Determination of Polyetheretherketone (PEEK) mechanical properties as a denture material.

PURPOSE: To optimize the gypsum mold temperatures for pressed PEEK, and to estimate the impact, tensile strength and flexural properties of pressed and milled PEEK. Where appropriate, these properties were compared with those of PMMA. MATERIALS AND METHODS: Since the mold temperature could affect the properties of the injected parts, the temperature of 20 gypsum specimens was monitored using the multi-thermocouple system (n = 5). A total of 210 specimens were prepared for mechanical tests according to the ISO standard for denture base polymer (n = 10). The Izod impact, tensile strength, and flexural behavior were assessed. PEEK-OptimaNI1 (PEEK-pressed) was tested after processing via the pressing method at4 different mold temperatures. Machining PEEK-Juvora (PEEK-milled) specimens were prepared using the CAD-CAM production method. Data were analyzed via one-way ANOVA performed at a confidence level of 95% and a significant P-value of (P ≤ 0.05). RESULTS: In comparison to the furnace temperature more heat was required to preheat the gypsum mold up to 100, 150, 175 and 200 °C for pressing purposes. The highest impact strength was 5.7 kJ/m2 for PEEK-pressed at 100 °C mold temperature and 4 kJ/m2 for PEEK-milled. The latter had a higher tensile strength of 118 MPa. The best result for PEEK-pressed was 97 MPa at 200 °C mold temperature. Under a 4-point bending test, Young's modulus of PEEK-milled was 5591 MPa, while the highest for PEEK-pressed was 4936 MPa at 200 °C mold temperature. CONCLUSIONS: Compared to PMMA, given the superior mechanical properties of PEEK, it may become the material of choice for future use. Dentures constructed from PEEK polymer could well be routinely constructed in the near future.

Spectral reflectance and color of dentin ceramics for all-ceramic restorations.

OBJECTIVE: The study was conducted to observe the spectral reflectance curves, and evaluate the color coordinates (CIELAB) of VM7 dentin ceramics (VITA, Germany) across the whole 3D-MASTER shade system. METHODS: Three disc samples, 13 mm in diameter and 1.4mm in thickness, were produced for each shade by firing following the manufacturer's instructions. Each fired disc was ground to a thickness of 1.0 mm and both faces were polished. Spectral reflectance data in the visible spectrum under the standard illuminant D65 were collected at 1 nm intervals by using a computer-controlled spectrophotometer. Color coordinates, L*, a*, b*, C*, h, in the three-dimensional CIELAB color space were obtained. RESULTS: (1) Spectral reflectance in the short-wavelength range systematically decreased with increasing chroma number (M1, M2, and M3) when compared within the same value (lightness) group (1M, 2M, 3M, 4M, and 5M). (2) Spectral reflectance decreased systematically across the whole visible spectrum with increasing value group when compared within the same chroma group. (3) A negative relationship was recognized between lightness (L*) and chromaticity index a* (red-green direction). That is, a* coordinate increases from approximately 1 for the 1M1 sample to approximately 13 for the 5M3 sample, the corresponding lightness systematically decreased from 87 to 69. (4) With increasing a* coordinate, hue angle (h) significantly decreased from 85 degrees for the 1M1 sample to 69 degrees for the 5M3 sample. (5) Lightness apparently increased with increasing hue angle (h) throughout the whole range of the 3D-MASTER shade system. (6) A strong positive relationship between chroma (C*) and chromaticity index b* (yellow-blue direction) was found, demonstrating that the chroma of the present ceramic is mainly controlled by the b* coordinate. SIGNIFICANCE: Systematic variations in spectral reflectance and color coordinates of VM7 dentin were observed throughout the 3D-MASTER shade system and were suggested to be caused by the fine structure of the sample which can interfere with shorter wavelengths in the visible spectrum.

The effects of different opacifiers on the translucency of experimental dental composite resins.

