Resistência ao Cisalhamento de Braquetes Colados com Dois Tipos de Agentes de União e Expostos à Ação de Bebidas Ácidas / Shear Bond Strength of Orthodontic Brackets Bond with Two Types of Bonding Agents and Exposed to Acidic Beverages
Rev. bras. ciênc. saúde
; 21(4): 291-298, 2017. ilus, tab
Article
em Pt
| LILACS
| ID: biblio-998106
Biblioteca responsável:
BR8.1
Localização: BR8.1; v.21, n.4
RESUMO
Objetivos:
Avaliar a influência de bebidas ácidas na resistência de união de braquetes ortodônticos colados com os agentes resinosos Transbond™ PLUS Color Change (TPCC) e Ortholink™ e quantificar o Índice de Remanescente Adesivo (IRA) após a descolagem do braquete, a fim de constatar qual compósito apresenta maior resistência à tensão cisalhante e o local onde ocorreu a falha adesiva, respectivamente.Materiais e Métodos:
Noventa e seis incisivos bovinos tiveram braquetes colados em sua superfície vestibular e foram divididos em dois grupos (n=48), de acordo com o agente de união utilizado I) TPCC e II)Ortholink. Em seguida, cada grupo foi separado em quatro subgrupos (n=12), de acordo com a substância na qual as amostras seriam imersas S1) Coca-cola®, S2) Suco de laranja Del Valle®, S3) Gatorade® e S4) saliva artificial (controle). As amostras dos subgrupos S1, S2 e S3 foram submetidas a três ciclos corrosivos diários de 5 minutos, com intervalos de 2 horas, durante 30 dias, sendo sempre recolocadas em saliva artificial até que um novo ciclo fosse iniciado. Ao fim deste período, foram submetidas ao ensaio mecânico de cisalhamento e à avaliação do IRA.Resultados:
Não foram encontradas diferenças estatisticamente significantes para as resinas entre si e entre os subgrupos, nos dois parâmetros testados (p>0,05).Conclusão:
Não houve influência das substâncias ácidas testadas sobre a força de adesão dos compósitos utilizados, possuindo ambos resistências semelhantes, e que tanto a interface resina/ braquete quanto braquete/dente apresentaram falhas adesivas. (AU)ABSTRACT
Objective:
To evaluate the influence of acidic beverageson the bond strength of orthodontic brackets bonded with the resinous agents Transbond ™ PLUS Color Change (TPCC) and Ortholink ™.The Adhesive Remnant Index (ARI) after bracket removal was further quantified, in order to determine which composite has a higher resistance to shear stress and where there was adhesive failure. Material andMethods:
Ninety-six bovine incisors had brackets bonded on their vestibular surfaces and were divided into two groups (n = 48), according to the bonding agent used I) TPCC and II) Ortholink. Then, each group was divided into four subgroups (n = 12) in accordance with the substance inwhich the samples would be immersed S1) Coca-Cola®, S2) Orange juice Del Valle®, S3) Gatorade® and S4) artificial saliva (control). Samples of subgroups S1, S2 and S3 were subjected to three corrosive cycles daily for 5 minutes with 2 hours intervals for 30 days, each being replaced in artificial saliva until a new cycle was started. At the end of this period, sampleswere subjected to mechanical shear test and the ARI assessment.Results:
No statistically significant differences were found betweenthe compositesand between the subgroups for the two parameters tested (P>0.05).Conclusion:
There was no influence of acidic beverageson the bond strength of the composites, asboth showedsimilar resistance, and the resin/bracket interfaces as well asthe bracket/tooth interfaces showed adhesive failures. (AU)Palavras-chave
Texto completo:
1
Base de dados:
LILACS
Assunto principal:
Ortodontia
/
Braquetes Ortodônticos
Limite:
Animals
Idioma:
Pt
Revista:
Rev. bras. ciênc. saúde
Assunto da revista:
MEDICINA
Ano de publicação:
2017
Tipo de documento:
Article
País de afiliação:
Brasil