Effect of nanostructured zirconium dioxide incorporation in an experimental adhesive resin.

OBJECTIVES: The aim of this study was to evaluate the influence of nanostructured zirconium dioxide incorporation in an experimental adhesive resin. METHODS: ZrO2 particles were characterized by X-ray diffraction (XRD), micro-Raman spectroscopy and Brunauer-Emmett-Teller (B.E.T). Experimental adhesive resins were formulated with 0, 0.5, 1, 4.8, and 9.1% ZrO2 in weight. The adhesives were evaluated based on degree of conversion (DC), radiopacity, softening in solvent and microtensile bond strength (µTBS) 24 h and after 1 year of aging. Mineral deposition at the hybrid layer was assessed with micro-Raman spectroscopy at the baseline and after 14 days. RESULTS: XRD showed monoclinic and tetragonal phases of ZrO2.particles. B.E.T data revealed a surface area of 37.41 m2/g, and typical chemical groups were shown on the Raman spectra. The addition of ZrO2 did not influence the radiopacity. The addition of 4.8% and 9.1 wt.% ZrO2 showed higher initial hardness with increased softening in solvent (P < 0.05) and promoted mineral deposition at the dentin interface. DC was significantly increased in the group with 1% ZrO2 (P < 0.05). The µTBS test showed difference on the group with 9.1 wt.% of ZrO2, with a significant reduction after aging. CONCLUSION: The incorporation of ZrO2 promoted mineral deposition on the adhesive interface and the addition of 1 wt.% caused a significant increase on the DC without compromising the other physicochemical characteristics, which may prove promising for the development of new dental adhesive systems. CLINICAL RELEVANCE: The mineral deposition on the hybrid layer can result in a longer stability of the adhesive, thus delaying the hydrolytic degradation.

Ionic liquid-loaded microcapsules doped into dental resin infiltrants.

Resin infiltrants have been effectively applied in dentistry to manage non-cavitated carious lesions in proximal dental surfaces. However, the common formulations are composed of inert methacrylate monomers. In this study, we developed a novel resin infiltrant with microcapsules loaded with an ionic liquid (MC-IL), and analyzed the physical properties and cytotoxicity of the dental resin. First, the ionic liquid 1-n-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide (BMI.NTf2) was synthesized. BMI.NTf2 has previously shown antibacterial activity in a dental resin. Then, MC-IL were synthesized by the deposition of a preformed polymer. The MC-IL were analyzed for particle size and de-agglomeration effect via laser diffraction analysis and shape via scanning electron microscopy (SEM). The infiltrants were formulated, and the MC-IL were incorporated at 2.5%, 5%, and 10 wt%. A group without MC-IL was used as a control. The infiltrants were evaluated for ultimate tensile strength (UTS), contact angle, surface free energy (SFE), and cytotoxicity. The MC-IL showed a mean particle size of 1.64 (±0.08) µm, shriveled aspect, and a de-agglomeration profile suggestive of nanoparticles' presence in the synthesized powder. There were no differences in UTS among groups (p > 0.05). The incorporation of 10 wt% of MC-IL increased the contact angle (p < 0.05), while the addition from 5 wt% reduced the SFE in comparison to the control group (p < 0.05). The human cell viability was above 90% for all groups (p > 0.05). The incorporation of microcapsules as a drug-delivery system for ionic liquids may be a promising strategy to improve dental restorative materials.

In vitro evaluation of visible light-activated titanium dioxide photocatalysis for in-office dental bleaching.

The evaluation of the photocatalysis of visible light activated titanium dioxide employed in hydrogen peroxide (H2O2) was carried using seven H2O2 solutions (3.5 and 35%) and/or methylene blue (MB), with or without light irradiation (LI); the absorbance of MB was the bleaching indicator. Color analysis was performed on bovine teeth (n=12) using two different concentrations of H2O2, 6 and 35% associated with titanium dioxide (TiO2). Data were analyzed with one and two-way ANOVA, and significance level of p<0.05. Solutions containing MB, H2O2 at 3.5 or 35%, and TiO2, followed by LI, showed significant difference when compared with other groups. Greater MB reduction was found in 35% concentration. H2O2 35%+TiO2 gel showed no difference in comparison to control group. All groups for the color analysis assay showed ΔE higher than 3.3. In conclusion, TiO2 and H2O2 association is a promisor alternative for reducing the clinical time of in-office dental bleaching.

