RESUMO
A novel biocomposite of carbon fiber (CF) reinforced hydroxyapatite (HA)/polylactide (PLA) was prepared by hot pressing a prepreg which consisting of PLA, HA and CF. The prepreg was manufactured by solvent impregnation process. Polymer resin PLA dissolved with chloroform was mixed with HA. After reinforcement CF bundle was impregnated in the mixture, the solvent was dried completely and subsequently hot-pressed uniaxially under a pressure of 40 MPa at 170 degrees C for 20 min. A study was carried out to investigate change in mechanical properties of CF/HA/PLA composites before and after degradation in vitro. The composites have excellent mechanical properties. A peak showed in flexural strength, flexural modulus and shear strength aspects, reaching up 430 MPa, 22 GPa, 212 MPa, respectively, as the HA content increased. Degraded in vitro for 3 months, the flexural strength and flexural modulus of the CF/HA/PLA fell 13.2% and 5.4%, respectively, while the shear strength of the CF/HA/PLA composites remains at the 190 MPa level. The SEM photos showed that there were gaps between the PLA matrix and CF after degradation. Water uptake increased to 5%, but the mass loss rate was only 1.6%. The pH values of the PBS dropped less than 0.1. That's because the alkaline of HA neutralize the acid degrades from PLA, which can prevent the body from the acidity harm.
Assuntos
Materiais Biocompatíveis/química , Carbono/química , Durapatita/química , Poliésteres/química , Fibra de Carbono , Clorofórmio/química , Vidro/química , Concentração de Íons de Hidrogênio , Teste de Materiais , Microscopia Eletrônica de Varredura/métodos , Polímeros/química , Pressão , Resistência ao Cisalhamento , Solventes/química , Estresse Mecânico , Propriedades de Superfície , Temperatura , Fatores de Tempo , Água/químicaRESUMO
Microfiber is a subgroup of microplastics and accounts for a large proportion of microplastics in aquatic environment, especially in municipal effluents. The purpose of the present study was to quantify microfiber shedding from three most populate synthetic textile fabrics: polyester, polyamide, and acetate fabrics. The results showed that more microfibers were released after washing with a pulsator laundry machine than a platen laundry machine. The greatest number of microfibers was released from acetate fabric, which was up to 74,816⯱â¯10,656 microfibers/m2 per wash, although microfibers were shed from all materials. Moreover, an increasing trend was found in the number of microfibers shedding from synthetic fabrics with the washing temperature increasing, and greater microfiber release occurred when washing fabrics with detergent rather than with water alone. The lint filter bag equipped with the pulsator laundry machine retained the longer microfibers (>1000⯵m), but not the shorter microfibers (<500⯵m) instead of releasing into the drainage system. Our data suggested that microfibers released during washing of synthetic fabrics may be an important source of microfibers in aquatic environment due to the increasing production and use of synthetic fabrics globally. Thus, more efficient filtering bags or other technologies in household washing machines should be developed to prevent and reduce the release of microfibers from domestic washing.
Assuntos
Lavanderia , Plásticos/análise , Têxteis/análise , Poluentes Químicos da Água/análise , Poliésteres , Resíduos , ÁguaRESUMO
Antimony (Sb) concentrations were measured in 10 brands of PET bottled drinking water available in supermarkets in China. To simulate general storage habits based on market research, these PET bottles with drinking water were stored for 4 weeks in a lab or a car trunk during the summer. Although the PET package material of brand A had the lowest Sb level (142.71 ± 29.81 µg/g), it showed a significant increase in Sb concentrations when stored in both the car trunk and the lab. There was significant release of Sb from the PET bottles into the water following 24 h of incubation at ≥ 40 °C (40, 50, 60, and 70 °C), especially at 70 °C. The potential health risk of Sb release from PET bottles was calculated based on daily intake values and determined to be acceptable for consumers under normal storage conditions.
Assuntos
Antimônio/análise , Água Potável/química , Polietilenotereftalatos/análise , Poluentes Químicos da Água/análise , China , Polietilenotereftalatos/química , Temperatura , Fatores de TempoRESUMO
Microplastics (MPs) have become a major global issue; their release from various products affects the aquatic environment, especially marine ecosystems. As a primary source of MPs, personal care and cosmetics products (PCCPs) containing MPs contribute to this environmental risk. We visited several supermarket chains in Beijing, China to identify PCCPs containing MPs. Overall, 7.1% of facial cleansers contained MPs, with an average weight of 25.04±10.69mgMP/g and average size of 313±130µm; whereas, 2.2% of shower gel products contained an average weight of 17.80±7.50mgMPs/g with an average size of 422±185µm. The majority of MPs were made of polyethylene, based on Raman and Fourier transform-infrared spectra analyses, while only a few were made of walnut shells and carbon particles. Finally, estimated 39tons MPs were released into the environment based on PCCPs use in China based on available data.