Constructing mesoporous biochar derived from waste carton: Improving multi-site adsorption of dye wastewater and investigating mechanism.

The development of cost-efficient biochar adsorbent with a simple preparation method is essential to constructing efficient wastewater treatment system. Here, a low-cost waste carton biochar (WCB) prepared by a simple two-step carbonization was applied in efficiently removing Rhodamine B (RhB) in aqueous environment. The maximum ability of WCB for RhB adsorption was 222 mg/g, 6 and 10 times higher than both of rice straw biochar (RSB) and broadbean shell biochar (BSB), respectively. It was mainly ascribed to the mesopore structure (3.0-20.4 nm) of WCB possessing more spatial sites compared to RSB (2.2 nm) and BSB (2.4 nm) for RhB (1.4 nm✕1.1 nm✕0.6 nm) adsorption. Furthermore, external mass transfer (EMT) controlled mass transfer resistance (MTR) of the RhB sorption process by WCB which was fitted with the Langmuir model well. Meanwhile, the adsorption process was dominated by physisorption through van der Waals forces and π-π interactions. A mixture of three dyes in river water was well removed by using WCB. This work provides a straightforward method of preparing mesoporous biochar derived from waste carton with high-adsorption capacity for dye wastewater treatment.

Insights into the highly efficient treatment of dyeing wastewater using algal bloom derived activated carbon with wide-range adaptability to solution pH and temperature.

Here, a low-cost acid-base and temperature tolerant algal bloom derived activated carbon (ABAC) was successfully prepared to remove rhodamine B (RhB) from water. The ABAC exhibited maximum adsorption capacity of RhB (1101 ± 11 mg/g), higher than that of laboratory-prepared rape straw activated carbon (176 ± 5 mg/g) and commercial activated carbon (489 ± 5 mg/g). It is attributed to larger surface area and mesoporous structure of the ABAC. Furthermore, the effective adsorption of RhB by using ABAC was achieved at a wide range of solution pH (3.2-10.8) and temperature(25-50 °C). The mass transfer resistance of RhB adsorption process well depicted by Langmuir model was controlled by external mass transfer. The adsorption process involved both secondly chemisorption (H-bonds and π-π interaction) and dominated physisorption. Four dyes in river water were efficiently removed. This work provides a promising approach for developing high-absorption biomass materials for actual dye wastewater treatment.