Changes in submicrometer structure of enzymatically hydrolyzed microcrystalline cellulose.

To understand the limitations occurring during enzymatic hydrolysis of cellulosic materials in renewable energy production, we used wide-angle X-ray scattering (WAXS), small-angle X-ray scattering (SAXS), X-ray microtomography, and transmission electron microscopy (TEM) to characterize submicrometer changes in the structure of microcrystalline cellulose (Avicel) digested with the Trichoderma reesei enzyme system. The microtomography measurements showed a clear decrease in particle size in scale of tens of micrometers. In all the TEM pictures, similar elongated and partly ramified structures were observed, independent of the hydrolysis time. The SAXS results of rewetted samples suggested a slight change in the structure in scale of 10-20 nm, whereas the WAXS results confirmed that the degree of crystallinity and the crystal sizes remained unchanged. This indicates that the enzymes act on the surface of cellulose bundles and are unable to penetrate into the nanopores of wet cellulose.

Negative Poisson ratio of crystalline cellulose in kraft cooked Norway spruce.

The tensile properties of kraft cooked Norway spruce were studied by tensile testing with in situ X-ray diffraction (XRD). Samples were of earlywood, cooked for varying times. The total lignin content of the samples was between 21.7% and 9.3%. Tensile tests with XRD were performed on wet samples, without XRD on dry samples. The tensile strength, the modulus of elasticity (MOE), and the elongation at fracture/yield were determined. X-ray diffraction was used to determine the microfibril angle (MFA) and the deformation of crystalline cellulose by monitoring the reflections 200 and 004. The (X-ray) Poisson ratio of crystalline cellulose was calculated, both before and after the yield point. The tensile strength and the MOE of the wet samples were significantly lower than in the dry samples. The tensile properties of dry samples were similar to dry earlywood samples of untreated Norway spruce. The MFA only showed notable changes due to strain when it was initially large, when a diminishing effect was observed. The Poisson ratio of crystalline cellulose was negative. The average values ranged between -0.26 and -1.17 before the yield point and between -0.86 and -1.05 after the yield point.