Influence of the incorporation of triclosan methacrylate on the physical properties and antibacterial activity of resin composite.

ABSTRACT

The incorporation of antimicrobials in the composites as an attempt to reduce bacterial adhesion without jeopardizing mechanical properties is a challenge for Dentistry. OBJECTIVE To evaluate the bacterial adhesion and physical properties of a composite containing the methacrylate triclosan- derivative monomer (TM). METHODOLOGY TM was synthesized and added to an experimental composite. Samples were divided into two groups Control and TM (13.4 wt%). Antibacterial Activity Three specimens of each material were prepared and placed on bacterial suspensions of Streptococcus mutans for 1, 5 and 10 days. After these periods the counting of the colonies (log10) was performed. Assays was performed in triplicate. Physical Properties Three-body Abrasion (TBA) Ten specimens of each material were prepared and stored at 37°C/24 h. The surface roughness (Ra) and hardness (KHN) were analyzed. Next, the specimens were submitted to abrasive wear (30,000 cycles) and re-evaluated for Ra and KHN; Sorption/solubility (SS) cylindrical specimens (n=10) were prepared and weighted. The specimens were immersed in deionized water for 7 days at 37°C and then their weight was verified again. SS were calculated using accepted formulas; Diametral tensile strength (DTS) specimens (n=10) underwent test performed in an Instron universal testing machine at a crosshead speed of 1 mm/min. Data were submitted to appropriate statistical tests according to data distribution and assay (p<0.05). RESULTS Bacterial Adhesion TM showed a significant reduction on biofilm accumulation in the evaluated periods 1 day (1.537±0.146); 5 days (2.183±0.138) and 10 days (4.469±0.155) when compared with Control 1 day (4.954±0.249); 5 days (5.498±0.257) and 10 days (6.306±0.287). Physical Properties For TBA, SS and DTS no significant difference was found between groups Control and TM. The incorporation of methacrylate triclosan-based monomer in the experimental composite reduce bacterial adhesion of S. mutans and did not affect important polymer properties.