The formation of cariogenic plaque to contemporary adhesive restorative materials: an in vitro study.

The research exploiting the ability of dental materials to induce or prevent secondary caries (SC) development still seems inconclusive. Controlling bacterial adhesion by releasing bacteriostatic ions and improving the surface structure has been suggested to reduce the occurrence of SC. This paper analyses the impact of five distinctively composed dental materials on cariogenic biofilm formation. Forty-five specimens of three composites (CeramX Spectra ST, Admira Fusion, Beautifil II) and two glass-ionomers (Fuji II LC, Caredyne Restore), respectively, were incubated in bacterial suspension composed of Streptococcus mutans, Lactobacillus acidophilus, Streptococcus mitis, Streptococcus sanguinis, and Streptococcus salivarius at pH 7.0 and 5.5. Coverslips were used as a control. Adhered bacteria were collected after 2, 4, 6, 12, 24, and 48 h and analyzed using quantitative polymerase chain reaction (qPCR). Fluoride leakage was measured at each collection. The specimens' surface topography was assessed using interferometry. In the present study, surface roughness seemed to have a partial role in bacterial adhesion and biofilm formation, together with chemical composition of the materials tested. Despite differences in fluoride leakage, biofilm accumulation was similar across materials, but the number of adhered bacteria differed significantly. A release of other ions may also affect adhesion. These variations suggest that certain materials may be more prone to initiating secondary caries.

Inhibition of tooth demineralization caused by Streptococcus mutans biofilm via antimicrobial treatment using hydrogen peroxide photolysis.

OBJECTIVES: An antimicrobial technique utilizing hydroxyl radicals generated by the photolysis of 3% H2O2 has been developed recently. The present study aimed to evaluate the effect of H2O2 photolysis treatment on tooth demineralization caused by Streptococcus mutans biofilm. MATERIALS AND METHODS: To induce tooth demineralization, S. mutans biofilm was allowed to form on the maxillary first molars collected from Wistar rats via 24-h culturing. The samples were immersed in 3% H2O2 and irradiated with 365-nm LED (H2O2 photolysis treatment). Viable bacterial counts in the biofilm were evaluated immediately after treatment and after an additional 30-h culturing by colony counting. The acidogenicity of the biofilm, re-established 30 h after treatment, was assessed by measuring the pH. The effect of H2O2 photolysis treatment on tooth demineralization was assessed by measuring the depth of the radiolucent layer in micro-CT images. RESULTS: H2O2 photolysis significantly reduced viable bacterial counts in the biofilm to 3.7 log colony forming units (CFU)/sample, while the untreated group had 7.9 log CFU/sample. The pH of the biofilm re-established after treatment (6.6) was higher than that of the untreated group (5.3). In line with the pH measurement, the treatment group had a significantly lower depth of radiolucent layer in dentin than the untreated group. CONCLUSIONS: H2O2 photolysis treatment was effective not only in killing the biofilm-forming S. mutans but also in lowering the acidogenicity of the biofilm. Thus, this technique could inhibit tooth demineralization. CLINICAL RELEVANCE: H2O2 photolysis can be applicable as a new dental caries treatment.

Impact of adhesive primer and light-curing on polymerization kinetics of self-adhesive resin cement in association with free radical reaction.

This study analyzed the impact of adhesive primer and light-curing on the polymerization kinetics of urethane dimethacrylate-based self-adhesive resin cement combined with free radical reaction. Specimens were prepared by mixing the cement paste with or without adhesive primer. Subsequently, specimens were light-cured or set without light-curing. The degree of conversion (DC), Vickers hardness (Hv), and free radical concentrations were repeatedly measured up to 168 h after the curing initiation. Irrespective of the curing procedures, DC, Hv, and free radical concentration rapidly increased during the initial 30 min of curing. The specimens cured with adhesive primer and/or light-curing generally showed higher values of DC, Hv, and radical concentration than those set by chemical curing alone, especially during the initial polymerization phase. Kinetic analysis using a linear mixed model revealed that the adhesive primer had a higher coefficient estimate than light-curing, indicating that the former had a higher impact on the polymerization. Additionally, the adhesive primer alleviated the Hv reduction caused by water and air during the initial polymerization phase, although light-curing hardly prevented the polymerization inhibition. Therefore, we suggest that application of adhesive primer is beneficial to achieve higher degree of conversion and better mechanical properties of self-adhesive resin cements by enhancing free radical reactions.

