Cytotoxicity and genotoxicity of calcium silicate-based cements on an osteoblast lineage
Gomes-Cornélio, Ana Lívia; Rodrigues, Elisandra Márcia; Mestieri, Leticia Boldrin; Falcoski, Thaís de Oliveira Rodrigues Sanzovo; Soares, Christiane Pienna; Guerreiro-Tanomaru, Juliane Maria; Rossa Junior, Carlos; Tanomaru Filho, Mário.
Braz. oral res. (Online)
; 30(1): e48, 2016. tab, graf
Artigo
em Inglês
| LILACS | ID: biblio-952020
Abstract Several calcium silicate-based biomaterials have been developed in recent years, in addition to Mineral Trioxide Aggregate (MTA). The aim of this study was to evaluate the cytotoxicity, genotoxicity and apoptosis/necrosis in human osteoblast cells (SAOS-2) of pure calcium silicate-based cements (CSC) and modified formulations modified calcium silicate-based cements (CSCM) and three resin-based calcium silicate cements (CSCR1) (CSCR 2) (CSCR3). The following tests were performed after 24 hours of cement extract exposure methyl-thiazolyl tetrazolium (MTT), apoptosis/necrosis assay and comet assay. The negative control (CT-) was performed with untreated cells, and the positive control (CT+) used hydrogen peroxide. The data for MTT and apoptosis were submitted to analysis of variance and Bonferroni's posttest (p < 0.05), and the data for the comet assay analysis, to the Kruskal-Wallis and Dunn tests (p < 0.05). The MTT test showed no significant difference among the materials in 2 mg/mL and 10 mg/mL concentrations. CSCR3 showed lower cell viability at 10 mg/mL. Only CSC showed lower cell viability at 50 mg/mL. CSCR1, CSCR2 and CSCR3 showed a higher percentage of initial apoptosis than the control in the apoptosis test, after 24 hours exposure. The same cements showed no genotoxicity in the concentration of 2 mg/mL, with the comet assay. CSC and CSCR2 were also not genotoxic at 10 mg/mL. All experimental materials showed viability with MTT. CSC and CSCR2 presented a better response to apoptosis and genotoxicity evaluation in the 10 mg/mL concentration, and demonstrated a considerable potential for use as reparative materials.
Assuntos
Humanos Osteoblastos/efeitos dos fármacos Silicatos/toxicidade Compostos de Cálcio/toxicidade Cimentos Dentários/toxicidade Óxidos/toxicidade Sais de Tetrazólio Materiais Biocompatíveis/toxicidade Teste de Materiais Sobrevivência Celular/efeitos dos fármacos Células Cultivadas Reprodutibilidade dos Testes Análise de Variância Apoptose/efeitos dos fármacos Compostos de Alumínio/toxicidade Ensaio Cometa Proliferação de Células/efeitos dos fármacos Combinação de Medicamentos Formazans Necrose/induzido quimicamente
Biblioteca responsável:
BR1.1
powered by iAHx-2.18-86
BVS Odontologia