Antimicrobial and anti-inflammatory drug-delivery systems at endodontic reparative material: Synthesis and characterization.

OBJECTIVE: The aim of this study was to synthesize and characterize an experimental endodontic paste. METHODS: An experimental endodontic paste (EX) was characterized by its particle size, zeta potential, drug content and morphology. The powder of EX is composed of amoxicillin microspheres, calcium tungstate and α-tricalcium phosphate, mixed with an indomethacin nanocapsules suspension. Ultracal® (Ultradent), an iodoform-based paste (GP) and the EX were evaluated by its physical properties (flow, film thickness and radiopacity). The cytocompatibility was performed by MTT and SRB-colorimetric assays; the cell-migration was tested with scratch assay and cell-ability to remineralization with ALP and Alizarin Red S, with fibroblastic cell line. The antibacterial activity was assessed by the formation of inhibition zones and against planktonic bacteria. RESULTS: The EX and UL flow achieved ISO6876 standard, and GP was lower than 17mm. All pastes achieved the film thickness required. Radiopacity was equivalent to 1.81±0.25mmAl for EX, which did not differ from GP group 1.39±0.33mmAl (p>0.05). The UL presented 3.04±0.33mmAl. The values for SRB showed better citocompatibility in comparison with MTT for all materials. The ALP activity and formation of mineralized nodules demonstrated the remineralization potential for UL and EX. Cell migration showed continuous wound closure until complete cell healing, however, the EX accelerated the process (p<0.05). The EX showed the greatest inhibition zone (p<0.05) and was the only group with antibacterial activity against planktonic bacteria. SIGNIFICANCE: The synthesized endodontic paste demonstrated reliable physical and biological properties and could be a promising material for periapical tissue repair.

Biomechanical and histologic basis of osseodensification drilling for endosteal implant placement in low density bone. An experimental study in sheep.

A bone drilling concept, namely osseodensification, has been introduced for the placement of endosteal implants to increase primary stability through densification of the osteotomy walls. This study investigated the effect of osseodensification on the initial stability and early osseointegration of conical and parallel walled endosteal implants in low density bone. Five male sheep were used. Three implants were inserted in the ilium, bilaterally, totaling 30 implants (n=15 conical, and n=15 parallel). Each animal received 3 implants of each type, inserted into bone sites prepared as follows: (i) regular-drilling (R: 2mm pilot, 3.2mm, and 3.8mm twist drills), (ii) clockwise osseodensification (CW), and (iii) counterclockwise (CCW) osseodensification drilling with Densah Bur (Versah, Jackson, MI, USA): 2.0mm pilot, 2.8mm, and 3.8mm multi-fluted burs. Insertion torque as a function of implant type and drilling technique, revealed higher values for osseodensification relative to R-drilling, regardless of implant macrogeometry. A significantly higher bone-to-implant contact (BIC) for both osseodensification techniques (p<0.05) was observed compared to R-drilling. There was no statistical difference in BIC as a function of implant type (p=0.58), nor in bone-area-fraction occupancy (BAFO) as a function of drilling technique (p=0.22), but there were higher levels of BAFO for parallel than conic implants (p=0.001). Six weeks after surgery, new bone formation along with remodeling sites was observed for all groups. Bone chips in proximity with the implants were seldom observed in the R-drilling group, but commonly observed in the CW, and more frequently under the CCW osseodensification technique. In low-density bone, endosteal implants present higher insertion torque levels when placed in osseodensification drilling sites, with no osseointegration impairment compared to standard subtractive drilling methods.