Influence of low-temperature degradation on the wear characteristics of zirconia against polymer-infiltrated ceramic-network material.

STATEMENT OF PROBLEM: Low-temperature degradation may affect zirconia restorations during their clinical service. Concerns have been raised about the effect of low-temperature degradation on the wear behavior of zirconia. Moreover, the wear resistance of this novel polymer-infiltrated ceramic-network material needs to be better evaluated. PURPOSE: The purpose of this in vitro study was to investigate the influence of aging on the wear resistance of zirconia opposing polymer-infiltrated ceramic-network material. MATERIAL AND METHODS: Twelve specimens for 2 newly developed polymer-based materials (a polymer-infiltrated ceramic-network material VITA ENAMIC and a resin nanocomposite material Lava Ultimate), 2 commonly used glass-ceramic materials (IPS e.max CAD and VITABLOCS Mark II), and 2 conventional composite resin materials (VITA CAD-Temp and PMMA Disk) were tested; human enamel was used as a control group. The wear simulator used was a ball-on-disk type with zirconia balls, with and without autoclaving (134°C, 200 kPa, 20 hours) as antagonists. The vertical loss and volume loss of specimens and the roughness average of zirconia antagonists were measured with a 3-dimensional optical profilometer. Vickers hardness values were determined using a micro-Vickers hardness tester. Data were statistically analyzed with a mixed-model ANOVA for wear loss (vertical loss [µm] and volume loss [mm3]) and roughness average (µm) of zirconia antagonists and with the Kruskal-Wallis test for Vickers hardness values (α=.05). The Spearman correlation coefficient was used to determine the relationship between wear loss and hardness. RESULTS: Results showed that specimens opposing the non-aged zirconia balls demonstrated significantly higher wear than those opposing the aged ones (P<.001). The polymer-infiltrated ceramic-network material VITA ENAMIC group (vertical loss=27.44-33.53 µm, volume loss=0.0198-0.315 mm3) and the resin nanocomposite material Lava Ultimate group (vertical loss=24.42-27.83 µm, volume loss=0.0159-0.0233 mm3) showed lower vertical loss and volume loss than the conventional composite resin groups (vertical loss=43.95-61.87 µm, volume loss=0.0395-0.0593 mm3) but higher wear than the glass-ceramic groups (IPS e.max CAD and VITABLOCS Mark II; vertical loss=8.95-11.47 µm, volume loss=0.0072-0.0094 mm3) and human enamel (vertical loss=9.95-12.32 µm; volume loss=0.0089-0.0103 mm3). The aged zirconia antagonists indicated greater roughness average values than the aged zirconia balls after the wear test (P<.001). Distinct abrasion-induced tracks were observed on the contact surfaces of the aged zirconia antagonists. CONCLUSIONS: Even though zirconia ceramic subjected to low-temperature degradation exhibited increased roughness after the wear test, it was still nonabrasive toward opposing materials. The polymer-infiltrated ceramic-network material showed intermediate wear resistance compared with glass-ceramic and conventional composite resin.

Oral mucosal irritation study in hamster to evaluate a therapeutic apparatus using hydrogen peroxide photolysis for periodontitis treatment.

