Surface modification of zirconia or lithium disilicate-reinforced glass ceramic by laser texturing to increase the adhesion of prosthetic surfaces to resin cements: an integrative review.

OBJECTIVE: The purpose of this study was to perform an integrative review on laser texturing the inner surface of lithium disilicate-reinforced glass ceramic or zirconia to increase their bond strength to resin-matrix cements. MATERIALS AND METHOD: A bibliographic review was performed on PubMed using the following search terms: "zirconia" OR "lithium disilicate" AND "laser" AND "surface" OR "roughness" AND "bond strength" AND "luting agent" OR "resin cement." Studies published in English language until March 15, 2023, were selected regarding the purpose of this study. RESULTS: A total of fifty-six studies were identified althoug thirteen studies were selected. The findings revealed that zirconia surfaces were significantly modified after laser irradiation resulting in macro-scale aligned retentive regions with depth values ranging from 50 to 120 µm. Average roughness values of laser-textured zirconia by Er,Cr:YSGG laser (~ 0.83 µm) were quite similar when compared to grit-blasted zirconia surfaces (~ 0.9 µm) although roughness increased up to 2.4 µm depending on the laser type and parameters. Lithium disilicate-reinforced glass ceramics textured with Er:YAG revealed an average roughness of around 3.5 µm while surfaces textured using Nd:YAG laser revealed an average roughness of 2.69 µm; that was quite similar to the roughness values recorded for etched surfaces (2.64 µm). The shear bond strength (SBS) values of zirconia surfaces textured on Nd:YVO4 laser irradiation were slightly higher (~ 33.5 MPa) than those recorded for grit-blasted zirconia surfaces (28 MPa). Laser-textured zirconia surfaces on CO2 laser revealed higher SBS values (18.1 ±0.8 MPa) than those (9.1 ± 0.56 MPa) recorded for untreated zirconia surfaces. On lithium disilicate-reinforced glass ceramics, higher SBS values to resin-matrix cements were recorded for specimens textured with a combination of fractional CO2 laser irradiation and HF acid etching (~ 22-24 MPa) when compared with grit-blasted specimens (12.2 MPa). Another study revealed SBS values at around 27.5 MPa for Er:YAG-textured lithium disilicate-reinforced glass ceramics to resin-matrix cements. CONCLUSIONS: The laser irradiation at high power increases the roughness of the inner surface of lithium disilicate-reinforced glass ceramic or zirconia leading to an enhanced bond strength to resin-matrix cements. Thus, the laser type and irradiation parameters can be adjusted to enhance the macro- and micro-scale retention of zirconia and glass ceramic surfaces to resin-matrix cements. CLINICAL RELEVANCE: Alternative methods for surface modification of lithium disilicate-reinforced glass ceramic and zirconia surfaces have been assessed to provide proper morphological aspects for enhanced adhesion to resin-matrix cements. An increase in the bond strength of glass ceramics or zirconia to resin-matrix cements can improve the long-term performance of cemented prosthetic structures in the oral cavity.

Effect of inorganic fillers on the light transmission through traditional or flowable resin-matrix composites for restorative dentistry.

OBJECTIVES: The aim of this in vitro study was to evaluate the light transmission through five different resin-matrix composites regarding the inorganic filler content. METHODS: Resin-matrix composite disc-shaped specimens were prepared on glass molds. Three traditional resin-matrix composites contained inorganic fillers at 74, 80, and 89 wt. % while two flowable composites revealed 60 and 62.5 wt. % inorganic fillers. Light transmission through the resin-matrix composites was assessed using a spectrophotometer with an integrated monochromator before and after light curing for 10, 20, or 40s. Elastic modulus and nanohardness were evaluated through nanoindentation's tests, while Vicker's hardness was measured by micro-hardness assessment. Chemical analyses were performed by FTIR and EDS, while microstructural analysis was conducted by optical microscopy and scanning electron microscopy. Data were evaluated using two-way ANOVA and Tukey's test (p < 0.05). RESULTS: After polymerization, optical transmittance increased for all specimens above 650-nm wavelength irradiation since higher light exposure time leads to increased light transmittance. At 20- or 40-s irradiation, similar light transmittance was recorded for resin composites with 60, 62, 74, or 78-80 wt. % inorganic fillers. The lowest light transmittance was recorded for a resin-matrix composite reinforced with 89 wt. % inorganic fillers. Thus, the size of inorganic fillers ranged from nano- up to micro-scale dimensions and the high content of micro-scale inorganic particles can change the light pathway and decrease the light transmittance through the materials. At 850-nm wavelength, the average ratio between polymerized and non-polymerized specimens increased by 1.6 times for the resin composite with 89 wt. % fillers, while the composites with 60 wt. % fillers revealed an increased ratio by 3.5 times higher than that recorded at 600-nm wavelength. High mean values of elastic modulus, nano-hardness, and micro-hardness were recorded for the resin-matrix composites with the highest inorganic content. CONCLUSIONS: A high content of inorganic fillers at 89 wt.% decreased the light transmission through resin-matrix composites. However, certain types of fillers do not interfere on the light transmission, maintaining an optimal polymerization and the physical properties of the resin-matrix composites. CLINICAL SIGNIFICANCE: The type and content of inorganic fillers in the chemical composition of resin-matrix composites do affect their polymerization mode. As a consequence, the clinical performance of resin-matrix composites can be compromised, leading to variable physical properties and degradation.

