RESUMO
This study demonstrated that immobilized Candida antarctica lipase B (N435) catalysis in bulk leads to higher molecular weight poly(glycerol sebacate), PGS, than self-catalyzed condensation polymerization. Since the glass-transition temperature, fragility, modulus, and strength for rubbery networks are inversely dependent on the concentration of chain ends, higher molecular weight PGS prepolymers will enable the preparation of cross-linked PGS matrices with unique mechanical properties. The evolution of molecular species during the prepolymerization step conducted at 120 °C for 24 h, prior to enzyme addition, revealed regular decreases in sebacic acid and glycerol-sebacate dimer with corresponding increases in oligomers with chain lengths from 3 to 7 units such that a homogeneous liquid substrate has resulted. At 67 h, for N435-catalyzed PGS synthesis, the carboxylic acid conversion reached 82% without formation of a gel fraction, and number-average molecular weight (Mn) and weight-average molecular weight (Mw) values reached 6000 and 59â¯400 g/mol, respectively. In contrast, self-catalyzed PGS condensation polymerizations required termination at 55 h to avoid gelation, reached 72% conversion, and Mn and Mw values of 2600 and 13â¯800 g/mol, respectively. We also report the extent that solvent fractionation can enrich PGS in higher molecular weight chains. The use of methanol as a nonsolvent increased Mn and Mw by 131.7 and 18.3%, respectively, and narrower dispersity (D) decreased by 47.7% relative to the nonfractionated product.
Assuntos
Decanoatos , Glicerol , Catálise , Decanoatos/química , Glicerol/análogos & derivados , Glicerol/química , Lipase , PolímerosRESUMO
A family of poly(glycerol sebacate) (PGS) analogues were synthesized by Candida antarctica lipase B (CALB) catalysis to tailor biomaterial properties. Different fractions of glycerol (G) units in PGS were replaced by 1,8-octanediol (O) units. Poly(glycerol-1,8-octanediol-sebacate), PGOS, synthesized by CALB catalysis with a 1:3 molar ratio of G to O units has Mn and Mw values of 9500 and 92,000, respectively. PGS undergoes fiber fusion during electrospinning, and cross-linked PGS rapidly resorbs when implanted. By decreasing the molar ratio of glycerol-to-octanediol from 1:1 to 1:4, the peak melting temperature (Tm) increased from 27 to 47 °C. PGOS with 1:3 G to O units was electrospun into nanofibers without the need for a second component. The copolymer is semicrystalline and, when cross-linked, undergoes slow in vitro mass loss (3.5 ± 1.0% in 31 days) at pH 7.4 and 37 °C. Furthermore, PGOS cross-linked films have an elastic modulus of 106.1 ± 18.6 MPa, which is more than 100 times that of cross-linked PGS. New PGOS polymers showed tunable molecular weights, better thermal properties, and excellent electrospinnability. This work expanded PGS analogues' function, making these suitable biodegradable polymers for various biomedical applications.