We conducted an oral mucosal irritation study in hamsters to evaluate a therapeutic apparatus using hydrogen peroxide (H2O2) photolysis for periodontitis treatment (ISO 10993-Part 10, Annex B.3). The cheek pouches in 15 male hamsters were allocated to one of six groups. Group 1 received pure water treatment (control group). Group 2 received laser irradiation at 80 mW. Group 3 received 3% H2O2. Groups 4-6 received laser irradiation of 3% H2O2 at 80, 40, and 20 mW, respectively. The total treatment time was set at 7 min and treatment was repeated three times at approximately 1-h intervals. Macroscopic and microscopic histologic observations of the treated sites were performed immediately after each treatment and/or 24 h after the last treatment. The mean scores in macroscopic and histologic examinations in all six groups were 0. Accordingly, irritation indices calculated by subtracting the mean score in each experimental group from that in the control group (Group 1) were 0. Our results suggest that treatment with the apparatus has no mucosal irritation potential in hamster cheek pouches under test conditions simulating clinical conditions.

Vaniprevir plus peginterferon alfa-2b and ribavirin in treatment-experienced Japanese patients with hepatitis C virus genotype 1 (GT1b) infection: Phase 3 studies.

BACKGROUND AND AIM: Vaniprevir is a macrocyclic hepatitis C virus (HCV) non-structural (NS)3/4A protease inhibitor. The objective of these phase 3 multicenter, open-label trials was to evaluate the safety and efficacy of vaniprevir + peginterferon alfa-2b + ribavirin (PR) in Japanese patients with HCV genotype (GT)1 infection who had previously failed treatment with interferon-based regimens. METHODS: Japanese patients with chronic HCV GT1 were enrolled. In PN044, patients with previous relapse or virologic breakthrough were randomized to vaniprevir (300 mg twice daily) + PR for 12 weeks followed by PR for another 12 weeks (12-week arm) or vaniprevir + PR for 24 weeks (24-week arm). In PN045, patients with previous partial/null response received vaniprevir + PR for 24 weeks. The primary endpoint was sustained virologic response at 24 weeks after completing treatment (SVR24 ). RESULTS: In PN044 (n = 51), SVR24 was 92.0% and 96.2% in the 12- and 24-week arms, respectively. In PN045 (n = 42), SVR24 was 61.9% in all patients and 55.2% in previous null responders. In both studies, vaniprevir + PR was generally safe and well tolerated; the majority of adverse events were mild/moderate and included pyrexia, decreased hemoglobin, headache, nausea, pruritus, and decreased platelet count. Polymorphisms in the HCV NS3 gene at baseline (Y56, Q80, and V170) did not impact treatment outcome. Virologic failure was principally associated with the on-treatment emergence of R155 or D168 mutations. CONCLUSIONS: Vaniprevir + PR is an effective, well-tolerated treatment for Japanese patients with HCV GT1 infection who failed previous interferon-based treatment. ClinicalTrials.gov Identifier NCT01405937 and NCT01405560 (Protocols PN044 and PN045).

Fatigue analysis of computer-aided design/computer-aided manufacturing resin-based composite vs. lithium disilicate glass-ceramic.

Resin-based composite molar crowns made by computer-aided design/computer-aided manufacturing (CAD/CAM) systems have been proposed as an inexpensive alternative to metal-ceramic or all-ceramic crowns. However, there is a lack of scientific information regarding fatigue resistance. This study aimed to analyze the fatigue behavior of CAD/CAM resin-based composite compared with lithium disilicate glass-ceramic. One-hundred and sixty bar-shaped specimens were fabricated using resin-based composite blocks [Lava Ultimate (LU); 3M/ESPE] and lithium disilicate glass-ceramic [IPS e.max press (EMP); Ivoclar/Vivadent]. The specimens were divided into four groups: no treatment (NT); thermal cycling (TC); mechanical cycling (MC); and thermal cycling followed by mechanical cycling (TCMC). Thermal cycling was performed by alternate immersion in water baths of 5°C and 55°C for 5 × 10(4) cycles. Mechanical cycling was performed in a three-point bending test, with a maximum load of 40 N, for 1.2 × 10(6) cycles. In addition, LU and EMP molar crowns were fabricated and subjected to fatigue treatments followed by load-to-failure testing. The flexural strength of LU was not severely reduced by the fatigue treatments. The fatigue treatments did not significantly affect the fracture resistance of LU molar crowns. The results demonstrate the potential of clinical application of CAD/CAM-generated resin-based composite molar crowns in terms of fatigue resistance.