Root canal disinfection and maintenance of the remnant tooth tissues by using grape seed and cranberry extracts.

The purpose of this study was to perform an integrative review on the effects of cranberry and grape seed extracts concerning the disinfection of root canals maintaining the strength of the remnant tooth tissues' structure. A bibliographical search was carried out on the PubMed electronic platform using the following key terms: cranberry, grape seed, vaccinium macrocarpon, proanthocyanidin, antibacterial, antimicrobial, decontamination, disinfection, bacteria removal, bacteria eradication, bacteria elimination, endodontic, root canal, faecalis, and strength. The inclusion criteria involved articles published in the English language, until March, 2022, reporting the antibacterial effect of grape seed and cranberry extracts. Of 185 studies identified, 13 studies were selected for the present review. The grape seed extract (GSE), composed of proanthocyanidins, showed an antioxidant activity against the main bacteria found in endodontic secondary infection. The percentage of bacteria removal was recorded at around 96.97% by using GSE. Studies on cranberry extracts, which are composed of proanthocyanidins, revealed antimicrobial effects against bacteria related to periodontitis and dental caries. Additionally, GSE or cranberry allowed the dentin collagen cross-linking that preserved the 3D collagen network leading to the maintenance of the strength of the remnant tooth structure. However, the contaminated smear layer could not be removed by using only GSE or cranberry. Cranberry extracts and GSE revealed a significant antimicrobial activity in endodontic disinfection without changing the mechanical properties of the remnant dentin tissues. Furthermore, those components can be associated with traditional compounds to enhance their antimicrobial effects and eliminate the smear layer.

Toxicity of resin-matrix cements in contact with fibroblast or mesenchymal cells.

The main aim of this study was to perform an integrative review on the toxic effects of resin-matrix cements and their products in contact with fibroblasts or mesenchymal cells. A bibliographic search was performed on PubMed using the following search terms: "cytotoxicity" AND "fibroblast" OR "epithelial" OR "mesenchymal" AND "polymerization" OR "degree of conversion" OR "methacrylate" OR "monomer" AND "resin cement" OR "resin-based cement". The initial search in the available database yielded a total of 277 articles of which 21 articles were included in this review. A decrease in the viability of mouse fibroblasts ranged between 13 and 15% that was recorded for different resin-matrix cements after light curing exposure for 20 s. The viability of human fibroblasts was recorded at 83.11% after light curing for 20 s that increased up to 90.9% after light curing exposure for 40 s. Most of the studies linked the highest toxicity levels when the cells were in contact with Bis-GMA followed by UDMA, TEGDMA and HEMA. Resin-matrix cements cause a cytotoxic reaction when in contact with fibroblasts or mesenchymal cells due to the release of monomers from the polymeric matrix. The amount of monomers released from the resin matrix and their cytotoxicity depends on the polymerization parameters.

Surface modification of zirconia dental implants by laser texturing.

The aim of this work was to perform an integrative literature review on the influence of laser irradiation on zirconia implants to enhance surface topographic aspects and the biological response for osseointegration. An electronic search was carried out on the PubMed database using the following search terms: "zirconia" AND "laser" AND "surface modification" OR "surface treatment" AND "dental implants" OR "bone" OR "osteoblast" OR "osseointegration." Of the identified articles, 12 studies were selected in this review. Results reported that the laser irradiation was capable of promoting changes on the zirconia surfaces regarding topographic aspects, roughness, and wettability. An increase in roughness was recorded at micro- and nano-scale and it resulted in an enhanced wettability and biological response. Also, adhesion, spreading, proliferation, and differentiation of osteogenic cells were also enhanced after laser irradiation mainly by using a femtosecond laser at 10nJ and 80 MHz. After 3 months of osseointegration, in vivo studies in dogs revealed a similar average percentage of bone-to-implant contact (BIC) on zirconia surfaces (around 47.9 ± 16%) when compared to standard titanium surfaces (61.73 ±16.27%), denoting that there is no significant difference between such different materials. The laser  approach revealed several parameters that can be used for zirconia surface modification such as irradiation intensity, time, and frequency. Laser irradiation parameters can be optimized and well-controlled to reach desirable surface morphologic aspects and biological response concerning the osseointegration process.

