A Ferrofluid with Surface Modified Nanoparticles for Magnetic Hyperthermia and High ROS Production.

A ferrofluid with 1,2-Benzenediol-coated iron oxide nanoparticles was synthesized and physicochemically analyzed. This colloidal system was prepared following the typical co-precipitation method, and superparamagnetic nanoparticles of 13.5 nm average diameter, 34 emu/g of magnetic saturation, and 285 K of blocking temperature were obtained. Additionally, the zeta potential showed a suitable colloidal stability for cancer therapy assays and the magneto-calorimetric trails determined a high power absorption density. In addition, the oxidative capability of the ferrofluid was corroborated by performing the Fenton reaction with methylene blue (MB) dissolved in water, where the ferrofluid was suitable for producing reactive oxygen species (ROS), and surprisingly a strong degradation of MB was also observed when it was combined with H2O2. The intracellular ROS production was qualitatively corroborated using the HT-29 human cell line, by detecting the fluorescent rise induced in 2,7-dichlorofluorescein diacetate. In other experiments, cell metabolic activity was measured, and no toxicity was observed, even with concentrations of up to 4 mg/mL of magnetic nanoparticles (MNPs). When the cells were treated with magnetic hyperthermia, 80% of cells were dead at 43 °C using 3 mg/mL of MNPs and applying a magnetic field of 530 kHz with 20 kA/m amplitude.

Photocatalytic Degradation of Diclofenac Using Al2O3-Nd2O3 Binary Oxides Prepared by the Sol-Gel Method.

This paper reports the sol-gel synthesis of Al2O3-Nd2O3 (Al-Nd-x; x = 5%, 10%, 15% and 25% of Nd2O3) binary oxides and the photodegradation of diclofenac activated by UV light. Al-Nd-based catalysts were analyzed by N2 physisorption, XRD, TEM, SEM, UV-Vis and PL spectroscopies. The inclusion of Nd2O3 in the aluminum oxide matrix in the 10-25% range reduced the band gap energies from 3.35 eV for the γ-Al2O3 to values as low as 3.13-3.20 eV, which are typical of semiconductor materials absorbing in the UV region. γ-Al2O3 and Al-Nd-x binary oxides reached more than 92.0% of photoconverted diclofenac after 40 min of reaction. However, the photocatalytic activity in the diclofenac degradation using Al-Nd-x with Nd2O3 contents in the range 10-25% was improved with respect to that of γ-Al2O3 at short reaction times. The diclofenac photoconversion using γ-Al2O3 was 63.0% at 10 min of UV light exposure, whereas Al-Nd-15 binary oxide reached 82.0% at this reaction time. The rate constants determined from the kinetic experiments revealed that the highest activities in the aqueous medium were reached with the catalysts with 15% and 25% of Nd2O3, and these compounds presented the lowest band gap energies. The experimental results also demonstrated that Nd2O3 acts as a separator of charges favoring the decrease in the recombination rate of electron-hole pairs.