Fracture resistance of computer-aided design/computer-aided manufacturing-generated composite resin-based molar crowns.

The aim of this study was to investigate whether different fabrication processes, such as the computer-aided design/computer-aided manufacturing (CAD/CAM) system or the manual build-up technique, affect the fracture resistance of composite resin-based crowns. Lava Ultimate (LU), Estenia C&B (EC&B), and lithium disilicate glass-ceramic IPS e.max press (EMP) were used. Four types of molar crowns were fabricated: CAD/CAM-generated composite resin-based crowns (LU crowns); manually built-up monolayer composite resin-based crowns (EC&B-monolayer crowns); manually built-up layered composite resin-based crowns (EC&B-layered crowns); and EMP crowns. Each type of crown was cemented to dies and the fracture resistance was tested. EC&B-layered crowns showed significantly lower fracture resistance compared with LU and EMP crowns, although there was no significant difference in flexural strength or fracture toughness between LU and EC&B materials. Micro-computed tomography and fractographic analysis showed that decreased strength probably resulted from internal voids in the EC&B-layered crowns introduced by the layering process. There was no significant difference in fracture resistance among LU, EC&B-monolayer, and EMP crowns. Both types of composite resin-based crowns showed fracture loads of >2000 N, which is higher than the molar bite force. Therefore, CAD/CAM-generated crowns, without internal defects, may be applied to molar regions with sufficient fracture resistance.

Cutting efficiency of diamond burs operated with electric high-speed dental handpiece on zirconia.

Zirconia-based dental restorations are becoming used more commonly. However, limited attention has been given to the difficulties experienced, concerning cutting, in removing the restorations when needed. The aim of the present study was to compare the cutting efficiency of diamond burs, operated using an electric high-speed dental handpiece, on zirconia (Zir) with those on lithium disilicate glass-ceramic (LD) and leucite glass-ceramic (L). In addition, evaluation of the cutting efficiency of diamond burs on Zir of different thicknesses was performed. Specimens of Zir were prepared with thicknesses of 0.5, 1.0, 2.0, and 4.0 mm, and specimens of LD and L were prepared with a thickness of 1.0 mm. Cutting tests were performed using diamond burs with super coarse (SC) and coarse (C) grains. The handpiece was operated at 150,000 rpm with a cutting force of 0.9 N. The results demonstrated that cutting of Zir took about 1.5- and 7-fold longer than cutting of LD and L, respectively. The SC grains showed significantly higher cutting efficiency on Zir than the C grains. However, when the thickness of Zir increased, the cutting depth was significantly decreased. As it is suggested that cutting of zirconia is time consuming, this should be taken into consideration in advance when working with zirconia restorations.

Fracture resistance of monolithic zirconia molar crowns with reduced thickness.

OBJECTIVES: The purpose of the present study was to analyze the relationship between fracture load of monolithic zirconia crowns and axial/occlusal thickness and to evaluate the fracture resistance of monolithic zirconia crowns with reduced thickness in comparison with that of monolithic lithium disilicate crowns with regular thickness. MATERIALS AND METHODS: Monolithic zirconia crowns (Lava Plus Zirconia, 3M/ESPE) with specified axial/occlusal thicknesses and lithium disilicate crowns (IPS e.max press, Ivoclar/Vivadent) with regular thickness were fabricated using a dental CAD/CAM system and a press technique, respectively. The crowns cemented onto dies were loaded until fracture. Based on measurements of the crown thickness made by micro-CT and the fracture load, multiple regression analysis was performed. RESULTS: It was revealed that the occlusal thickness significantly affected the fracture load (p < 0.01), but the axial thickness did not (p = 0.2828). Although the reduction of the occlusal thickness decreased the fracture resistance of the monolithic zirconia crowns, the fracture load of the zirconia crowns with the occlusal thickness of 0.5 mm (5558 ± 522 N) was significantly higher than that of lithium disilicate crowns with an occlusal thickness of 1.5 mm (3147 ± 409 N). CONCLUSION: Within the limitations of the present study, it is suggested that monolithic zirconia crown with chamfer width of 0.5 mm and occlusal thickness of 0.5 mm can be used in the molar region in terms of fracture resistance.