The influence of inorganic fillers on the light transmission through resin-matrix composites during the light-curing procedure: an integrative review.

PURPOSE: The objective of this study was to perform an integrative review on the effect the inorganic fillers on the light transmission through the resin-matrix composites during the light-curing procedure. METHOD: A bibliographic review was performed on PubMed using the following search terms: "fillers" OR "particle" AND "light curing" OR "polymerization" AND "light transmission" OR "light absorption" OR "light irradiance" OR "light attenuation" OR "light diffusion" AND "resin composite." The search involved articles published in English language in the last 10 years. RESULTS: Selected studies reported a decrease in biaxial strength and hardness in traditional resin-matrix composites in function of the depth of polymerization. However, there were no significant differences in biaxial strength and hardness recorded along the polymerization depth of Bulk-Fill™ composites. Strength and hardness were enhanced by increasing the size and content of inorganic fillers although some studies revealed a progressive decrease in the degree of conversion on increasing silica particle size. The translucency of glass-ceramic spherical fillers promoted light diffusion mainly in critical situations such as in the case of deep proximal regions of resin-matrix composites. CONCLUSIONS: The amount of light transmitted through the resin-matrix composites is influenced by the size, content, microstructure, and shape of the inorganic filler particles. The decrease of the degree of conversion affects negatively the physical and mechanical properties of the resin-matrix composites. CLINICAL RELEVANCE: The type and content of inorganic fillers in the chemical composition of resin-matrix composites do affect their polymerization. As a consequence, the clinical performance of resin-matrix composites can be compromised leading to variable physical properties and degradation. The polymerization mode of resin-matrix composites can be improved according to the type of inorganic fillers in their chemical composition.

Surface modification of glass fiber-reinforced composite posts to enhance their bond strength to resin-matrix cements: an integrative review.

BACKGROUND: Endodontically treated teeth usually can reveal an extensive loss of dental structure and require the use of intraradicular posts to provide adequate support and retention. Retention of the post depends on the surface treatment of the endodontic post itself and on the root canal dentin as well as on the type of resin-matrix cement. PURPOSE: The main aim of this study was to conduct an integrative review on the influence of different surface treatment methods of glass fiber-reinfored resin composite (GFRC) posts on their push-out bond strength to resin-matrix cements in endodontically treated teeth rehabiliation. METHOD: A literature search was performed on PubMed (via National Library of Medicine) regarding articles published within the last 10 years, using the following combination of search terms: "intracanal post" OR "endodontic post" OR "root canal post" OR "intraradicular post" OR "glass fiber" AND "resin cement" AND "adhesion" OR "bond strength" OR "shear bond strength" OR "push out". RESULTS: Results from the selected studies recorded the highest push-out bond strength around 22.5 MPa) on GFRC posts to resin-matrix cements when the surfaces were pre-treated by grit-blasting with silicate followed by silane conditioning. However, high values of push-out bond strength (21.5 MPa) were also noticed for GFRC posts after etching with hydrogen peroxide followed by silance conditioning. Thus, the highest values of bond strength of endodontic posts to the resin-matrix cements were recorded when a combined physico-chemical approach was assessed. Non-treated surfaces showed the lowest bond strength values between 5 to and 9 MPa. Surface analyses of GFRC posts showed an increased roughness after grit-blasting or etching that promoted a mechanical interlocking of the adhesive and resin-matrix cements. CONCLUSION: The combined treatment of glass fiber-reinforced resin composite post surfaces by physical and chemical methods can promote the increase in roughness and chemical functionalization of the surfaces prior to cementation., That results in a high mechanical interlocking of the resin-matrix cements and a stable retention of the teeth root intracanal posts. CLINICAL RELEVANCE: Combining chemical and physical modification methods of surfaces can provide the most promising adhesion-enhancing pathways of GFRC posts to resin-matrix cements, that can decrease the risk of clinical failures by fracture and detachment of endodontic posts.

Remnant oral biofilm and microorganisms after autoclaving sterilization of retrieved healing abutments.

