Designing of Drug Delivery Systems to Improve the Antimicrobial Efficacy in the Periodontal Pocket Based on Biodegradable Polyesters.

Delivery systems for biologically active substances such as proanthocyanidins (PCANs), produced in the form of electrospun nonwoven through the electrospinning method, were designed using a polymeric blend of poly(L-lactide-co-glycolide) (PLGA)and poly[(R,S)-3-hydroxybutyrate] ((R,S)-PHB). The studies involved the structural and thermal characteristics of the developed electrospun three-dimensional fibre matrices unloaded and loaded with PCANs. In the next step, the hydrolytic degradation tests of these systems were performed. The release profile of PCANs from the electrospun nonwoven was determined with the aid of UV-VIS spectroscopy. Approximately 30% of the PCANs were released from the tested electrospun nonwoven during the initial 15-20 days of incubation. The chemical structure of water-soluble oligomers that were formed after the hydrolytic degradation of the developed delivery system was identified through electrospray ionization mass spectrometry. Oligomers of lactic acid and OLAGA oligocopolyester, as well as oligo-3-hydroxybutyrate terminated with hydroxyl and carboxyl end groups, were recognized as degradation products released into the water during the incubation time. It was also demonstrated that variations in the degradation rate of individual mat components influenced the degradation pattern and the number of formed oligomers. The obtained results suggest that the incorporation of proanthocyanidins into the system slowed down the hydrolytic degradation process of the poly(L-lactide-co-glycolide)/poly[(R,S)-3-hydroxybutyrate] three-dimensional fibre matrix. In addition, in vitro cytotoxicity and antimicrobial studies advocate the use of PCANs for biomedical applications with promising antimicrobial activity.

Investigating the Anticancer Potential of Zinc and Magnesium Alloys: From Base Materials to Nanocoated Titanium Implants.

In this work, we show the in vitro anticancer potential of surgical wires, obtained from zinc (ZnMg0.004) or magnesium (MgCa0.7) alloys by spatial technology comprising casting, extrusion, and final drawing processes. We also present the selective anticancer effects of applied soluble multilayer nanocoatings of zinc and magnesium onto titanium surfaces using the pulse laser deposition method. In the latter, the titanium samples were produced via 3D printing using the selective laser melting method and coated with various combinations of zinc and magnesium layers. For cytotoxicity studies, human dental pulp-derived stem cells (hDPSCs) and human osteosarcoma SaOS-2 cell line were used as representatives of healthy and cancer cells. Cells were examined against the 0.3-3.0 cm2/mL material extract ratios obtained from experimental and steel surgical wires, the latter being the current clinical industry standard. The MgCa0.7 alloy wires were approx. 1.5 times more toxic to cancer cells at all examined extract ratios vs. the extracts from steel surgical wires that exhibited comparable toxicity towards healthy and cancer cells. The ZnMg0.004 alloy wires displayed increased toxicity towards cancer cells with decreasing extract ratios. This was also reflected in the increased anticancer effectiveness, calculated based on the viability ratio of healthy cells to cancer cells, from 1.1 to 4.0 times. Healthy cell viability remained at 80-100%, whereas cancer cell survival fluctuated at 20-75%, depending on the extract ratio. Furthermore, the culture of normal or cancer cells on the surface of Zn/Mg-coated titanium allowed us to select combinations of specific coating layers that yielded a comparable anticancer effectiveness to that observed with the experimental wires that ranged between 2 and 3. Overall, this work not only demonstrates the substantial anticancer properties of the studied wires but also indicates that similar anticancer effects can be replicated with appropriate nanocoatings on titanium samples. We believe that this work lays the groundwork for the future potential development of the category of new implants endowed with anticancer properties.

Analysis of biologically-derived small particles--searching for geometry correction factors using Monte Carlo simulation.