OBJECTIVE: The aim of this study was to evaluate the effects of different opacifiers on the translucency of experimental dental composite-resins. METHODS: Three metal oxides that are used as opacifiers were tested in this study: titanium oxide (TiO2), aluminium oxide (Al2O3) and zirconium oxide (ZrO2). Experimental composite-resins were fabricated containing 25wt.% urethane dimethacrylate (UDMA)-based resin matrix and 75% total filler including different concentrations of metal oxides (0, 0.25, 0.5, 0.75 and 1wt.%) blended into silane treated barium-silicate filler. The specimens (15.5mm diameter and 1mm thickness) were light-cured and tested in the transmittance mode using a UV/VIS spectrophotometer at wavelengths from 380 to 700nm under a standard illuminant D65. The color differences (ΔE* ab) between different concentrations of opacifiers were also measured in transmittance mode based on their Lab values. RESULTS: Statistical analysis by ANOVA and Tukey's test showed a significant decrease (p<0.05) in light transmittance with the addition of opacifiers to the experimental composite-resins. There was a linear correlation between different concentrations of TiO2 and Al2O3 and total transmittance. Total transmittance was also found to be wavelength dependent. The color differences for the concentrations of 0-1wt.% of the opacifiers were above 1 ΔE* unit, with Al2O3 showing the smallest color shift. SIGNIFICANCE: The type and the amount of the opacifiers used in this study had a significant effect on the translucency of the experimental UDMA-based dental composite resins. The most effective opacifier was TiO2, followed by ZrO2 and Al2O3 in decreasing order, respectively.

Relationship between Color and Translucency of Multishaded Dental Composite Resins.

The aim of the present study was to compare the translucency of different shades of two highly aesthetic multilayered restorative composite resins. In total nine shades from Esthet.X and ten shades from Filtek Supreme composite resins were chosen. Discs of each shade were prepared (N = 3) and light-cured. Total and diffuse transmittance values for each sample were measured. Statistical analysis showed that the opaque dentine shades of both composites were the least translucent and the enamel shades had the highest translucency. There was a significant decrease in translucency from A2 to C2 of regular body shades and also from A4 to C4 of opaque dentine shades of Esthet.X composite resin. Grey enamel shade had a significantly higher diffuse translucency compared to clear and yellow enamel shades. There was a significant decrease in translucency from A2B to D2B and also in diffuse translucency from A4D to C6D shades of Filtek Supreme composite resin. It can be concluded that the color of the composite resins tested in this study had a significant effect on their translucency. Information on the translucency of different shades of composite resins can be very useful for the clinicians in achieving optimal esthetic restorative outcome.

Optical properties of base dentin ceramics for all-ceramic restorations.

OBJECTIVES: The study was conducted to compare the optical parameters of VM7(®) M-shade base dentin ceramics (VITA, Germany) for all ceramic restorations to the chemical composition across the 3D-MASTER(®) shade system. METHODS: Three disc samples, 13 mm diameter and 1.4 mm thickness, were produced for each M-shade following the manufacturer's instructions. Each disc was ground and polished to a thickness of 1.0 mm. Spectral light transmittance and reflectance data were recorded in the visible spectrum under the standard illuminant D65 and 2° observer at 10 nm intervals by using a computer-controlled spectrophotometer. Opacity, translucency and opalescence parameters were determined for each sample. RESULTS: (1) Spectral transmittance and reflectance in the short-wavelength range systematically decreased with increasing chroma number (M1, M2, M3) when compared within the same value (lightness) group. (2) Spectral transmittance and reflectance decreased systematically across the whole visible spectrum with increasing value group number when compared within the same chroma group. (3) Analysis of relationship between chemical composition and various optical parameters for all the samples showed the significant contribution of ZrO2 and Y2O3 substances to optical properties of the present material. SIGNIFICANCE: Systematic variations in optical properties of VM7(®) M-shade base dentin ceramics were observed throughout the 3D-MASTER(®) shade system and were suggested to be caused by the fine structure of the sample which can interfere with shorter wavelengths in the visible spectrum.

Effect of resin matrix composition on the translucency of experimental dental composite resins.

OBJECTIVES: The purpose of this study was to investigate the effect of the resin matrix composition on the translucency of experimental dental composite resins. METHODS: Three types of unfilled resin matrices (TEGDMA-, UDMA- and BisGMA-based) were formulated and light cured. In addition, six different experimental dental composite resins with constant filler loading but varying in the type of monomer and the content of BisGMA were fabricated. Discs of each test material with 15.5mm diameter and 1.0mm thickness were prepared (N=3) and light cured. Total and diffuse transmittance values for each sample were measured using a UV/VIS spectrophotometer with the range of readings from 380 to 700nm. Difference in color was measured using the CIE Lab system. RESULTS: Statistical analysis by one-way ANOVA followed by Tukey's test showed that there was no statistically significant difference in transmittance values between the three unfilled resins. However, with the addition of filler, BisGMA-containing composite resins showed significantly higher transmittance values than the UDMA- and TEGDMA-based composite resins. Regression analysis revealed that there was a linear correlation between the percentage of BisGMA in the resin matrix and the total and diffuse translucency. SIGNIFICANCE: The amount of BisGMA used in the resin matrix has a significant effect on the translucency of silica filler-containing dental composite resins.