OBJECTIVE: The purpose of this study was to evaluate the sterilization effectiveness against biofilms on retrieved healing abutments used in implant dentistry. BACKGROUND: A large number of clinicians reuse healing abutments to decrease treatment costs although it can promote infection due to the presence of remnant biofilm biomass. METHODS: One hundred and eighty-five titanium healing abutments previously used for 3 months in oral cavity were assessed in this study. Abutments were submitted to cleaning, chemical disinfection, and autoclave sterilization according to clinical guidelines. The abutments were aseptically placed into glass tubes containing specific bacterial growth medium and then incubated for 10 days. From glass tubes with bacterial growth, 100 µl medium was transferred to Schaedler's agar for morphological identification and counting of strict anaerobes and to Columbia blood agar for presumptive identification of facultative anaerobes after incubation. Isolated strains were then identified at species level by enzymatic and biochemical tests within API microorganism detection platform. Also, polymerase chain reaction (PCR) was performed for identification of undefined strains. RESULTS: After the standard cleaning and sterilization procedures, fifty-six (approximately 30%) retrieved abutments showed the presence of remnant biofilm biomass. The bacteria identified into the remnant biofilms covering the abutments were representative of the commensal oral microbiota including Aggregatibacter actinomycetemcomitans, Prevotella intermedia, and Enterococcus faecalis. CONCLUSION: Although some healing abutments did not reveal the existence of bacteria, organic components from biofilm biomass are still strongly adhered on the retentive micro-regions and surfaces of abutments and therefore that would support the accumulation of biofilm including pathogenic species leading to patients' cross-infections. Further studies should be performed on the assessment of different materials, design, and connections of the healing abutments associated with clinical disinfection procedures in implant dentistry.

Cytotoxic effects of submicron- and nano-scale titanium debris released from dental implants: an integrative review.

OBJECTIVE: This integrative review aimed to report the toxic effect of submicron and nano-scale commercially pure titanium (cp Ti) debris on cells of peri-implant tissues. MATERIALS AND METHODS: A systematic search was carried out on the PubMed electronic platform using the following key terms: Ti "OR" titanium "AND" dental implants "AND" nanoparticles "OR" nano-scale debris "OR" nanometric debris "AND" osteoblasts "OR "cytotoxicity" OR "macrophage" OR "mutagenic" OR "peri-implantitis". The inclusion criteria involved articles published in the English language, until December 26, 2020, reporting the effect of nano-scale titanium particles as released from dental implants on the toxicity and damage of osteoblasts. RESULTS: Of 258 articles identified, 14 articles were selected for this integrative review. Submicron and nano-scale cp Ti particles altered the behavior of cells in culture medium. An inflammatory response was triggered by macrophages, fibroblasts, osteoblasts, mesenchymal cells, and odontoblasts as indicated by the detection of several inflammatory mediators such as IL-6, IL-1ß, TNF-α, and PGE2. The formation of a bioactive complex composed of calcium and phosphorus on titanium nanoparticles allowed their binding to proteins leading to the cell internalization phenomenon. The nanoparticles induced mutagenic and carcinogenic effects into the cells. CONCLUSIONS: The cytotoxic effect of debris released from dental implants depends on the size, concentration, and chemical composition of the particles. A high concentration of particles on nanometric scale intensifies the inflammatory responses with mutagenic potential of the surrounding cells. CLINICAL RELEVANCE: Titanium ions and debris have been detected in peri-implant tissues with different size, concentration, and forms. The presence of metallic debris at peri-implant tissues also stimulates the migration of immune cells and inflammatory reactions. Cp Ti and TiO2 micro- and nano-scale particles can reach the bloodstream, accumulating in lungs, liver, spleen, and bone marrow.

The influence of zirconia veneer thickness on the degree of conversion of resin-matrix cements: an integrative review.

OBJECTIVE: The main aim of this study was to conduct an integrative review on the influence of the zirconia veneer thickness on the degree of conversion of resin-matrix cements. MATERIALS AND METHOD: An electronic search was performed on PubMed using a combination of the following search items: zirconia, thickness, veneer, degree of conversion, resin cement, light curing, and polymerization. Articles published in the English language, up to July 2020, were included regarding the influence of ceramic veneer thickness on the degree of conversion of resin-matrix cements. Randomized controlled trials and prospective cohort studies were also evaluated. RESULTS: Of the 21 selected studies, 9 investigated the light-curing effect, while five other articles evaluated the ceramic translucency. Three studies evaluated the degree of conversion of the resin-matrix cement while four articles assessed the veneer thickness. Results revealed a significant decrease of light transmission through the zirconia with a thickness ranging from 0.1 up to 1.5 mm. However, the ultra-thin thickness around 0.1 and 0.3 mm allowed a full polymerization of the dual-curing resin-matrix cement resulting in the integrity of the interface properties. The light-curing process of resin-matrix cements is also affected by the shade, chemical composition, and microstructure of zirconia and resin cement. Optimal conditions of light-curing are required to reach the threshold intensity of light and energy for polymerization of resin-matrix cements. CONCLUSIONS: The increase in zirconia veneer thickness negatively affects the degree of conversion of resin-matrix cements. Also, shade and microstructure are key factor to improve the light curing of resin cements. CLINICAL RELEVANCE: Clinicians should consider the zirconia thickness on resin-based cementation since a higher veneer thickness can negatively affect the light irradiation intensity towards the dual-curing resin-matrix cement. Thus, the degree of conversion of the resin-matrix cement can decrease leading to a low chemical stability (e.g., color instability) and poor mechanical properties.

