Maintenance of enamel properties after bleaching with high-concentrated hydrogen-peroxide gel containing calcium polyphosphate sub-microparticles.

OBJECTIVE: To assessed the physical and chemical properties of human-enamel after treatment with an experimental bleaching gel containing 35%-hydrogen peroxide (HP) and calcium polyphosphate sub-microparticles (CaPP). MATERIALS AND METHODS: Enamel/dentin specimens (4 × 4 × 3 mm) were obtained (n = 120) and allocated to different groups: control (saliva only); experimental (HP35%); commercial (whiteness-HP-Maxx); CaPP0.5% (HP35% + CaPP0.5wt%); CaPP1.5% (HP35% + CaPP1.5wt%). Three sessions were performed. The specimens' color was assessed using a spectrophotometer and the color (ΔE/ΔE00) and bleaching index (ΔWID) determined. The surface roughness and microhardness were assessed with a roughness tester and Knoop indenter. Raman spectroscopy was performed to obtain the ratios between the areas under the 431, 580, and 1070 cm-1 and the 960 cm-1 bands (430:960, 580:960, 1070:960). Kruskal-Wallis and Dunn compared the color, Ra, and SMH data. The Raman data was analyzed with Kruskal-Wallis and Dunn (α = 5%). RESULTS: The ΔE, ΔE00, and ΔWID were similar among the bleached groups (p > 0.05). The roughness was not different between the groups (p > 0.05). After the 3rd session, CaPP0.5% had higher microhardness than the experimental (p < 0.05). The 1070:960 was higher in the experimental than in the CaPP1.5% and control (p < 0.05). CONCLUSIONS: In human enamel, CaPP did not alter the bleaching effectiveness or roughness, and additionally, CaPP-containing gels increased the microhardness and preserved the mineral content when compared to the experimental without CaPP. CLINICAL RELEVANCE: Experimental bleaching gels containing calcium polyphosphate sub-microparticles as a mineral source reduce the mineral content alteration and superficial microhardness reduction, known potential side effects of the in-office bleaching treatments.

Calcium-Polyphosphate Submicroparticles (CaPP) Improvement Effect of the Experimental Bleaching Gels' Chemical and Cellular-Viability Properties.

The aim of this research was to develop and characterize the chemical and cellular-viability properties of an experimental high-concentration bleaching gel (35 wt%-H2O2) containing calcium-polyphosphate particles (CaPP) at two concentrations (0.5 wt% and 1.5 wt%). The CaPP submicroparticles were synthesized by coprecipitation, keeping a Ca:P ratio of 2:1. The CaPP morphology, size, and chemical and crystal profiles were characterized through scanning and transmission electron microscopy, energy-dispersive X-ray analysis, and X-ray diffraction, respectively. The assessed bleaching gels were experimental (without CaPP); 0.5% CaPP; 1.5% CaPP; and commercial. The gels' pH values and H2O2 concentrations (iodometric titration) were determined. The odontoblast-like cell viability after a gel's exposure was assessed by the MTT assay. The pH and H2O2 concentration were compared through a repeated-measures analysis of variance (ANOVA) and a Tukey's test and the cell viability through a one-way ANOVA and a Tukey's test using a GraphPad Prism (α < 0.05). The CaPP particles were spherical (with Ca and P, 135.7 ± 80.95 nm size) and amorphous. The H2O2 concentration decreased in all groups after mixing (p < 0.001). The 0.5% CaPP resulted in more-stable pH levels and higher viability levels than the experimental one (p < 0.05). The successful incorporation of CaPP had a positive impact on the bleaching gel's chemical and cellular-viability properties when compared to the experimental gel without these particles.

Designing Highly Photoactive Hybrid Aerogels for In-Flow Photocatalytic Contaminant Removal Using Silica-Coated Bacterial Nanocellulose Supports.

