Highly Reactive Thiol-Norbornene Photo-Click Hydrogels: Toward Improved Processability.

In the present work, gelatin type B is modified with highly reactive norbornene functionalities (Gel-NB) following a one-pot synthesis approach to enable subsequent thiol-ene photo-click crosslinking. The modification strategy displays close control over the amount of introduced functionalities. Additionally, Gel-NB exhibits considerably improved processing capabilities in terms of two-photon polymerization when benchmarked to earlier-reported crosslinkable gelatin derivatives (e.g., gelatin-methacrylamide (Gel-MOD) and gelatin-methacrylamide-aminoethylmethacrylate (Gel-MOD-AEMA)). The improvement is especially apparent in terms of minimally required laser power (20 mW vs ≥60 mW (Gel-MOD) vs ≥40 mW (Gel-MOD-AEMA) at 100 mm s-1 scan speed) and processable concentration range (≥5 w/v% vs ≥10 w/v% (Gel-MOD/Gel-MOD-AEMA)). Furthermore, the proposed functionalization scheme maintains the excellent biocompatibility and cell interactivity of gelatin. Additionally, the norbornene functionalities have potential for straightforward postprocessing "thiol-ene" surface grafting of active molecules. As a consequence, a very promising material toward tissue engineering applications and more specifically, biofabrication, is presented.

A Modular Approach to Sensitized Two-Photon Patterning of Photodegradable Hydrogels.

Photodegradable hydrogels have emerged as useful platforms for research on cell function, tissue engineering, and cell delivery as their physical and chemical properties can be dynamically controlled by the use of light. The photo-induced degradation of such hydrogel systems is commonly based on the integration of photolabile o-nitrobenzyl derivatives to the hydrogel backbone, because such linkers can be cleaved by means of one- and two-photon absorption. Herein we describe a cytocompatible click-based hydrogel containing o-nitrobenzyl ester linkages between a hyaluronic acid backbone, which is photodegradable in the presence of cells. It is demonstrated for the first time that by using a cyclic benzylidene ketone-based small molecule as photosensitizer the efficiency of the two-photon degradation process can be improved significantly. Biocompatibility of both the improved two-photon micropatterning process as well as the hydrogel itself is confirmed by cell culture studies.

Cross-Linkable Gelatins with Superior Mechanical Properties Through Carboxylic Acid Modification: Increasing the Two-Photon Polymerization Potential.

The present work reports on the development of photo-cross-linkable gelatins sufficiently versatile to overcome current biopolymer two-photon polymerization (2PP) processing limitations. To this end, both the primary amines as well as the carboxylic acids of gelatin type B were functionalized with photo-cross-linkable moieties (up to 1 mmol/g) resulting in superior and tunable mechanical properties (G' from 5000 to 147000 Pa) enabling efficient 2PP processing. The materials were characterized in depth prior to and after photoinduced cross-linking using fully functionalized gelatin-methacrylamide (gel-MOD) as a benchmark to assess the effect of functionalization on the protein properties, cross-linking efficiency, and mechanical properties. In addition, preliminary experiments on hydrogel films indicated excellent in vitro biocompatibility (close to 100% viability) both in the presence of MC3T3 preosteoblasts and L929 fibroblasts. Moreover, 2PP processing of the novel derivative was superior in terms of applied laser power (≥40 vs ≥60 mW for gel-MOD at 100 mm/s) as well as post-production swelling (0-20% vs 75-100% for gel-MOD) compared to those of gel-MOD. The reported novel gelatin derivative (gel-MOD-AEMA) proves to be extremely suitable for direct laser writing as both superior mimicry of the applied computer-aided design (CAD) was obtained while maintaining the desired cellular interactivity of the biopolymer. It can be anticipated that the present work will also be applicable to alternative biopolymers mimicking the extracellular environment such as collagen, elastin, and glycosaminoglycans, thereby expanding current material-related processing limitations in the tissue engineering field.

Photo-crosslinkable recombinant collagen mimics for tissue engineering applications.

Gelatin is frequently used in various biomedical applications. However, gelatin is generally extracted from an animal source, which can result in issues with reproducibility as well as pathogen transmittance. Therefore, we have investigated the potential of a recombinant peptide based on collagen I (RCPhC1) for tissue engineering applications and more specifically for adipose tissue regeneration. In the current paper, RCPhC1 was functionalized with photo-crosslinkable methacrylamide moieties to enable subsequent UV-induced crosslinking in the presence of a photo-initiator. The resulting biomaterial (RCPhC1-MA) was characterized by evaluating the crosslinking behaviour, the mechanical properties, the gel fraction, the swelling properties and the biocompatibility. The obtained results were compared with the data obtained for methacrylamide-modified gelatin (Gel-MA). The results indicated that the properties of RCPhC1-MA networks are comparable to those of animal-derived Gel-MA. RCPhC1-MA is thus an attractive synthetic alternative for animal-derived Gel-MA and is envisioned to be applicable for a wide range of tissue engineering purposes.