A Monte Carlo simulation was used to determine geometry correction factors that increase accuracy of quantitative X-ray microanalysis of laterally semithick biological materials. A model composed of cellulose with homogeneously distributed biological elements and lateral dimensions between 0.5-25 µm was chosen. The specimen was exposed to 5, 10, and 15 keV electrons, the net intensities of characteristic X-rays registered for the elements, and presented as a function of the lateral dimensions of the model. This showed the double decay exponential function fitted the distribution of X-ray intensities in relation to the model size. The applicability of the function as a correction method was successfully tested for 30 specimens with varying composition and dimensions. The value of relative error decreased from ±60% to ±5% when the correction was applied. Moreover, the minimal lateral size of the material was defined, below which the correction is not required. The simulation also revealed that the difference of the weighted sum of Z²/A between the unknown and the standard could reach 25% without significant influence on the quantitative results. The correction method could be helpful for accurate assessment of elemental composition in biological or organic matrices, when their lateral dimensions are smaller than the distribution range.

Gellan gum hydrogels cross-linked with carbodiimide stimulates vacuolation of human tooth-derived stem cells in vitro.

The natural polysaccharides are promising compounds for applications in regenerative medicine. Gellan gum (GG) is the bacteria-derived polysaccharide widely used in food industry. Simple modifications of its chemical properties make GG superior for the development of biocompatible hydrogels. Beside reversible cationic integration of GG chains, more efficient binding is accomplished with 1-ethyl-3-[3-(dimethylamino)propyl]carbodiimide (EDC). However, the side-products of polymer cross-linking might affect viability and differentiation of stem cells introduced into the hydrogels. We found that O-acylisourea (EDU) stimulates autophagy-based vacuolation in both periodontal ligament and dental pulp stem cells. 24-h treatment of cells with GG extracts cross-linked with 15 mM EDC developed large cytoplasmic vacuoles. Freshly prepared EDU (2-6 mM) but not 15 mM EDC solutions initiated vacuole development with concomitant reduction of cell viability/metabolism. Most of the vacuoles stained with acridine orange displayed highly acidic environment further confirmed by flow cytometric analysis. Western blot of the LC3 autophagy marker followed by a transmission electron microscopy indicated the process is autophagy-dependent. We propose that the high reactivity of EDU with intracellular components initiates autophagy, although the targets of EDU remain unknown. Nevertheless, a burst release of EDU from GG hydrogels might modulate negatively cellular processes and final effectiveness of tissue regeneration.

Incorporation of Ca ions into anodic oxide coatings on the Ti-13Nb-13Zr alloy by plasma electrolytic oxidation.

The present work concerns the surface modification of The Ti-13Nb-13Zr alloy by electropolishing and plasma electrolytic oxidation (PEO) process in Ca-containing electrolytes: calcium formate and calcium lactate solutions (0.1-1.0 mol dm-3) under voltages of 200 and 400 V. As a result of the PEO process, a porous oxide layer containing incorporated calcium compounds was formed on the Ti-13Nb-13Zr alloy surface. The morphology and chemical composition of the modified Ti-13Nb-13Zr alloy were investigated using scanning electron microscopy (SEM + EDS), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). An increase in the applied voltage caused an increase in the number of pores and an increase in the amount of calcium incorporated in the oxide layer. Analysis showed that all samples were covered by titanium oxide, which was present in the form of anatase and/or rutile. In course of the experiments, it was showed that the proposed procedure has a positive effect on the overall bioactivity of the Ti-13Nb-13Zr alloy. Bioactivity investigations using simulated body fluid (SBF) confirmed the formation of apatite on the anodized surfaces. The cell adhesion results obtained by the use of human bone marrow mesenchymal stem cells (hBMSC) demonstrated that the PEO coatings on the Ti-13Nb-13Zr alloy remarkably enhanced the cytocompatibility of the substrate, indicating a potential application in orthopedic surgeries. The incorporation of Ca into the oxide layer proceeded to a higher extent when the PEO treatment was performed in the calcium lactate bath. The oxide layers formed in the calcium lactate solution exhibited also superior biological behavior towards hBMSC. This can be ascribed to the presence of carboxylic groups onto coatings' surface (as identified by XPS), which facilitated the anchoring of cells and tissues.

In vitro bioactivity investigations of Ti-15Mo alloy after electrochemical surface modification.