This study explores the use of silica-coated bacterial nanocellulose (BC) scaffolds with bulk macroscopic yet nanometric internal pores/structures as functional supports for high surface area titania aerogel photocatalysts to design flexible, self-standing, porous, and recyclable BC@SiO2-TiO2 hybrid organic-inorganic aerogel membranes for effective in-flow photo-assisted removal of organic pollutants. The hybrid aerogels were prepared by sequential sol-gel deposition of the SiO2 layer over BC, followed by coating of the resulting BC@SiO2 membranes with a porous titania aerogel overlayer of high surface area using epoxide-driven gelation, hydrothermal crystallization, and subsequent supercritical drying. The silica interlayer between the nanocellulose biopolymer scaffold and the titania photocatalyst was found to greatly influence the structure and composition, particularly the TiO2 loading, of the prepared hybrid aerogel membranes, allowing the development of photochemically stable aerogel materials with increased surface area/pore volume and higher photocatalytic activity. The optimized BC@SiO2-TiO2 hybrid aerogel showed up to 12 times faster in-flow photocatalytic removal of methylene blue dye from aqueous solution in comparison with bare BC/TiO2 aerogels and outperformed most of the supported-titania materials reported earlier. Moreover, the developed hybrid aerogels were successfully employed to remove sertraline drug, a model emergent contaminant, from aqueous solution, thus further demonstrating their potential for water purification.

Self-sterilizing ormosils surfaces based on photo-synzthesized silver nanoparticles.

Medical device-related infections represent a major healthcare complication, resulting in potential risks for the patient. Antimicrobial materials comprise an attractive strategy against bacterial colonization and biofilm proliferation. However, in most cases these materials are only bacteriostatic or bactericidal, and consequently they must be used in combination with other antimicrobials in order to reach the eradication condition (no viable microorganisms). In this study, a straightforward and robust antibacterial coating based on Phosphotungstate Ormosil doped with core-shell (SiO2@TiO2) was developed using sol-gel process, chemical tempering, and Ag nanoparticle photoassisted synthesis (POrs-CS-Ag). The coating was characterized by X-ray Fluorescence Spectroscopy (XRF), Field Emission Scanning Electron Microscopy (FE-SEM), Atomic Force Microscopy (AFM) and X-ray Photoelectron Microscopy (XPS). The silver free coating displays low antibacterial activity against Staphylococcus aureus and Pseudomonas aeruginosa, in opposition to the silver loaded ones, which are able to completely eradicate these strains. Moreover, the antimicrobial activity of these substrates remains high until three reutilization cycles, which make them a promising strategy to develop self-sterilizing materials, such as POrs-CS-Ag-impregnated fabric, POrs-CS-Ag coated indwelling metals and polymers, among other materials.

Physical, chemical and antimicrobial evaluation of a composite material containing quaternary ammonium salt for braces cementation.

The antibiofilm effect of iodide quaternary ammonium methacryloxy silicate (IQAMS) in Transbond XT Light Cure Adhesive resin used for braces cementation was evaluated. Fourier Transform Infrared (FTIR) spectroscopy confirmed IQAMS formation and Scanning Electron Microscopy coupled to Energy-Dispersive X-ray Spectroscopy (SEM-EDS) revealed that as coating, the quaternary ammonium groups from IQAMS were homogeneously dispersed throughout the surface. When incorporated, the composite material presented homogeneous dispersion throughout the resin. Assays with Streptococcus mutans demonstrated enhanced antibiofilm effect for the IQAMS coated resin, with much lower colony-forming units (CFU), in comparison to incorporated IQAMS. Such a difference was assigned to low availability of quaternary ammonium groups at the surface of resin when IQAMS was incorporated, hindering its antibiofilm effect. Additionally, the incorporation of IQAMS led to slight decrease in ultimate bond strength (UBS) and shear bond strength (SBS), in comparison to the neat commercial resin. Thus, the synthesized IQAMS displays great potential as antibiofilm coating or sealant to prevent oral infections in brackets during orthodontic treatment.