Rikkosan's Short-Term Analgesic Effect on Burning Mouth Syndrome: A Single-Arm Cohort Study.

Burning mouth syndrome (BMS) is a chronic oral pain disorder. There is a theory that BMS is a form of nociplastic pain. A standard treatment for BMS has not yet been established. Kampo medicine is a traditional oriental medicine. The purpose of this study is to evaluate the effectiveness of Rikkosan-a traditional Japanese herbal medicine (Kampo)-in the treatment of BMS. A single-center retrospective study was conducted on 20 patients who were diagnosed with BMS and treated with Rikkosan alone (total daily dose; 7.5 g) three times daily for approximately 4 weeks (29.5 ± 6.5 days). Rikkosan was dissolved in hot water and taken internally. They had an average age of 63 years, and 90% were being treated for other illnesses, but their medication status was the same during this study period, except for Rikkosan. No adverse events were observed in patients. Numerical rating scale (NRS) or visual analog scale (VAS)/10 scores decreased significantly between the time of the initiation of Rikkosan and one month after (-2.1 ± 1.2, p < 0.05). Rikkosan has a short-term effect of reducing NRS by two levels in BMS patients.

Critical evaluations on the crystallographic properties of translucent dental zirconia ceramics stabilized with 3-6 mol% yttria.

OBJECTIVES: This study aimed to determine the crystalline phase composition of 3-6 mol% yttria-stabilized zirconia (3-6YSZ), specifically investigating the presence of tetragonal (t), cubic (c), and/or additional yttria-rich tetragonal (t') phase. METHODS: Laboratory-fabricated specimens comprising 3-5YSZ, resembling translucent dental zirconia ceramics (TZ specimens), and a blend of 3YSZ and 8YSZ, representing a c-phase reference, were prepared. Additionally, 25 dental zirconia products stabilized with 3-6 mol% yttria were analyzed. Whole X-ray diffraction (XRD) patterns were obtained for Rietveld analysis, complemented by fine scanning in the 2θ region from 72º to 76º for qualitative phase analysis. Moreover, yttria concentrations in each specimen were determined using X-ray fluorescence (XRF) spectroscopy. RESULTS: In the 2θ region from 72º to 76º, TZ and dental zirconia product specimens displayed four peaks attributed to t- and t'-phases, but the c-phase peak was absent. Rietveld analysis of the whole XRD patterns, utilizing a t-t' model, demonstrated the t-phase fraction ranging from 86 mass% in 3YSZ to 11 mass% in 6YSZ. Rietveld analysis appeared reliable, as the yttria contents calculated based on lattice parameters aligned well with those measured by XRF. This study established that dental 3-6YSZ consisted of yttria-lean t- and yttria-rich t'-phases. SIGNIFICANCE: The present study enhances understanding of the crystalline structure of dental zirconia ceramics. Future crystallographic analyses of these ceramics should consider the presence of t- and t'-phases.

Residual stress associated with crystalline phase transformation of 3-6 mol% yttria-stabilized zirconia ceramics induced by mechanical surface treatments.

