Cuspal movement related to different polymerization protocols.

OBJECTIVE: The aim of this study to investigate the effects of different polymerization protocols on the cuspal movement in class II composite restorations. MATERIALS AND METHODS: Human premolar teeth were prepared with class II cavities and then restored with composite and three-step and two-step etch-and-rinse adhesive systems under different curing techniques (n = 10). It was used a light- emitting-diode curing unit and the mode of polymerization were: standard (exposure for 40 seconds at 700 mW/cm(2)), pulse-delay (initial exposure for 6 seconds at 350 mW/cm(2) followed by a resting period of 3 minutes and a final exposure of 37 seconds at 700 mW/cm(2)) and soft-start curing (exposure 10 seconds at 350 mW/cm(2) and 35 seconds at 700 mW/cm(2)). The cuspal distance (µm) was measured before and after the restorative procedure and the difference was recorded as cuspal movement. The data were submitted to two-way ANOVA and Bonferroni test (p < 0.05). RESULTS: The type of adhesive system did not influenced the cuspal movement for all the curing methods. Standard protocol showed the highest values of cuspal movement and was statistically different from the pulse-delay and soft-start curing modes. CONCLUSION: Although the cuspal displacement was not completely avoided, alternative methods of photocuring should be considered to minimize the clinical consequences of composites contraction stress.

Resistência de união ao microcisalhamento de sistemas adesivos autocondicionates com graus de acidez distintos: efeito de diferentes tratamentos em substrato dentinário normal e hipermineralizado artificialmente / Microshear bond strength of adhesive systems with different degrees of acidity: effect of different treatments on normal and artificially hipermineralized dentin substrate

O objetivo deste trabalho, dividido em três estudos: foi avaliar a resistência de união de diferentes sistemas adesivos autocondicionantes, com graus de acidez distintos, frente a diferentes tratamentos dentinários: condicionamento ácido, laser e ponta diamantada em dentina normal e hipermineralizada artificialmente. No primeiro estudo, foi realizada uma busca na literatura sobre o uso do laser Er;Cr:YSGG na Odontologia Restauradora. Nos segundo e terceiro, duzentos e vinte e quatro (n = 224) molares humanos hígidos foram selecionados. Os dentes tiveram seu terço oclusal seccionado com o objetivo de expor superfície dentinária plana e foram lixados para a exposição de uma superfície dentinária uniforme e "padronizada". Os espécimes foram divididos aleatoriamente em dois diferentes grupos, de acordo com o tipo de dentina: normal (N/n=108) e hipermineralizada artificialmente (H/ n=116). O grupo H recebeu tratamento para hipermineralização e oito dentes foram selecionados aleatoriamente e observados em MEV para a confirmação do procedimento de hipermineralização. Os dentes de cada grupo foram divididos aleatoriamente em quatro diferentes subgrupos, de acordo com o sistema adesivo autocondicionante empregado: Clearfil S3 Bond e Optibond All in One ­ Passo único - (Artigo 2); Clearfil SE Bond e Adhese ­ Dois Passos ­ (Artigo 3). Cada subgrupo (n=9) recebeu diferentes tratamentos: (1) condicionamento convencional: aplicação do sistema adesivo autocondicionante segundo recomendações do fabricante; (2) condicionamento da superfície dentinária com laser Er,Cr:YSGG (Waterlase Millennium, Biolaser Technology, San Clement, CA, USA) + aplicação do sistema adesivo segundo recomendações do fabricante; (3) "asperização" da superfície dentinária com ponta diamantada 3098 + aplicação do sistema adesivo segundo recomendações do fabricante. Em seguida, matrizes transparentes cilíndricas foram posicionadas sobre cada superfície de dentina tratada com os adesivos testados e foram preenchidos com resina composta (Filtek Z350 XT - 3M ESPE) e fotoativadas por 40s. As matrizes foram removidas para expor os cilindros de resina composta. Após período de armazenagem de 24 horas em ambiente úmido a 37°C, os espécimes foram adaptados a um dispositivo para resistência de união ao microcisalhamento em uma máquina de testes universal com velocidade de travessa de 0,5 mm/min. Posteriormente, o padrão de fratura de cada espécime foi determinado. Um espécime de cada grupo foi preparado, a fim de avaliar a morfologia da interface e/ou a aparência de tags de resina em MEV. Os dados de resistência de união (µTBS) foram analisados por Two-way ANOVA e Tukey's (p<0,05). Desta maneira, baseado nos resultados apresentados nos três estudos, pode-se concluir que a utilização dos adesivos autocondicionantes empregados neste estudo podem ser uma alternativa em dentina esclerótica. E o tratamento com irradiação com o laser Er,Cr:YSGG (71,4J/cm2; 200mJ, ≈4W, 20Hz) foi favorável a µTBS em dentina hipermineralizada quando comparada a dentina normal

