RESUMEN
We demonstrate fiber optic sensors with temperature compensation for the accurate measurement of ethanol concentration in aqueous solutions. The device consists of two photonic crystal (PhC) fiber-tip sensors: one measures the ethanol concentration via refractive index (RI) changes and the other one is isolated from the liquid for the independent measurement of temperature. The probes utilize an optimized PhC design providing a Lorentzian-like, polarization-independent response, enabling a very low imprecision (pm-level) in the wavelength determination. By combining the information from the two probes, it is possible to compensate for the effect that the temperature has on the concentration measurement, obtaining more accurate estimations of the ethanol concentration in a broad range of temperatures. We demonstrate the simultaneous and single-point measurements of temperature and ethanol concentration in water, with sensitivities of 19 pm/°C and â¼53 pm/%, in the ranges of 25 °C to 55 °C and 0 to 50% (at 25 °C), respectively. Moreover, a maximum error of 1.1% in the concentration measurement, with a standard deviation of ≤0.8%, was obtained in the entire temperature range after compensating for the effect of temperature. A limit of detection as low as 0.08% was demonstrated for the concentration measurement in temperature-stable conditions.
RESUMEN
Carbon materials slightly doped with heteroatoms such as nitrogen (N-RFC) or sulfur (S-RFC) are investigated as active catalysts for the electrochemical bielectronic oxygen reduction reaction (ORR) to H2 O2 . Mesoporous carbons with wide, accessible pores were prepared by pyrolysis of a resorcinol-formaldehyde resin using a PEO-b-PS block copolymer as a sacrificial templating agent and the nitrogen and sulfur doping were accomplished in a second thermal treatment employing 1,10-phenanthroline and dibenzothiophene as nitrogen and sulfur precursors, respectively. The synthetic strategy allowed to obtain carbon materials with very high surface area and mesopore volume without any further physicochemical post treatment. Voltammetric rotating ring-disk measurements in combination with potentiostatic and galvanostatic bulk electrolysis measurements in 0.5 m H2 SO4 demonstrated a pronounced effect of heteroatom doping and mesopores volume on the catalytic activity and selectivity for H2 O2 . N-RFC electrode was employed as electrode material in a 45â h electrolysis showing a constant H2 O2 production of 298â mmol g-1 h-1 (millimoles of H2 O2 divided by mass of catalyst and electrolysis time), with a faradic efficiency (FE) up to 61 % and without any clear evidence of degradation. The undoped carbon RFC showed a lower production rate (218â mmol g-1 h-1 ) but a higher FE of 76 %, while the performances drastically dropped when S-RFC (production rate 11â mmol g-1 h-1 and FE=39 %) was used.