RESUMEN
An Er(3+)-doped SiO2:Ta2O5 optical channel waveguide and nanocomposite were prepared by the sol-gel route at a Si:Ta 50:50 molar ratio. Channels with an excellent surface profile were easily and quickly fabricated by focusing a femtosecond laser onto the surface of multilayered films deposited on SiO2/Si substrates. In parallel, the same sol used to prepare the film was annealed at 900, 1000, and 1100 degrees C for 2 h, to get the nanocomposite materials. A broadband NIR emission around 1538 nm, assigned to the 4I13/2 --> 4I15/2 transition of the Er3+ ions was observed in the nanocomposites of amorphous SiO2 containing dispersed Ta2O5 nanocrystals. The 4I13/2 lifetime and emission bandwidth depend on the annealing temperature. In conclusion, Er(3+)-doped SiO2:Ta2O5 channel waveguides and nanocomposites are promising materials for photonic applications.