The resin-matrix cement layer thickness resultant from the intracanal fitting of teeth root canal posts: an integrative review.

OBJECTIVE: The aim of this study was to perform an integrative review on the layer thickness and microstructure of resin-matrix cements around custom-made or standard teeth root intracanal posts. MATERIALS AND METHODS: An electronic search was conducted on the PubMed using a combination of the following scientific terms: intraradicular post, root intracanal post, resin cement, thickness, adaptation, endodontic post, layer thickness, fit, shape, and endodontic core. The literature selection criteria accepted articles published in the English language, up to May 2021, involving in vitro analyses, meta-analyses, randomized controlled trials, and prospective cohort studies. RESULTS: The search identified 154 studies, of which 24 were considered relevant to this study. The selected studies provided important data considering cement layer thickness, tooth preparation, endodontic post, and type of resin-matrix cement. The anatomical variability of root canal systems, such as the oval- or C-shaped, represents a challenge in dental restoration with tooth root intracanal posts. The fitting of intracanal posts to different root regions is variable resulting in thick and irregular layers of resin-matrix cement. Defects like pores, micro-cracks, and micro-gaps were detected in the resin-matrix cement microstructure and represent spots of stress concentration and fracture. Custom-made tooth root intracanal posts provide a proper fitting and decrease the layer thickness of resin-matrix cement. CONCLUSIONS: In fact, the layer thickness of resin-matrix cements depends on the fitting of endodontic posts to tooth root canals. An increase of resin cement thickness causes the appearance of defects like pores, micro-cracks, and micro-gaps that can induce stress concentration and fractures at interfaces. CLINICAL RELEVANCE: The fitting of the endodontic post into the teeth root canal determine the layer thickness of the resin-matrix cement to establish an adequate retention. However, the increase in the thickness of the resin-matrix cement layer can lead to a high number of defects like pores or cracks and therefore decrease the strength of the interface.

Comparison of CAD-CAM and traditional chairside processing of 4-unit interim prostheses with and without cantilevers: Mechanics, fracture behavior, and finite element analysis.

STATEMENT OF PROBLEM: How processing by computer-aided design and computer-aided manufacturing (CAD-CAM) or traditional chairside fabrication techniques affects the presence of defects and the mechanical properties of interim dental prostheses is unclear. PURPOSE: The purpose of this in vitro study was to compare the effects of CAD-CAM versus traditional chairside material processing on the fracture and biomechanical behavior of 4-unit interim prostheses with and without a cantilever. MATERIAL AND METHODS: Two types of 4-unit interim prostheses were fabricated with abutments on the first premolar and first mandibular molar, one from a prefabricated CAD-CAM block and one with a traditional chairside polymer-monomer autopolymerizing acrylic resin (n=10). Both groups were assessed by compressive strength testing and additionally with or without a cantilevered second molar by using a universal testing machine with a 5-kN load cell. A finite element model (FEM) was built by scanning both prosthesis designs. Finite element analysis (FEA) replicated the experimental conditions to evaluate the stress distribution through the prostheses. RESULTS: Interim fixed prostheses manufactured by CAD-CAM showed significantly higher mean fracture loading values (3126 N to 3136 N) than for conventionally made interim fixed prostheses (1287 N to 1390 N) (P=.001). The presence of a cantilever decreased the fracture loading mean values for CAD-CAM (1954 N to 2649 N), although the cantilever did not influence the traditional prostheses (1268 N to 1634 N). The highest von Mises stresses were recorded by FEA on the occlusal surface, with the cantilever design, and at the transition region (connector) between the prosthetic teeth. CONCLUSIONS: Interim partial prostheses produced by CAD-CAM had a higher strength than those manufactured traditionally. The presence of a cantilever negatively affected the strength of the prostheses, although the structures manufactured by CAD-CAM still revealed high strength and homogenous stress distribution on occlusal loading.

