RESUMEN
Nitrogen doped lutetium hydride has drawn global attention in the pursuit of room-temperature superconductivity near ambient pressure and temperature. However, variable synthesis techniques and uncertainty surrounding nitrogen concentration have contributed to extensive debate within the scientific community about this material and its properties. We used a solid-state approach to synthesize nitrogen doped lutetium hydride at high pressure and temperature (HPT) and analyzed the residual starting materials to determine its nitrogen content. High temperature oxide melt solution calorimetry determined the formation enthalpy of LuH1.96N0.02 (LHN) from LuH2 and LuN to be -28.4 ± 11.4 kJ/mol. Magnetic measurements indicated diamagnetism which increased with nitrogen content. Ambient pressure conductivity measurements observed metallic behavior from 5 to 350 K, and the constant and parabolic magnetoresistance changed with increasing temperature. High pressure conductivity measurements revealed that LHN does not exhibit superconductivity up to 26.6 GPa. We compressed LHN in a diamond anvil cell to 13.7 GPa and measured the Raman signal at each step, with no evidence of any phase transition. Despite the absence of superconductivity, a color change from blue to purple to red was observed with increasing pressure. Thus, our findings confirm the thermodynamic stability of LHN, do not support superconductivity, and provide insights into the origins of its diamagnetism.
RESUMEN
Neodymium monoxide (NdO) is a metastable rare earth oxide material with a unique electronic structure, which has potential applications across various fields such as semiconductors, energy, catalysis, laser technology, and advanced communications. Despite its promising attributes, the thermodynamic properties of NdO remain unexplored. In this study, high pressure, high temperature phases of neodymium monoxide (NdO, with a rocksalt structure) and body-centered cubic (bcc) Nd metal were synthesized at 5 GPa and 1473 K. X-ray photoelectron spectroscopy (XPS) measurements indicate that the Nd 3d peak shifts to higher energy in NdO relative to Nd2O3, suggesting the possibility of complex electronic states in NdO. Formation enthalpies for the reaction 1/3Nd2O3 + 1/3bcc Nd = NdO obtained from high temperature solution calorimetry in molten sodium molybdate and for the reaction dhcp Nd (metal) = bcc Nd (metal) from differential scanning calorimetry are 25.98 ± 8.65 and 5.2 kJ/mol, respectively. Utilizing these enthalpy values, we calculated the pressure-temperature boundary for the reaction 1/3 bcc Nd + 1/3Nd2O3 = NdO, which has a negative P-T slope of -1.68× 10-4 GPa/K. These insights reveal the high pressure behavior of NdO and neodymium metal, underscoring their potential utility in technological applications.