Biocompatibility and bioactive potential of an experimental tricalcium silicate-based cement in comparison with Bio-C repair and MTA Repair HP materials.

AIM: To evaluate the tissue reaction of a tricalcium silicate-based repair material associated with 30% calcium tungstate (TCS + CaWO4 ) in comparison to Bio-C Repair (Bio-C; Angelus) and to MTA Repair HP (MTA HP; Angelus). METHODOLOGY: Polyethylene tubes filled with one of the materials or left empty (control group, CG) were implanted into the subcutaneous tissues of rats for 7, 15, 30 and 60 days (n = 32/group). The capsule thickness, number of inflammatory cells, collagen content, interleukin-6 (IL-6), osteocalcin (OCN), von Kossa reaction and analysis under polarized light were evaluated. The data were subjected to generalized linear models for repeated measures, except the OCN. OCN data were submitted to Kruskal-Wallis and Dunn's post hoc test and Friedman followed by Nemenyi's test at significance level of 5%. RESULTS: At all time points, significant differences in the number of inflammatory cells were not observed between TCS + CaWO4 and Bio-C, whereas, at 15, 30 and 60 days, no significant difference was detected between TCS + CaWO4 and MTA HP. At all periods, significant differences were not detected in the number of fibroblasts in TCS + CaWO4 versus MTA HP, and, at 60 days, no significant difference was demonstrated between these groups and CG. Significant differences in the immunoexpression of IL-6 were not detected amongst bioceramic materials at all periods. From 7 to 60 days, significant reduction in the number of inflammatory cells, number of IL-6-immunopositive cells and in the capsule thickness was accompanied by significant increase in the collagen in all groups. OCN-immunolabelled cells, von Kossa-positive structures and amorphous calcite deposits were observed around all materials, whereas, in the CG, these structures were not seen. CONCLUSIONS: These findings indicate that the experimental material (TCS + CaWO4 ) is biocompatible and has a bioactive potential, similar to the MTA HP and Bio-C Repair, and suggest its use as a root repair material.

Biocompatibility, bioactive potential, porosity, and interface analysis calcium silicate repair cements in a dentin tube model.

OBJECTIVES: This study is to evaluate biocompatibility, bioactive potential, porosity, and dentin/material interface of Bio-C Repair (BIOC-R), MTA Repair HP (MTAHP), and Intermediate Restorative Material (IRM). MATERIALS AND METHODS: Dentin tubes were implanted into subcutaneous of rats for 7, 15, 30, and 60 days. Thickness of capsules, number of inflammatory cells (ICs), interleukin-6 (IL-6), osteocalcin (OCN), and von Kossa were evaluated. Porosity and material/dentin interface voids were also analyzed. Data were submitted to ANOVA and Tukey's tests (p < 0.05). RESULTS: IRM capsules were thicker and contained greater ICs and IL-6-immunopositive cells at 7 and 15 days. BIOC-R capsules exhibited higher thickness and ICs at 7 days and greater IL-6 at 7 and 15 days than MTAHP (p < 0.05). At 30 and 60 days, no significant difference was observed among the groups. OCN-immunopositive cells, von Kossa-positive, and birefringent structures were observed in BIOC-R and MTAHP. MTAHP exhibited higher porosity and interface voids (p < 0.05). CONCLUSIONS: BIOC-R, MTAHP, and IRM are biocompatible. Bioceramics materials demonstrate bioactive potential. MTAHP presented the highest porosity and presence of voids. CLINICAL RELEVANCE: BIOC-R and MTAHP have adequate biological properties. BIOC-R demonstrated lower porosity and presence of voids, which may represent better sealing for its clinical applications.

Bioactive potential of Bio-C Pulpo is evidenced by presence of birefringent calcite and osteocalcin immunoexpression in the rat subcutaneous tissue.