Bioactive-Enhanced Polyetheretherketone Dental Implant Materials: Mechanical Characterization and Cellular Responses.

The aim of this study was to characterize the mechanical properties of a bioactive-modified polyetheretherketone (PEEK) manufacturing approach for dental implants and to compare the in vitro biological behavior with titanium alloy (Ti6Al4V) as the reference. PEEK, PEEK with 5% hydroxyapatite (HA), PEEK with 5% beta-tricalcium phosphate (ßTCP), and Ti6Al4V discs were produced using hot pressing technology to create a functionally graded material (FGM). Surface roughness values (Ra, Rz), water contact angle, shear bond strength, and Vickers hardness tests were performed. Human osteoblasts and gingival fibroblasts bioactivity was evaluated by a resazurin-based method, alkaline phosphatase activity (ALP), and confocal laser scanning microscopy (CLSM) images of fluorescent-stained fibroblasts. Morphology and cellular adhesion were confirmed using field emission gun-scanning electron microscopy (FEG-SEM). Group comparisons were tested using analysis of variance (Tukey post hoc test), α = .05. All groups presented similar roughness values (P > .05). Ti6Al4V group was found to have the highest contact angle (P < .05). Shear bond strength and Vickers hardness of different PEEK materials were similar (P > .05); however, the mean values in the Ti6Al4V group were significantly higher when compared with those of the other groups (P < .05). Cell viability and proliferation of osteoblast and fibroblast cells were higher in the PEEK group (P < .05). PEEK-ßTCP showed the highest significant ALP activity over time (P < .05 at 14 days of culture). An enhanced bone and soft-tissue cell behavior on pure PEEK was obtained to the gold standard (Ti6Al4V) with equivalent roughness. The results substantiate the potential role of chemical composition rather than physical properties of materials in biological responses. The addition of 5% HA or ßTCP by FGM did not enhance PEEK mechanical properties or periodontal cell behavior.

Surface damage of dental implant systems and ions release after exposure to fluoride and hydrogen peroxide.

OBJECTIVE: The aim of this study was to evaluate surface changes on dental implant systems and ions release after immersion in fluoride and hydrogen peroxide. METHODS: Ten implant-abutment assemblies were embedded in acrylic resin and cross-sectioned along the implant vertical axis. Samples were wet ground and polished. Delimited areas of groups of samples were immersed in 1.23% sodium fluoride gel (F) or in 35% hydrogen peroxide (HP) for 16 min. Gels (n = 3) were collected from the implant surfaces and analyzed by inductively coupled plasma mass spectrometry (ICP-MS), to detect the concentration of metallic ions released from the implant systems. Selected areas of the abutment and implant (n = 15) were analyzed by atomic force microscopy (AFM) and scanning electron microscopy (SEM). RESULTS: SEM images revealed surface topographic changes on implant-abutment joints after immersion in fluoride. Implants showed excessive oxidation within loss of material, while abutment surfaces revealed intergranular corrosion after immersion in fluoride. ICP-MS results revealed a high concentration of Ti, Al, V ions in fluoride after contact with the implant systems. Localized corrosion of implant systems could not be detected by SEM after immersion in hydrogen peroxide although the profilometry showed increase in roughness. ICP-MS showed the release of metallic ions in hydrogen peroxide medium after contact with dental implants. CONCLUSION: Therapeutical substances such as fluorides and hydrogen peroxide can promote the degradation of titanium-based dental implant and abutments leading to the release of toxic ions.

Injectable platelet rich fibrin: cell content, morphological, and protein characterization.