Monolithic dental prostheses made of 3-6 mol% yttria-stabilized zirconia (3-6YSZ) have gained popularity owing to their improved material properties and semi-automated fabrication processes. In this study, we aimed to evaluate the influence of mechanical surface treatments, such as polishing, grinding, and sandblasting, on the residual stress of 3-6YSZ used for monolithic prostheses in association with crystalline phase transformation. Plate specimens were prepared from five dental zirconia blocks: Aadva Zirconia ST (3YSZ), Aadva Zirconia NT (6YSZ), Katana HT (4YSZ), Katana STML (5YSZ), and Katana UTML (6YSZ). The specimens were either polished using 1, 3, or 9 µm diamond suspensions, ground using 15, 35, or 55 µm diamond discs, or sandblasted at 0.2, 0.3, or 0.4 MPa. The residual stress, crystalline phase, and hardness were analyzed using the cosα method, X-ray diffraction (XRD), and Vickers hardness test, respectively. Additionally, we analyzed the residual stress on the surfaces of monolithic zirconia crowns (MZCs) made of 4YSZ, 5YSZ, and 6YSZ, which were processed using clinically relevant procedures, including manual grinding, followed by polishing using a dental electric motor on the external surface, and sandblasting on the internal surface. Residual stress analysis demonstrated that grinding and sandblasting, particularly the latter, resulted in the generation of compressive residual stress on the surfaces of the plate specimens. XRD revealed that the ground and sandblasted specimens contained a larger amount of the rhombohedral phase than that of the polished specimens, which may be a cause of the residual stress. Sandblasting significantly increased the Vickers hardness compared to polishing, which may possibly be due to the generation of compressive residual stress. In the case of MZCs, compressive residual stress was detected not only on the sandblasted surface, but also on the polished surface. The difference in the residual stress between the plate and crown specimens may be related to the force applied during the automated and manual grinding and polishing procedures. Further studies are required to elucidate the effects of the compressive residual stress on the clinical performance of MZCs.

Influence of grain size and veneer firing process on the flexural strength of zirconia ceramics.

The aim of the present investigation was to study the influence of grain size on the strength of yttria-stabilized zirconia upon exposure to an additional heat treatment, mimicking the veneering process. The green bodies of zirconia discs prepared by cold isostatic pressing were sintered at 1,425, 1,500, or 1,575°C to customize the grain size. The disc-shaped specimens were highly polished and then processed with or without additional heat treatments (five times at 850-930°C). Ten specimens from each treatment group were subjected to a biaxial flexural strength test according to the ISO 6872 standard. The grain size of the specimens was analyzed by the mean linear intercept technique using scanning electron microscopy. It was demonstrated that the mechanical strength of zirconia ceramics was not reduced by the veneer firing processes when polished specimens were used, but the strength was found to decrease with increasing grain size. The raw materials and the sintering process used should be selected appropriately to avoid grain coarsening because it was found that the strength was influenced by large grains.

Most dentists approve of oral health check-ups for local residents at community pharmacies and desire collaboration with community pharmacists.

Community pharmacies are required to play a role in maintaining the health of local residents. Since September 2015, a national policy in Japan has allowed saliva tests to be used for oral health check-ups at community pharmacies. In the present study, we aimed to reveal dentists' perceptions and expectations for oral health check-ups provided at community pharmacies. A questionnaire survey was administered to dentists at 1,000 randomly selected dental clinics in Tokyo, Japan; 257 responses (25.7%) were included in the analysis and 85.2% of respondents approved of oral health check-ups at community pharmacies. Most respondents who approved of oral health check-ups expected that community pharmacists would recommend that local residents visit a dental clinic (85.8%) and provide a report to dentists (60.3%) after the check-up. Furthermore, 79.0% of respondents desired collaboration with community pharmacies. These findings suggested the potential for oral health check-ups to facilitate collaboration between community pharmacies and dental clinics aimed at maintaining and improving oral health of local residents.

Influence of crystalline phase transformation induced by airborne-particle abrasion and low-temperature degradation on mechanical properties of dental zirconia ceramics stabilized with over 5 mol% yttria.

