Effect of Diamond Bur Grit Size on Composite Repair.

PURPOSE: This study investigated the effect of diamond bur grit size on the repair bond strength of fresh and aged resin composites. MATERIALS AND METHODS: Blocks of microhybrid composite (Opallis, FGM) were stored in distilled water at 37°C for 24 h (fresh composite) or subjected to 5000 thermal cycles (aged composite). The surfaces were roughened using diamond-coated, flame-shaped carbide burs with medium grit (#3168), fine grit (#3168F), or extra-fine grit (#3168FF). The control group underwent no surface treatment. Surface roughness, water contact angle, and surface topography by scanning electron microscopy (SEM) were evaluated (n = 3). Samples were restored with resin composite and sectioned into beam-shaped specimens, which were subjected to microtensile bond testing. Failure modes were classified using a stereomicroscope. Data were statistically analyzed using the Student- Newman-Keuls test and two-way ANOVA, with significance set at p < 0.05. RESULTS: Higher surface roughness was observed for groups treated with the medium- and fine-grit burs; aged composites were rougher than fresh composites. The water contact angle formed on the aged composite was lower than that on the fresh composite. The highest repair bond strength was observed for the fine-grit bur group, and the lowest was recorded for control. Interfacial failures were more predominant. SEM images showed that the surfaces treated with fine- and extra-fine-grit burs had a more irregular topography. CONCLUSION: Surface roughening of fresh or aged resin composites with diamond burs improved retention of the repair material. Fine-grit burs generally performed better than medium- and extra-fine-grit burs.

Comparative evaluation of dental resin composites based on micron- and submicron-sized monomodal glass filler particles.

OBJECTIVES: A model resin composite containing a novel monomodal inorganic filler system based on submicron-sized Ba-Si-Al glass particles (NanoFine NF180; Schott) was formulated and compared with an experimental composite containing micron-sized particles (UltraFine UF1.0; Schott). METHODS: The filler particles were characterized using X-ray microanalysis and granulometry, while the composites were characterized in terms of filler-resin morphology, radiopacity, degree of CC conversion, hardness, flexural strength/modulus, work-of-fracture, surface roughness and gloss (before and after simulated toothbrushing abrasion), and bulk compressive creep. The composites were formulated from the same photoactivated dimethacrylate co-monomer, incorporating mass fractions of 75% micron- and 78% submicron-sized particles. Quantitative data were analyzed at a significance level of p<0.05. RESULTS: Both filler systems exhibited a narrow grain size range (175±30 and 1000±200 nm), with differences restricted to the size and specific area of the particles. The composites were similar in radiopacity, flexural strength, work-of-fracture, and creep. The submicron composite was harder but had lower flexural modulus and CC conversion. No significant differences in roughness were observed before brushing, although the submicron composite had higher gloss. Brushing increased roughness and decreased gloss on both materials, but the submicron composite retained higher gloss after brushing. SIGNIFICANCE: The monomodal submicron glass filler system demonstrated potential for use in restorative dental composites, particularly due to improved esthetic properties.

1,3-Diethyl-2-thiobarbituric acid as an alternative coinitiator for acidic photopolymerizable dental materials.

The ethyl-4-dimethylaminobenzoate (EDAB) is widely used as a coinitiator of the camphorquinone (CQ), but in acidic circumstances it might present some instability, reducing the polymerization efficiency of the material. Considering this, new coinitiators are being evaluated. Hence, this study evaluated the kinetic of polymerization (KP), the degree of conversion (DC), and the rate of polymerization (RP ) of experimental resin adhesives containing 1,3-diethyl-2-thiobarbituric acid (TBA) as a coinitiator of the CQ. The experimental monomeric blend was prepared with bisphenol A glycidyl dimethacrylate, 2-hydroxyethyl methacrylate, and acidic monomers. CQ was added at 1 mol % as photoinitiator. Six groups were formulated: four containing concentrations of 0.1, 0.5, 1, and 2 mol % of TBA, one without coinitiator, and the last one containing 1 mol % of EDAB (control group). The KP and the RP were performed using real-time Fourier Transform infrared spectroscopy. The group without coinitiator has not formed a polymer, whereas the addition of TBA resulted in the conversion of monomers in polymer. The DC of the adhesives was as higher as the increase in the TBA content. The group with 2 mol % of TBA presented improved DC and reactivity (RP ) than the other groups and the control one. Hence, the TBA has performed as a coinitiator of the CQ for the radical polymerization of methacrylate resin adhesives and it has improved the DC and the reactivity of the materials. Thus, it is a potential coinitiator for the photopolymerization of dental materials.