OBJECTIVES: The aim of the present study was to evaluate the blood cell content, morphological aspects, gene expression of type I collagen, and release of growth factors on an injectable platelet rich fibrin (i-PRF). MATERIALS AND METHODS: Blood samples were collected from 15 volunteers to prepare i-PRF samples. Peripheral blood was used as a control group. Blood clot and i-PRF samples were cultured for 10 days. The supernatant of the samples was collected for ELISA immunoassay quantification of PDGF and VEGF growth factors over periods of 1, 8, 24, 72, and 240 h. I-PRF and blood clot samples were biologically characterized using histological and immunohistochemistry analysis for IL-10, osteocalcin, and TGF-ß. Scanning electron microscopy (SEM) was used to inspect the fibrin network and distribution of blood platelets and leukocytes. Reverse transcriptase polymerase chain reaction (RT-PCR) method was used to evaluate gene expression for type I collagen. RESULTS: A higher concentration of platelets and lymphocytes was recorded in i-PRF than in peripheral blood (p < 0.05). The release of VEGF was higher in blood clot samples (1933 ± 704) than that for i-PRF (852 ± 376; p < 0.001). Immunohistochemistry showed upregulation of TGF-B, IL-10, and osteocalcin in the i-PRF group. RT-PCR showed increased type I collagen gene expression in i-PRF (p < 0.05). SEM images revealed agglomeration of platelets in some regions, while a fibrin networking was noticeable in the entire i-PRF sample. CONCLUSIONS: Injectable platelet rich fibrin becomes a good approach for soft and mineralized tissue healing considering the formation of a three-dimensional fibrin network embedding platelets, leukocytes, type I collagen, osteocalcin, and growth factors. Indeed, the injectable platelet rich fibrin can be indicated in several medical applications regarding bioactivity, simplied technique, and flowable mixing with other biomaterials. CLINICAL RELEVANCE: Morphological, cell, and protein characterization of platelet rich fibrin provides a better understanding of the clinical effects and improvement of clinical guidelines for several medical applications. Once well physicochemical and biologically characterized, the use of an injectable platelet rich fibrin can be extended to other applications in the field of orthopedics, periodontics, and implant dentistry on the repairing process of both soft and mineralized tissues.

Mechanical integrity of cement- and screw-retained zirconium-lithium silicate glass-ceramic crowns to Morse taper implants.

STATEMENT OF PROBLEM: The improved esthetics of ceramic dental prostheses has increased their popularity, although their high elastic modulus and low fracture toughness and tensile strength may reduce the long-term performance of dental prostheses. PURPOSE: The purpose of this in vitro study was to assess the mechanical integrity of zirconium-lithium silicate glass-ceramic crowns cement- and screw-retained to a titanium implant-abutment after fatigue. MATERIAL AND METHODS: Forty titanium implants were placed in polyacetal to mimic bone support. Abutments were tightened to the implants to 20 Ncm by using a digital handheld torque meter. The implant abutment assemblies received a pressed maxillary premolar crown, either lithium disilicate (LD) or zirconium-lithium silicate glass-ceramic (LZS). The specimens (n=10) were subjected to fatigue at 200 N and 5 Hz for 500 000 cycles in a Ringer electrolytic solution (37°C). After fatigue, the crowns were removed to evaluate removal torque values on the implant-abutment connection. The remaining crown-implant-abutment assemblies were cross-sectioned at 90 degrees to the implant-abutment joint for inspection of cracks and the micro-gaps by scanning electron microscopy. RESULTS: Removal torque values before fatigue were recorded at 18 ±1.63 Ncm for the LD group and 18.2 ±0.81 Ncm for the LZS group. After fatigue, the removal torque values decreased significantly (12.8 ±1.6 Ncm for LD, 14.9 ±1.08 Ncm for LZS; P<.05). Micro-gaps at the implant-abutment connections were measured at 0.9 ±0.3 µm before fatigue and at 4.2 ±0.9 µm after fatigue. Cracks were detected at the crown adhesive or at the adhesive-abutment interface for both systems after fatigue. CONCLUSIONS: Cement- and screw-retained implant zirconium-lithium silicate glass-ceramic crowns revealed effective fatigue resistance on mean cyclic loading in an electrolyte solution. However, mechanical instability of the crown-adhesive-abutment interfaces and implant-abutment joints was detected after fatigue.

Wear of Morse taper and external hexagon implant joints after abutment removal.

The aim of this in vitro study was to evaluate the removal torque values on abutments and the morphological wear aspects of two different dental implant joints after immersion in a medium containing biofilm from human saliva. Twenty implant-abutment assemblies were divided into four groups in this study: (A) Morse taper free of medium containing biofilm, and (B) after contact with a medium containing biofilm from human saliva; (C) External Hexagon free of medium containing biofilm, and (D) after contact with medium containing biofilm from human saliva. The abutments were firstly torqued to the implants according to the manufacturer´s recommendations, using a handheld torque meter. Groups B and D were immersed into 24 well-plates containing 2 ml BHI medium with microorganisms for 72 h at 37 °C under microaerophilic conditions. After detorque evaluation, the abutments were removed and the implants were analyzed by scanning electron microscopy (SEM) and profilometry. On the detorque evaluation, the torque values decreased for the external hexagon implants and increased for the Morse taper implants. However, the values were lower when both implant-abutment assemblies were in contact with a medium containing biofilm from human saliva. The wear areas of contacting surfaces of the implants were identified by SEM. The highest average roughness values were recorded on the surfaces free of biofilm. The medium containing biofilm from human saliva affected the maintenance of the torque values on Morse taper and external hexagon abutments. Additionally, the removal of abutment altered the inner implant surfaces resulting in an increase of wear of the titanium-based connection.