Titanium and its aluminum and vanadium-free alloys have especially great potential for medical applications. Electrochemical surface modification improves their surface bioactivity and stimulates osseointegration process. In this work, the effect of plasma electrolytic oxidation of the ß-type alloy Ti-15Mo surface on its bioactivity is presented. Bioactivity of the modified alloy was investigated by immersion in simulated body fluid (SBF). Biocompatibility of the modified alloys were tested using human bone marrow stromal cells (hBMSC) and wild intestinal strains (DV/A, DV/B, DV/I/1) of Desulfovibrio desulfuricans bacteria. The particles of apatite were formed on the anodized samples. Human BMSC cells adhered well on all the examined surfaces and expressed ALP, collagen, and produced mineralized matrix as determined after 10 and 21 days of culture. When the samples were inoculated with D. desulfuricans bacteria, only single bacteria were visible on selected samples. There were no obvious changes in surface morphology among samples. Colonization and bacterial biofilm formation was observed on as-ground sample. In conclusion, the surface modification improved the Ti-15Mo alloy bioactivity and biocompatibility and protected surface against colonization of the bacteria. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 903-913, 2016.

Bioactivity of coatings formed on Ti-13Nb-13Zr alloy using plasma electrolytic oxidation.

In this work, we investigated the bioactivity of anodic oxide coatings on Ti-13Nb-13Zr alloy by plasma electrolytic oxidation (PEO) in solutions containing Ca and P. The bioactive properties of the films were determined by immersion in simulated body fluid (SBF), and their biocompatibility was examined using adult human bone marrow derived mesenchymal stem cells (hBMSCs). The oxide layers were characterised based on their surface morphology (SEM, AFM, profilometry) as well as on their chemical and phase compositions (EDX, XRF, XRD, XPS). We report that anodic oxidation of Ti-13Nb-13Zr led to the development of relatively thick anodic oxide films that were enriched in Ca and P in the form of phosphate compounds. Furthermore, the treatment generated rough surfaces with a significant amount of open pores. The surfaces were essentially amorphous, with small amounts of crystalline phases (anatase and rutile) being observed, depending on the PEO process parameters. SBF soaking led to the precipitation of small crystals after one week of experiment. During culturing of hBMSCs on the bioactive Ti-13Nb-13Zr surfaces the differentiation of human mesenchymal stem cells toward osteoblasts was promoted, which indicated a potential of the modified materials to improve implant osseointegration.

Degradation, bioactivity, and osteogenic potential of composites made of PLGA and two different sol-gel bioactive glasses.

We have developed poly(L: -lactide-co-glycolide) (PLGA) based composites using sol-gel derived bioactive glasses (S-BG), previously described by our group, as composite components. Two different composite types were manufactured that contained either S2-high content silica S-BG, or A2-high content lime S-BG. The composites were evaluated in the form of sheets and 3D scaffolds. Sheets containing 12, 21, and 33 vol.% of each bioactive glass were characterized for mechanical properties, wettability, hydrolytic degradation, and surface bioactivity. Sheets containing A2 S-BG rapidly formed a hydroxyapatite surface layer after incubation in simulated body fluid. The incorporation of either S-BG increased the tensile strength and Young's modulus of the composites and tailored their degradation rates compared to starting compounds. Sheets and 3D scaffolds were evaluated for their ability to support growth of human bone marrow cells (BMC) and MG-63 cells, respectively. Cells were grown in non-differentiating, osteogenic or osteoclast-inducing conditions. Osteogenesis was induced with either recombinant human BMP-2 or dexamethasone, and osteoclast formation with M-CSF. BMC viability was lower at higher S-BG content, though specific ALP/cell was significantly higher on PLGA/A2-33 composites. Composites containing S2 S-BG enhanced calcification of extracellular matrix by BMC, whereas incorporation of A2 S-BG in the composites promoted osteoclast formation from BMC. MG-63 osteoblast-like cells seeded in porous scaffolds containing S2 maintained viability and secreted collagen and calcium throughout the scaffolds. Overall, the presented data show functional versatility of the composites studied and indicate their potential to design a wide variety of implant materials differing in physico-chemical properties and biological applications. We propose these sol-gel derived bioactive glass-PLGA composites may prove excellent potential orthopedic and dental biomaterials supporting bone formation and remodeling.