Monolithic dental prostheses fabricated from 5 mol% yttria-stabilized zirconia (5YZ) have been developed to improve the translucency of conventional 3 mol% yttria-stabilized zirconia. In this study, we aimed to evaluate the influence of airborne-particle abrasion (APA) and low-temperature degradation (LTD) on the mechanical properties of 5YZ in association with the crystalline phase transformation. In total, 120 disc-shaped specimens of two brands of 5YZ (Lava Esthetic and Katana UTML) were prepared. The specimens were divided into four groups (n = 15 for each group): (i) control, (ii) APA, (iii) LTD, and (iv) APA + LTD groups. APA was performed with 50 µm alumina particles, and LTD was induced by autoclaving at 134 °C for 50 h. The biaxial flexural strength of the specimens was assessed using a piston-on-three-ball test according to ISO 6872:2015, and Vickers hardness was determined using a microhardness tester. The crystalline phase was analyzed by the Rietveld refinement of X-ray diffraction patterns. APA significantly increased the flexural strength of the Lava Esthetic specimens, whereas LTD hardly affected the strength of both materials. APA and APA + LTD significantly increased the Vickers hardness of both materials. According to Rietveld analysis, the pseudocubic phase was predominant in both materials, i.e., 66 mass% and 81 mass% in the Lava Esthetic and Katana UTML specimens, respectively. APA induced the rhombohedral phase at approximately 37 mass% in both materials, while LTD induced the monoclinic phase at 2.8 mass% in the Lava Esthetic specimens and 0.9 mass% in the Katana UTML specimens. APA + LTD weakly affected the amount of the rhombohedral phase but slightly increased the amount of the monoclinic phase. These findings suggest that APA may improve the mechanical properties of 5YZ, particularly hardness, via the generation of the rhombohedral phase. In contrast, the influence of LTD on the mechanical and microstructural properties of 5YZ was limited.

Resin Cement-Zirconia Bond Strengthening by Exposure to Low-Temperature Atmospheric Pressure Multi-Gas Plasma.

The purpose of this study was to investigate the effect of gas species used for low-temperature atmospheric pressure plasma surface treatment, using various gas species and different treatment times, on zirconia surface state and the bond strength between zirconia and dental resin cement. Three groups of zirconia specimens with different surface treatments were prepared as follows: untreated group, alumina sandblasting treatment group, and plasma treatment group. Nitrogen (N2), carbon dioxide (CO2), oxygen (O2), argon (Ar), and air were employed for plasma irradiation. The bond strength between each zirconia specimen and resin cement was compared using a tension test. The effect of the gas species for plasma irradiation on the zirconia surface was investigated using a contact angle meter, an optical interferometer, an X-ray diffractometer, and X-ray photoelectric spectroscopy. Plasma irradiation increased the wettability and decreased the carbon contamination on the zirconia surface, whereas it did not affect the surface topography and crystalline phase. The bond strength varied depending on the gas species and irradiation time. Plasma treatment with N2 gas significantly increased bond strength compared to the untreated group and showed a high bond strength equivalent to that of the sandblasting treatment group. The removal of carbon contamination from the zirconia surface and an increase in the percentage of Zr-O2 on the zirconia surface by plasma irradiation might increase bond strength.

Effect of airborne-particle abrasion and polishing on novel translucent zirconias: Surface morphology, phase transformation and insights into bonding.

PURPOSE: The purpose this study was to investigate the effect of Kern´s air-borne particle abrasion protocol (KAPA) and polishing on two translucent zirconias (4Y, 5Y-zirconias) compared to a traditional zirconia (3Y-zirconia). METHODS: Two different surface treatments were analysed by X-ray diffraction (XRD) and interferometry 1) KAPA (0.1 MPa, 50 µm alumina, 10-12 mm distance, 15 sec and 30 sec and cleaning in ultrasound using isopropyl alcohol 99%) and 2) Clinical-delivery polishing paste (Zircon Brite, Dental Ventures, USA). Shear-bond strength tests (SBS's) were performed with a highly polished and virtually flat surface in combination with a 10-MDP based cement and a surface modified by KAPA in combination with zinc phosphate cement. The SBS was expressed in terms of MPa. RESULTS: The mean values for monoclinic content were 13 wt%, 7 wt% and 2 wt% for 3Y-, 4Y- and 5Y-zirconias respectively, no differences were found between 15 and 30 seconds. Polishing did not result in phase transformation to monoclinic phase in any of the zirconias. The rhombohedral phase was identified in all types of zirconias regardless of surface treatment. Shear-bond strength tests showed 5 MPa for polished/10-MDP based cement and 3 MPa for KAPA/ Zinc phosphate. Statistically significant differences were found between the two different surface treatments but not between the types of zirconias. CONCLUSIONS: KAPA for 15 sec seems to be equal to 30 sec regarding morphology and phase transformation. Sole micro-retention appears not to be fully responsible for the bonding phenomena of 10-MDP and zirconia that underwent KAPA.