THERMAL RESIDUAL STRESSES IN BILAYERED, TRILAYERED AND GRADED DENTAL CERAMICS.

Layered ceramic systems are usually hit by residual thermal stresses created during cooling from high processing temperature. The purpose of this study was to determine the thermal residual stresses at different ceramic multi-layered systems and evaluate their influence on the bending stress distribution. Finite elements method was used to evaluate the residual stresses in zirconia-porcelain and alumina-porcelain multi-layered discs and to simulate the 'piston-on-ring' test. Temperature-dependent material properties were used. Three different multi-layered designs were simulated: a conventional bilayered design; a trilayered design, with an intermediate composite layer with constant composition; and a graded design, with an intermediate layer with gradation of properties. Parameters such as the interlayer thickness and composition profiles were varied in the study. Alumina-porcelain discs present smaller residual stress than the zirconia-porcelain discs, regardless of the type of design. The homogeneous interlayer can yield a reduction of ~40% in thermal stress relative to bilayered systems. Thinner interlayers favoured the formation of lower thermal stresses. The graded discs showed the lowest thermal stresses for a gradation profile given by power law function with p=2. The bending stresses were significantly affected by the thermal stresses in the discs. The risk of failure for all-ceramic dental restorative systems can be significantly reduced by using trilayered systems (homogenous or graded interlayer) with the proper design.

The bending stress distribution in bilayered and graded zirconia-based dental ceramics.

The purpose of this study was to evaluate the biaxial flexural stresses in classic bilayered and in graded zirconia-feldspathic porcelain composites. A finite element method and an analytical model were used to simulate the piston-on-ring test and to predict the biaxial stress distributions across the thickness of the bilayer and graded zirconia-feldspathic porcelain discs. An axisymmetric model and a flexure formula of Hsueh et al. were used in the FEM and analytical analysis, respectively. Four porcelain thicknesses were tested in the bilayered discs. In graded discs, continuous and stepwise transitions from the bottom zirconia layer to the top porcelain layer were studied. The resulting stresses across the thickness, measured along the central axis of the disc, for the bilayered and graded discs were compared. In bilayered discs, the maximum tensile stress decreased while the stress mismatch (at the interface) increased with the porcelain layer thickness. The optimized balance between both variables is achieved for a porcelain thickness ratio in the range of 0.30-0.35. In graded discs, the highest tensile stresses were registered for porcelain rich interlayers (p=0.25) whereas the zirconia rich ones (p=8) yield the lowest tensile stresses. In addition, the maximum stresses in a graded structure can be tailored by altering compositional gradients. A decrease in maximum stresses with increasing values of p (a scaling exponent in the power law function) was observed. Our findings showed a good agreement between the analytical and simulated models, particularly in the tensile region of the disc. Graded zirconia-feldspathic porcelain composites exhibited a more favourable stress distribution relative to conventional bilayered systems. This fact can significantly impact the clinical performance of zirconia-feldspathic porcelain prostheses, namely reducing the fracture incidence of zirconia and the chipping and delamination of porcelain.

Fitting of Different Intraradicular Composite Posts to Oval Tooth Root Canals: A Preliminary Assessment.

The purpose of the present study was to perform a preliminary analysis of the fitting of different fiber-reinforced composite (GFRC) posts to tooth root canals and determine the resin cement layer thickness. The following GFRC posts were assessed: bundle posts (Rebilda GTTM, VOCO, Germany), sleeve system (SAPTM, Angelus Ind, Brazil), and accessory posts (ReforpinTM, Angelus, Brazil). Twenty-four freshly extracted mandibular single-rooted pre-molars were endodontically treated and divided into six groups, according to the type of GFRC post and resin cement (self-adhesive or conventional dual-cured). Then, specimens were cross-sectioned and inspected by optical microscopy regarding the cement layer thickness and presence of defects such as pores, voids, or fissures were assessed. Bundle and accessory posts revealed a regular distribution of resin cement with a lower number of voids than found with sleeve systems. The sleeve system posts showed poor fitting at the apical portion of the root canals. The type of resin cement did not affect the thickness of the interface, although both bundle and accessory posts allow a better distribution of resin cement and fibers. The present preliminary study reveals interesting insights on the fitting of bundle and accessory posts to root dentin and resin cement layer thickness in oval-shape root canals. The sleeve system posts showed adequate fitting only at the coronal portion of the canals.