Effect of Er,Cr:YSGG laser treatment on microshear bond strength of zirconia to resin cement before and after sintering.

PURPOSE: To evaluate the effect of Er,Cr:YSGG laser treatment on microshear bond strength of zirconia to resin cement before and after sintering. MATERIALS AND METHODS: Ninety pre-sintered yttrium-stabilized tetragonal zirconia specimens (4 × 3 × 2 mm) were divided into 6 groups (n = 15). In group C, sintered zirconia was not treated (control group). In groups AS2 and AS3, sintered zirconia blocks were irradiated by Er,Cr:YSGG using a power of 2 and 3 W, respectively. Groups PS2 and PS3 consisted of pre-sintered blocks conditioned by Er,Cr:YSGG at 2 and 3 W, respectively. In group AA, sintered zirconia was air abraded with 50-µm alumina powder. One block was made using the same preparations as mentioned above and was morphologically assessed by SEM. Microcylinders of Panavia F 2.0 were placed on the treated surface of the groups. Samples were incubated at 37°C and 98% humidity for 48 h and then subjected to microshear bond strength testing. The mode of failure was evaluated. Data were analyzed by one-way ANOVA and Tukey's HSD test (p < 0.05). RESULTS: There was a statistically significant difference between group AA and the others (p < 0.0001). A significant difference was also noted between groups AS3 and C (p = 0.031). Complete surface roughness was seen in group AA and the bond failure was mostly cohesive, while in laser-treated groups, the surfaces roughness was much lower vs other groups, and the mode of failure was mostly adhesive. CONCLUSION: Laser treatment of pre-sintered Y-TZP cannot be recommended for improving the bond. Although sandblasting of sintered Y-TZP yielded better results than the rest of the groups, 3 W power after sintering can also be effective in enhancing the bonding strength of resin cement to zirconia.

Antibacterial Activity of Diode Laser and Sodium Hypochlorite in Enterococcus Faecalis-Contaminated Root Canals.

INTRODUCTION: The aim of the present in vitro study was to evaluate the disinfection ability of 980-nm diode laser in comparison with sodium hypochlorite (NaOCl) as a common root canal irrigant in canals infected with Enterococcus faecalis (E. faecalis). METHODS AND MATERIALS: The root canals of 18 extracted single-rooted premolars were prepared by rotary system. After decoronation, the roots were autoclaved. One specimen was chosen for the negative control, and the remaining teeth were incubated with E. faecalis suspension for two weeks. Subsequently, one specimen was selected as the positive control and the remaining samples were divided into two groups (n=8). The samples of the first group were irrigated with 5.25% NaOCl and the second group were treated with a 980-nm diode laser. Microbial samples were taken from the root canals and bacterial cultivation was carried out. The average value and the standard deviation of colony-forming units (CFU) of each specimen were measured using descriptive statistics. The student's t-test was used to compare the reduction in CFU in each group. The equality of variance of CFU was measured by the Levene's test. RESULTS: NaOCl resulted in 99.87% removal of the bacteria and showed significantly more antibacterial effect compared to the 980-nm diode laser which led to 96.56% bacterial reduction (P<0.05). CONCLUSION: Although 5.25% NaOCl seems to reduce E. faecalis more effectively, the diode laser also reduced the bacterial count. Therefore a 980-nm diode laser could be considered as a complementary disinfection method in root canal treatment.