Gene transfection achieved by utilizing antibacterial calcium phosphate nanoparticles for enhanced regenerative therapy.

Protamine-coated multi-shell calcium phosphate (CaP) was developed as a non-viral vector for tissue regeneration therapy. CaP nanoparticles loaded with different amounts of plasmid DNA encoding bone morphogenetic protein 2 (BMP-2) and insulin-like growth factor 1 (IGF-1) were used to treat MC3T3E1 cells, and the yield of the released BMP-2 or IGF-1 was measured using ELISA 3 days later. Collagen scaffolds containing CaP nanoparticles were implanted into rat cranial bone defects, and BMP-2 and IGF-1 yields, bone formation, and bone mineral density enhancement were evaluated 28 days after gene transfer. The antibacterial effects of CaP nanoparticles against Streptococcus mutans and Aggregatibacter actinomycetemcomitans increased with an increase in the protamine dose, while they were lower for Staphylococcus aureus and Porphyromonas gingivalis. In the combination treatment with BMP-2 and IGF-1, the concentration ratio of BMP-2 and IGF-1 is an important factor affecting bone formation activity. The calcification activity and OCN mRNA of MC3T3E1 cells subjected to a BMP-2:IGF-1 concentration ratio of 1:4 was higher at 14 days. During gene transfection treatment, BMP-2 and IGF-1 were released simultaneously after gene transfer; the loaded dose of the plasmid DNA encoding IGF-1 did not impact the BMP-2 or IGF-1 yield or new bone formation ratio in vitro and in vivo. In conclusion, two growth factor-releasing systems were developed using an antibacterial gene transfer vector, and the relationship between the loaded plasmid DNA dose and resultant growth factor yield was determined in vitro and in vivo.

Reactions of dental pulp to hydrogen peroxide photolysis-based antimicrobial chemotherapy under ultraviolet-A irradiation in rats.

Hydrogen peroxide photolysis-based antimicrobial chemotherapy that utilizes ultraviolet-A irradiation (UVA-H2O2 photolysis) has been previously proposed as a method of treatment of cariogenic biofilm. Therefore, in the present study, we aimed to assess time-dependent reactions in the dental pulp of rats after UVA-H2O2 photolysis. Maxillary first molars were treated. UVA irradiation (wavelength: 365 nm) with 3 wt% H2O2 was performed for 90 s at a radiant emittance of 500-2000 mW/cm2 on the rats for 3 consecutive days or only 1 day. The animals were sacrificed at Days 1, 3, 7, and 21 after the treatment for the histological evaluation of inflammatory cells and immunohistochemistry of heat shock protein (HSP)-25, a marker of odontoblasts. Tertiary dentin formation was evaluated at Day 21 by histomorphometry and micro-CT analysis. UVA-H2O2 photolysis elicited little infiltration of inflammatory cells, but disturbances in the odontoblast layer and/or presence of localized degenerative tissue were observed on Day 3. This condition was followed by a healing process that was characterized by the reappearance of HSP-25 positive odontoblast-like cells at Day 7 and tertiary dentin formation at Day 21. The amount of tertiary dentin formed was dependent on the intensity of treatment; repeated UVA irradiations of H2O2 at 2000 mW/cm2 resulted in the largest amount of tertiary dentin formation at the pulp horn regions. Our findings suggest that UVA-H2O2 photolysis treatment can be used to treat dental caries clinically because the post-treatment inflammatory reaction was minimal and tertiary dentin formation was substantial, which may prove effective in protecting dental pulp from external irritants. As a cautionary consideration, the radiant emittance of the UVA irradiation should be carefully optimized before clinical application.