Surface crack detection and sizing is essential for the manufacturing and maintenance of engines, run parts, and other metal elements of aircrafts. Among various non-destructive detection methods, the fully non-contact and non-intrusive technique based on laser-stimulated lock-in thermography (LLT) has recently attracted a lot of attention from the aerospace industry. We propose and demonstrate a system of reconfigurable LLT for three-dimensional surface crack detection in metal alloys. For large area inspection, the multi-spot LLT can speed up the inspection time by a factor of the number of spots. The minimum resolved size of micro-holes is ~50 µm in diameter limited by the magnification of the camera lens. We also study the crack length ranging from 0.8 to 3.4 mm by varying the modulation frequency of LLT. An empirical parameter related to the thermal diffusion length is found to show the linear dependence with the crack length. With the proper calibration, this parameter can be used to predict the sizing of the surface fatigue cracks. Reconfigurable LLT allows us to quickly locate the crack position and accurately measure its dimensions. This method is also applicable to the non-destructive detection of surface or sub-surface defect in other materials used in various industries.
RESUMEN
Excellent castability, significantly refined microstructure, and good mechanical properties make eutectic high-entropy alloys (EHEAs) a natural fit for rapid solidification processes, e.g., additive manufacturing. Previous investigations have focused on developing EHEAs through trial and error and mixing known binary eutectic materials. However, eutectic compositions obtained from near-equilibrium conditions do not guarantee a fully eutectic microstructure under rapid solidifications. In this work, a thermodynamically guided high-throughput framework is proposed to design EHEAs for rapid solidification. Empirical formulas derived from past experimental observations and thermodynamic computations are applied and considered phase growth kinetics under rapid solidification (skewed phase diagram). The designed alloy candidate, Co25.6Fe17.9Ni22.4Cr19.1Ta8.9Al6.1 (wt.%), contains nanostructured eutectic lamellar and shows a high Vickers hardness of 675 Hv. In addition to this specific composition, the alloy design toolbox enables the development of new EHEAs for rapid solidification without the limitation of previous knowledge.