The aim this work, divided in three studies, was evaluate the bond strength of different adhesive systems with different degrees of acidity, to different dentinal treatments: acid etching, laser and diamond bur in normal dentin and artificially hypermineralized dentin. In the first study, it was performed a literature review on the use of the Er,Cr : YSGG in Restorative Dentistry. In the second and third, two hundred twenty-four (n = 224) human molars were selected. The teeth had their third occlusal sectioned in order to expose flat dentin surface and it were ground to expose dentin surface uniform, " standardized". The specimens were randomly divided into two groups according to the type of dentin normal (N /n = 108) and artificially hypermineralized (H / n = 116) . The group H received treatment for hypermineralization and eight teeth were randomly selected and observed by SEM to confirm the hypermineralization procedure. The teeth of each group were randomly divided into four different subgroups, according to the adhesive system used: Clearfil S3 Bond and Optibond All in One ­ One step- (Article 2 ); Clearfil SE Bond and AdheSE - Two steps - (Article 3). Each subgroup (n = 9) received different treatments: (1) conventional conditioning : application of the adhesive system according to the manufacturer's recommendations, (2) conditioning of the dentin surface with Er,Cr:YSGG laser (Waterlase Millennium Biolaser Technology, San Clement, CA, USA) + adhesive system according to the recommendations of the manufacturer, (3) " roughening " of the dentin surface with a diamond tip 3098 + adhesive system according to the recommendations of the manufacturer. Then, cylindrical transparent molds were placed on the dentin surface treated with the adhesives and were filled with composite resin (Z350 XT FiltekTM - 3M ESPE) and light-cured for 40s. The molds were removed to expose the composite resin cylinders. After a storage period of 24 hours in a humid environment at 37 °C, the samples were adjusted to a device for microshearbond strength on a universal testing machine at a speed of traverse of 0.5 mm/min. Subsequently, the fracture pattern of each specimen was determined. One sample from each group was prepared in order to evaluate the morphology of the interface and/or the appearance of the resin tags by SEM. Data microshear bond strength (µSBS) were analyzed by two-way ANOVA and Tukey 's ( p < .05 ). Thus, based on the results reported in all three studies, it can be concluded that the use of adhesives employed in this study can be an alternative to sclerotic dentin. And treatment with irradiation with the Er,Cr:YSGG (71.4 J/cm2 ; 200mJ, ≈ 4W, 20Hz) was favorable to µTBS in hypermineralized dentin than compared to normal dentin

Avaliação da resistência á flexão e determinação das propriedades mecânicas de resinas compostas e sua aplicação no método dos elementos finitos / Evaluation of flexural strength and determination of mechanical properties of composite resins and their application in finite element method

