Covalently grafting polycation to bacterial cellulose for antibacterial and anti-cell adhesive wound dressings.

Hydrogel-based wound dressings are becoming increasingly important for wound healing. Bacterial cellulose (BC) has been commonly used as wound dressings due to its good in vitro and in vivo biocompatibility. However, pure BC does not possess antibacterial properties. In this regard, polycation gel was grafted onto the BC using a surface-initiated activator regenerated by electron transfer atom transfer radical polymerization (SI-ARGET ATRP) with subsequent quaternization for antibacterial wound dressing. Dimethylethyl methacrylate (DMAEMA) was successfully polymerized on the BC surface which was confirmed by Fourier transform infrared spectroscopy and elemental analysis. The morphology structure, specific surface area, pore size, and mechanical properties were also characterized. The quaternized PDMAEMA grafted on the BC endowed it with excellent antibacterial activity against E. coli (Gram-negative) and S. aureus (Gram-positive) with a killing rate of 89.2 % and 93.4 %, respectively. The number of cells was significantly reduced on QPD/BC hydrogel, demonstrating its good anti-adhesion ability. In vitro cellular evaluation revealed that the antibacterial wound dressing exhibited good biocompatibility. Overall, this study provides a feasible method to develop antibacterial and anti-cell adhesive hydrogel, which has a promising potential for wound healing.

Properties and toughening mechanisms of PVA/PAM double-network hydrogels prepared by freeze-thawing and anneal-swelling.

It is well known that preparation method of hydrogels has a significant effect on their properties. In this paper, freeze-thawing and anneal-swelling were applied to prepare poly(vinyl alcohol)/polyacrylamide (PVA/PAM) double-network hydrogels with covalently and physically cross-linked networks. The properties of these hydrogels were investigated and compared to control hydrogels. Results indicated that hydrogels fabricated by freeze-thawing show larger pores size and higher swelling capacity than those made by anneal-swelling and control hydrogels. Hydrogels prepared by anneal-swelling exhibit higher mechanical strength, energy dissipation, fracture energy, gel fraction and crystallinity than those made by freeze-thawing and control hydrogels. Physical cross-linking plays a key role in formation of physical-chemical double-network. The toughening mechanism of double-network hydrogel is related to their chain-fracture behavior and elasticity. The results also indicated that appropriate methods can endow hydrogels with specific microstructures and properties which would broaden current hydrogels research and applications in biomedical fields.