Effects of experimental bleaching gels containing co-doped titanium dioxide and niobium pentoxide combined with violet light.

OBJECTIVES: The objective of the study is to evaluate the bleaching potential of 6% hydrogen peroxide (6% HP) gels containing NF_TiO2 or Nb2O5 irradiated with a violet LED light and the effects on enamel mineral content and surface morphology. METHODS: Particles were synthesized, and experimental gels were chemically analyzed by preliminary and accelerated stability tests, pH, and HP decomposition rate. Bovine enamel blocks were treated with 6% HP gels containing (n = 10): 5% NF_TiO2, 5% Nb2O5, 2.5% NF_TiO2 + 2.5% Nb2O5 or without particles (6% HP), irradiated or not with LED, and the control was treated with 35% HP. Color (∆E00) and whitening index (∆WID) variations, surface microhardness (SH), average roughness (∆Ra), Ca-P concentration (EDS), and enamel morphology (SEM) were assessed. Bleaching was performed in 3 sessions of 30 min and 7-day intervals. Data were submitted to two- (pH, decomposition rate, ∆E00, and ∆WID) or three-way ANOVA and Bonferroni (SH), Kruskal-Wallis (∆Ra), and Dunnet tests (α = 0.05). RESULTS: No changes in the gel's color, odor, or translucency were observed. The pH (6 to 6.5) remained stable over time, and light irradiation boosted the HP decomposition rate. NF_TiO2 and Nb2O5-containing gels displayed higher ∆E00 and ΔWID when light-irradiated (p < 0.05). Nb2O5 and Nb2O5 + NF_TiO2 decreased enamel SH (p < 0.05), but no SH changes were found among groups (p > 0.05). No differences among groups were noted in ∆Ra, Ca-P content, and enamel morphology after treatments (p > 0.05). CONCLUSION: Experimental light-irradiated 6% HP gels containing NF_TiO2 or Nb2O5 were chemically stable and exhibited bleaching potential comparable with 35% HP. CLINICAL RELEVANCE: Low-concentrated HP gels containing NF_TiO2 or Nb2O5 and light-irradiated stand as a possible alternative to in-office bleaching.

Mechanical and antibacterial properties of an experimental flowable composite containing Nb2O5 and NF_TiO2 nanoparticles.

This study developed an experimental flowable composite incorporated with niobium pentoxide (Nb2O5) combined or not with titanium dioxide co-doped with fluorine and nitrogen (NF_TiO2) and evaluated the mechanical and antibacterial properties. The experimental flowable composite (TEGDMA + BisGMA 1:1 + 60%wt - inorganic filler - borosilicate 0.7 µm) was formulated according to the type and concentration of Nb2O5 and NF_TiO2 (0.5, 1, 1.5 and 2 wt%) or NF_TiO2 + Nb2O5 (0.25, 0.5, 0.75 and 1 wt% - 1:1). The control groups were formed by the experimental composite without the incorporation of Nb2O5 and/or NF_TiO2 (GC-E) and by a commercial flowable composite (GC). The characterization of the surface of the composite and its particles was carried out using scanning electron microscopy (SEM) and energy dispersive x-rays (EDX). Specimens were manufactured and subjected to mechanical tests of flexural strength (FS) (n = 12), flexural modulus (FM) (n = 12), roughness (Ra) (n = 10), microhardness (n = 10), and contact angle (n = 10); and, to evaluate the antibacterial activity, they were submitted to tests of biofilm formation against S. mutans (CFU/mL) (n = 5), biofilm biomass by dry weight (n = 5) and confocal laser microscopy (%LIVE/DEAD) (n = 5). Data were submitted to one-way ANOVA and Tukey's post-hoc and, those that were not homoscedastic, but with normality, were submitted to Welch's ANOVA and Games-Howell's post-hoc. Dunnet's test was used to compare the controls with the other experimental groups (α = 5). The Nb2O5 particles had an average size of 32.4 µm and the nanoparticles (NPs) of NF_TiO2, 10 nm. EDX analysis identified isolated peaks of N, F, Ti, and Nb confirming the presence of these particles in the resin matrix. The 1.5% NF_TiO2 group had a higher FS and FM than the controls (p < 0.05). GC showed higher microhardness between groups (p < 0.05). There was no difference between the experimental groups regarding contact angle and roughness (p > 0.05), except for GC, which had the highest Ra values and the lowest contact angle between groups (p < 0.05). Composites containing 0.5%, 1%, 1.5%, and 2% Nb2O5, 1%, 1.5%, and 2% NF_TiO2 and 2% Nb2O5 + NF_TiO2 showed lower biofilm formation (p < 0.05), lower total biofilm biomass (p < 0.05), and a higher percentage of dead cells (44%, 52%, 52%, 79%, 42% 43%, 62%, 65%, respectively) than GC and GC-E (5% and 1%, respectively). It is concluded that the incorporation of 1.5% NF_TiO2 promoted a greater FS and FM among the experimental composites and that the addition of Nb2O5 particles (0.5%, 1%, 1.5%, and 2%), NF_TiO2 (1%, 1.5% and 2%) and the combination Nb2O5 + NF_TiO2 (2%) showed significant antibacterial effects.

Color stability of enamel treated with different antioxidant agents following at-home bleaching with 10% hydrogen peroxide

Abstract Objective This study evaluated the color stability of enamel submitted to 10% hydrogen peroxide (HP) followed by antioxidants agents, and the pH and antioxidant activity (AA%) of these agents. Methodology Bovine enamel-dentin blocks were randomly distributed into groups (n=10/group): GNC (negative control: no treatment); GPC (positive control: bleaching only); TOC_10% (HP+10% α-tocopherol); GT_10% (HP+10% green tea extract); GS_5% (HP+5% grape seed extract); SA_10% (HP+10% sodium ascorbate); QUI_10% (HP+10% quinoa extract); and QC_1% (HP+1% quercetin). Color (ΔE00) and whiteness index (ΔWID) changes were analyzed using a digital spectrophotometer. The pH and AA% were determined using a pH meter and the DPPH method, respectively. Data were analyzed by ANOVA/Tukey's and Dunnett's tests (α=0.05). Results At 14 days post-bleaching, GNC promoted the lowest ΔWID and ΔE00 (p<0.05), and no differences were found between GPC and the remaining groups submitted to the antioxidant agents (p>0.05). QC_1% and QUI_10% exhibited acidic pH levels (3.64 and 4.75, respectively), whereas TOC_10% and GS_5% exhibited alkaline pH (7.07 and 7.64, respectively). No differences in AA% were found between the agents (p>0.05), ranging from 92.6 to 97.6%. Conclusion The antioxidant agents did not interfere in bleached enamel color stability, showing satisfactory antioxidant activity. However, QUI and QC gels displayed acidic pH. Clinical significance: The antioxidants evaluated showed high AA% and no impact on post-bleaching color stability, suggesting that their capacity to recover bond strength demonstrated elsewhere would not compromise the esthetic efficacy of tooth bleaching. However, those with acidic pH should be used with caution due to potential enamel damage.