Effect of zirconia surface modification using dopamine polymerisation on the shear bond strength of resin cement.

This study evaluated the influence of polydopamine treatment on the surface properties and bond strength of yttria-stabilised tetragonal zirconia polycrystal (Y-TZP). Sixty-three zirconia blocks (10 × 10 × 2 mm) were randomly divided into three groups defined by surface treatment: (i) control group (C), (ii) grit-blasted with 110 µm alumina particles (GB), and (iii) polydopamine (PDA) coating. The surfaces of specimens subjected to different treatments were investigated by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and water contact angle measurements. After the surface treatments, the specimens were cemented to resin composite cylinders. After bonding, the shear bond strength of the ceramic to the resin was measured, and the failure mode of each specimen was analysed using a stereomicroscope. The results indicated that the shear bond strength is highest for the GB treatment and lowest for the controls. However, the difference between groups GB and PDA was not statistically significant. In the control group, adhesive failure was predominant, whereas in the treatment groups, mixed mode failure was predominant. The pre-treatment of Y-TZP ceramic with the polydopamine coating might improve the bond strength of the resin cement to the zirconia ceramic.

[Effect of sintering temperature on mechanical properties of dental zirconia toughened alumina ceramics].

PURPOSE: To investigate the effect of sintering temperature on mechanical properties of dental zirconia toughened alumina (ZTA) ceramics prepared by gel-casting technique. METHODS: The samples prepared by gel-casting were sintered at 1100, 1200, 1250, 1300 and 1400degrees centigrade for each group. The flexural strength, fracture toughness, Vickers hardness and brittleness index were obtained and microscopic morphology of each group was observed under scanning electron microscope (SEM). The data were statistically analyzed using SPSS 19.0 software package. RESULTS: The flexural strength, fracture toughness and Vickers hardness increased with the increasing sintering temperature during 1100~1400degrees centigrade. The lowest brittleness index (0.74±0.16) µm-1/2 was observed in group sintered at 1200degrees centigrade and the highest (2.76±0.14) µm-1/2 was at 1400degrees centigrade (P<0.05), while the flexural strength of these two groups was (46.89±3.24) MPa and (349.64±54.72) MPa, respectively. CONCLUSIONS: The ZTA dental ceramics exhibit good machinability with proper sintering temperature (1200degrees centigrade) and the strength meets the requirement of clinical application.