PURPOSE: To summarize experience with and the efficacy of fenestrated/branched thoracic endovascular repair (F/B-TEVAR) using physician-modified stent-grafts (PMSGs) under 3D printing guidance in triple aortic arch branch reconstruction. MATERIALS AND METHODS: From February 2018 to April 2022, 14 cases of aortic arch aneurysms and 30 cases of aortic arch dissection (22 acute aortic arch dissection and 8 long-term aortic arch dissection)were treated by F/B-TEVAR in our department, including 34 males and 10 females, with an average age of 59.84 ± 11.72 years. Three aortic arch branches were affected in all patients. A 3D-printed model was made according to computed tomography angiography images and used to guide the fabrication of PMSGs. All patients were followed up. RESULTS: A total of 132 branches were successfully reconstructed with no case of conversion to open surgery. The average operation time was 4.97 ± 1.40 hours, including a mean 44.05 ± 7.72 minutes for stent-graft customization, the mean postoperative hospitalization duration was 9.91 ± 4.47 days, the average intraoperative blood loss was 480.91 mL (100-2810 mL), and the mean postoperative intensive care unit monitoring duration was 1.02 days (0-5 days). No deaths occurred within 30 days of surgery. Postoperative neurological complications occurred in 1 case (2.3%), and retrograde type A dissection occurred in 1 case (2.3%). CONCLUSION: Compared with conventional surgery, triple aortic arch branch reconstruction under the guidance of 3D printing is a minimally invasive treatment method with the advantages of accurate positioning, rapid postoperative recovery, few complications, and reliable short- to mid-term effects. CLINICAL IMPACT: At present the PMSG usually depend on imaging data and software calculation. With the guidance of 3D printing technology, image data could be transformed into 3D model, which has improved the accuracy of the positioning of the fenestrations. The diameter reduction technique and the internal mini cuff technique have made a complement to the slimed-down fenestration selection process and the low rate of endoleak. As reproducible study, our results may provide reference for TEVAR in different cases.
RESUMEN
Metallic glasses (MGs) are promising candidates for catalysts with high efficiency for dyeing wastewater remediation, due to their metastable nature, disordered structure, and large residual stresses. However, dyeing wastewater usually contains a high concentration of inorganic ions which may have adverse effects on the degradation process, while the impacts of these ions on MGs' degradation capability have often been overlooked and still remain unknown. Thus, the roles of inorganic ions (Cl-, NO3-, SO42-, and H2PO4-) on the degradation of azo dye by Fe-based MG with nominal composition of Fe81Si4B14Cu1 were systematically investigated. The results showed that the inorganic ions have significant influence on MG's surface morphology, degradation capability, mineralization and durability. All these aspects need to be considered prior to application of MGs for azo dyes degradation in real natural contaminated water or saline wastewater.