorimetry. The reversible dimerization of An induced by heating enables the cyclic PCL to have a switchable "on-off" capability. This novel light-induced ring-closure technique can be one of the most powerful candidates for producing various well-defined cyclic polymers in highly concentrated polymer solution.