O Método de Elementos Finitos (MEF) constitui-se de uma ferramenta de amplo uso que permite, em computador, simular condições específicas em um material e determinar sua resposta para essas condições. O MEF pode ser utilizado em diversas áreas das ciências e, devido à sua grande aplicabilidade e eficiência, trabalhos com esta metodologia têm sido realizados nas diversas especialidades odontológicas, quando se deseja analisar comportamento mecânico. O objetivo deste trabalho foi determinar a resistência à flexão de resinas compostas "in vitro", suas propriedades mecânicas e comprovar a aplicabilidade do Método dos Elementos Finitos nas mesmas. As resinas compostas selecionadas para esse trabalho foram: Nano-híbrida (Tetric NCeram - Ivoclar Vivadent), Nanoparticulada (Filtek Z350 ­ 3M Espe) e Microparticulada (Heliomolar ­ Ivoclar Vivadent). A primeira etapa do trabalho foi a execução do ensaio de resistêcia à flexão segundo a norma ISO no 4049:1988 no qual os corpos de prova foram confeccionados usando uma matriz metálica. O material restaurador foi inserido e acomodado na cavidade da matriz até o preenchimento com mínimo excesso. Após o preenchimento da matriz, a resina composta foi fotoativada. Após a fotopolimerização, o corpo de prova permaneceu em repouso, para em seguida, ser cuidadosamente separado da matriz e imerso em água destilada e em seguida polido. Posteriormente, foram armazenados em água destilada, à temperatura de 37o C, por 24 horas. Os espécimes foram retirados da água, secos, e suas dimensões verificadas e inseridas na fórmula para o cálculo da resistência à flexão. Então, o teste de resistência à flexão foi executado. A segunda etapa do trabalho consistiu em determinar as propriedades mecânicas: coeficiente de Poisson e módulo de Young (módulo de elasticidade) dessas resinas compostas segundo a norma ASTM D638 - 01, sendo que os corpos de prova foram confeccionados em uma matriz, os materiais fotopolimerizados e submetidos ao teste em uma máquina de ensaio de tração. A terceira etapa do trabalho consistiu em gerar um modelo em CAD com as propriedades mecânicas: Coeficiente de Poisson e módulo de elasticidade obtidos na segunda etapa, simulando as mesmas condições do ensaio de flexão (da primeira etapa) utilizando o Método dos Elementos Finitos (MEF) comparando os resultados experimentais e computacionais, comprovando a aplicabilidade do MEF para resinas compostas. É importante salientar o envolvimento multidisciplinar, pois o estudo possibilitou a integração de várias áreas do conhecimento como a Odontologia e a Engenharia

The Finite Element Method (FEM) consists of a tool of ample use that allows, in computer, to simulate specific conditions in a material and to determine their behavior for these conditions. The FEM can be used in various fields of sciences and, because of its wide applicability and efficiency, works with this methodology have been conducted in various dental specialties, when we want to analyze mechanical behavior. The aim of this study was to determine the flexural strength of composite resins in vitro, their mechanical properties and prove the applicability of the Finite Element Method in them. The composite resins were selected for this work were: Nano-hybrid (Tetric N-Ceram - Ivoclar Vivadent), nanoparticulated (Filtek Z350 - 3M Espe) and microparticulated (Heliomolar - Ivoclar Vivadent). The first stage of this work was the flexural strenght test according to ISO 4049:1988 where the specimens were prepared using a metal matrix. The restorative material was inserted and accommodated in the cavity of the matrix filling it with minimal excess. After filling the matrix, the composite was light cured. After curing, the specimen remained at rest, to then be carefully separated from the matrix and immersed in distilled water and then polished. Were subsequently stored in distilled water at a temperature of 37o C for 24 hours. The specimens were removed from water, dried, and its dimensions recorded and entered into the formula for calculating the flexural strength. Then, the test was performed. The second stage of the study was to determine the mechanical properties: Poisson's Ratio and Young's Modulus (Modulus of Elasticity) of these composites according to ASTM D638 - 01, where the specimens were prepared using a matrix and the material cured subjected to the test in a tensile testing machine. The third stage of this work was to generate a CAD model with the mechanical properties: Poisson's Ratio and elasticity modulus obtained in the second step, simulating the same conditions as the flexural strenght test (first stage) using the Finite Element Method (FEM) comparing the experimental and computational results, proving the applicability of FEM for composites. It is important to accentuate the multidisciplinary involvement, the study allowed the integration of various knowledge areas such as dentistry and engineering