Highly efficient replacement of traditional intumescent flame retardants in polypropylene by manganese ions doped melamine phytate nanosheets.

ABSTRACT

The intumescent flame retardant (IFR) with ammonium polyphosphate (APP) as the main component has many defects in practical applications, more than that, APP can be traced to non-renewable phosphate rock resources. For the foregoing reasons, the melamine phytate supramolecular nanosheet flame retardant incorporating manganese ion (PAMA-Mn) was successfully prepared with a facile and environmental friendly hydrothermal procedure based on renewable bio-based material phytic acid (PA). The flame retardant polypropylene composite (PPI) with 13.5 wt% APP and 4.5 wt% pentaerythritol (PER) failed to the UL-94 test, and its limiting oxygen index (LOI) value was only 26.5%. After 33 wt% of APP was replaced by PAMA-Mn, the PPMn33 incorporating only 18 wt% flame retardant additives passed the UL-94 V-0 rating, and its LOI value was increased to 31.9%. Compared with PP, pHRR and pSPR values of PPMn33 were reduced by 56% and 23%, respectively. The fire retardant mechanism of PPMn33 was thoroughly discussed via a variety of characterization methods. It was found that the peak of the Gram-Schmidt curve of PPMn33 was drastically reduced by 49% relative to that of PPI, indicating a remarkably decrease of combustible volatile products owing to the incorporation of PAMA-Mn, thereby rapidly reducing the fire hazard risk.