As the biocompatibility and bioactive potential of repair materials are desired characteristics in dentistry, the tissue response of Bio-C Pulpo, a bioceramic material launched on the marked by Angelus (Brazil), was compared with Biodentine (Septodont, France) and White MTA (WMTA; Angelus, Brazil). In 32 rats, 148 polyethylene tubes filled with Bio-C Pulpo, Biodentine or WMTA, and empty (CG, control group) were implanted into subcutaneous tissues for 7, 15, 30, and 60 days. The capsule thickness, numerical density of inflammatory cells (IC) and fibroblasts (Fb), amount of collagen, immunohistochemistry detection of interleukin-6 (IL-6) and osteocalcin (OCN), von Kossa and analysis under polarized light were performed. Data were subjected to two-way ANOVA followed by Tukey's test (p ≤ 0.05). At 7 and 15 days, the capsules around Bio-C Pulpo were thicker than in WMTA while, at 30 and 60 days, significant differences were not observed among the groups. Although at 7, 15, and 30 days, a greater number of IL-6-immunostained cells was found in Bio-C Pulpo and Biodentine than in WMTA, no significant difference was detected among the groups at 60 days. In all groups, the number of Fb and collagen content increased significantly over time. The capsules around materials exhibited von Kossa-positive and birefringent structures, and OCN-immunostained cells whereas, in the CG, these structures were not observed. Bio-C Pulpo, similarly to Biodentine and WMTA, is biocompatible, allows the connective tissue repair and presents bioactive potential in connective tissue of rats.

Physicochemical, biological, and antibacterial evaluation of tricalcium silicate-based reparative cements with different radiopacifiers.

OBJECTIVE: To evaluate tricalcium silicate-based (TCS) experimental materials, associated with zirconium oxide (ZrO2), calcium tungstate (CaWO4) or niobium oxide (Nb2O5) radiopacifiers, in comparison with MTA Repair HP (Angelus). METHODS: Physicochemical tests: setting time, radiopacity, pH and solubility. In vitro assays: cytotoxicity: MTT and Neutral Red - NR; cell bioactivity: alkaline phosphatase activity (ALP), Alzarin red staining (ARS) and real time PCR (qPCR). Antibacterial activity: direct contact on Enterococcus faecalis in the planktonic form. Physicochemical and ARS data were submitted to ANOVA/Tukey tests; antibacterial activity, to Kruskall-Wallis and Dunn tests; MTT, NR, ALP and qPCR were analyzed by ANOVA/Bonferroni tests (α = 0.05). RESULTS: TCS + CaWO4 presented the longest setting time and MTA HP the shortest. Except for TCS, all the materials presented radiopacity above 3 mmAl. The cements had alkaline pH, antibacterial activity, low solubility and no cytotoxic effects. The highest ALP activity occurred in 14 days, especially to TCS, TCS + ZrO2 and TCS + CaWO4. TCS + ZrO2, TCS + Nb2O5 and MTAHP had higher mineralized nodule formation than those of the negative control (NC). After 7 days, there was no difference in mRNA expression for ALP, when compared to NC. However, after 14 days there was no overexpressed ALP mRNA, especially TCS + Nb2O5, in relation to the CN. All the materials presented antimicrobial action. SIGNIFICANCE: The pure tricalcium silicate associated with ZrO2, CaWO4 or Nb2O5 had appropriate physicochemical properties, antibacterial activity, cytocompatibility and induced mineralization in Saos-2, indicating their use as reparative materials.

Acute caffeine mouth rinsing does not improve 10-km running performance in CYP1A2 C-allele carriers.

