Análise perfilométrica de materiais restauradores submetidos a clareamento / Profilometric analysis od restorative materials submetted to bleaching
Rev. odontol. UNESP
; 35(2): 199-203, abr.-jun. 2006. ilus, tab
Article
en Pt
| LILACS, BBO
| ID: lil-512568
Biblioteca responsable:
BR39.2
RESUMO
Este estudo avaliou o efeito do peróxido de carbamida a 10% na rugosidade desuperfície de amálgama, compômero, ionômero de vidro e resina composta. Para os grupos controle(sem clareamento) e experimental (com clareamento), cinco espécimes de cada material forampreparados. Os espécimes experimentais foram expostos ao agente clareador por 8 horas diárias,por 4 semanas. Durante as 18 horas remanescentes, eram mantidos em solução salina. Os espécimescontrole foram mantidos em solução salina durante todo o experimento. A rugosidade de superfíciefoi analisada com um perfilômetro 3D. A análise qualitativa das imagens foi realizada, e a análisequantitativa avaliou o sPa , o sPv e o sPsk. Os resultados foram analisados estatisticamente peloteste de Tukey (α = 0,05). Para o amálgama, diferença significante foi encontrada para o sPv,enquanto para o sPa e o sPsk não houve diferença significante. Para o cimento ionômero de vidro,diferença significante foi constatada para os parâmetros sPa e sPv. Para a resina composta e ocompômero, não foi verificada diferença significante. Concluiu-se que o peróxido de carbamida10% pode alterar a rugosidade de superfície do ionômero de vidro e do amálgama.
ABSTRACT
This study examined the effect of 10% carbamide peroxide bleaching agents onthe surface roughness of amalgam, compomer, glass ionomer cement and composite resins. Forthe control (no bleaching) and experimental (bleaching treatment) groups, 5 specimens of eachmaterial were prepared. The experimental specimens were exposed to the bleaching agent for8 hours a day for 4 weeks. During the remaining time (18 h), they were stored in saline solution. Thecontrol specimens remained immersed in saline solution throughout the experiment. The surfaceroughness was analyzed with a 3D profilometer. Qualitative analysis of images was carried out,and quantitative analysis was made with sPa, o sPv, and sPsk. Results were statistically analyzedby Tukeys test (α = 0.05), and revealed for amalgam significant difference for sPv, in contrast tosPa and sPsK. Glass ionomer cement presented a significant difference for sPa and sPv. Compositeresin and compomer presented no significant difference. It was concluded that 10% carbamideperoxide can alter the surface roughness of glass ionomer cement and amalgam.
Texto completo:
1
Banco de datos:
BBO
/
LILACS
Asunto principal:
Peróxidos
/
Blanqueamiento de Dientes
/
Materiales Dentales
/
Estética Dental
Tipo de estudio:
Qualitative_research
Idioma:
Pt
Revista:
Rev. odontol. UNESP
Asunto de la revista:
ODONTOLOGIA
Año:
2006
Tipo del documento:
Article
País de afiliación:
Brasil