PURPOSE: This study assessed whether caffeine mouth rinsing affects 10-km run performance and vertical jump in recreational runners. METHODS: A double-blind, placebo-controlled, crossover study was conducted. Ten well-trained volunteers performed two trials, following caffeine or placebo mouth rinse, separated by seven days. Immediately before the 10-km run, a 10-second mouth rinse with either 300 mg of caffeine (1.2%) or microcrystalline cellulose (placebo) diluted in 25 mL of water was performed. Pre- and post-exercise, participants performed a vertical jump test. A Garmin Forerunner® GPS, was used to measure 10-km running time and an 11-point Borg scale was used post-exercise to measure ratings of perceived exertion. Blood samples were also collected during the visit in the laboratory in the afternoon period to classify individuals according to their CYP1A2 genotype. Vertical jump performance was evaluated using a force plate. RESULTS: Nine runners (90%) were CC homozygotes and one (10%) was an AC heterozygote for CYP1A2. There was no difference in 10-km time-trial performance (Placebo: 47.07 ± 5.18 vs. CAF: 47.45 ± 6.34 min, p = 0.89), ratings of perceived exertion (Placebo: 17 ± 1 vs. CAF: 16 ± 2, p = 0.34) or vertical jump power (Placebo, Pre: 4.5 ± 0.6 W•kg-1 and Post: 4.5 ± 0.7 W•kg-1; CAF: Pre: 4.4 ± 0.7 W•kg-1 and Post: 4.4 ± 0.8 W•kg-1, d = 0.21, p = 0.66) between trials. CONCLUSION: Acute caffeine mouth rinsing (1.2%) did not improve 10-km performance and showed similar null effects on vertical jump performance in CYP1A2 C-allele carriers.

Development and evaluation of reparative tricalcium silicate-ZrO2 -Biosilicate composites.

Biosilicate is a bioactive glass-ceramic used in medical and dental applications. This study evaluated novel reparative materials composed of pure tricalcium silicate (TCS), 30% zirconium oxide (ZrO2 ) and 10 or 20% biosilicate, in comparison with Biodentine. Setting time was evaluated based on ISO 6876 standard, radiopacity by radiographic analysis, solubility by mass loss, and pH by using a pH meter. Cytotoxicity was evaluated by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide and NR assays. Alkaline phosphatase (ALP) activity and alizarin red were used to evaluate cell bioactivity. Antimicrobial activity was assessed on Enterococcus faecalis by the direct contact test. The data were submitted to analysis of variance (ANOVA)/Tukey; Bonferroni and Kruskal-Wallis, and Dunn tests (α = 0.05). The association of Biosilicate with TCS + ZrO2 had appropriate setting time, radiopacity, and solubility, alkaline pH, and antimicrobial activity. TCS and Biodentine showed higher ALP activity in 14 days than the control (serum-free medium). All cements produced mineralized nodules. In conclusion, Biosilicate + TCS ZrO2 decreased the setting time and increased the radiopacity in comparison to TCS. Biosilicate + TCS ZrO2 presented lower solubility and higher radiopacity than Biodentine. In addition, these experimental cements promoted antimicrobial activity and mineralization nodules formation, suggesting their potential for clinical use.

Acute Caffeine Mouth Rinse Does Not Change the Hydration Status following a 10 km Run in Recreationally Trained Runners.

BACKGROUND AND AIMS: Caffeine mouth rinsing has emerged as an alternative to oral caffeine consumption for improving performance without provoking lower gastrointestinal distress. However, it remains unclear if hydration status and sweat rate are negatively affected by caffeine mouth rinsing. This study is aimed at evaluating the effects of 10 seconds of caffeine mouth rinsing (1.2% anhydrous caffeine solution) on hydration status and sweat rate following a 10 km run trial. METHODS: Ten recreationally trained runners (30.1 ± 6.4 y) volunteered to participate in this double-blind, placebo-controlled, and crossover research study. Participants completed two 10 km run trials separated by approximately one week. Immediately prior to running, participants completed a 10-second mouth rinse protocol with either 300 mg of caffeine or microcrystalline cellulose (placebo) diluted in 25 mL of water. The effects of caffeine mouth rinsing on hydration status and sweat rate were assessed following a 10 km run trial. RESULTS: Sweat rate (placebo: 15.34 ± 9.71 vs. caffeine: 11.91 ± 6.98 mL · min-1; p = 0.39), dehydration (placebo: 1.20 ± 0.57 vs. caffeine: 1.49 ± 0.29%; p = 0.15), and hydration (placebo: 15.32 ± 9.71 vs. caffeine: 11.89 ± 6.99 mL · min-1; p = 0.37) measures were not significantly different between trials. CONCLUSION: Caffeine mouth rinse does not appear to alter the hydration status or sweat rate following a 10 km run.