ABSTRACT
Multidimensional data recording inside nanoporous high-silica glass by a femtosecond laser beam has been investigated. It is shown that three femtosecond laser pulses at pulse repetition rates up to 1 MHz are sufficient for recording 3 bits of information inside nanoporous glass, which is an order of magnitude lower than the number of pulses required for data writing in silica glass and provides a corresponding gain in the data writing speed. Multilayer data recording and reading were demonstrated providing the storage density corresponding to the capacity of 25 GB in the optical compact disc form factor. An outstanding thermal stability of the proposed optical data storage is confirmed by the 24 h long heat treatment at 700°C, which could not damage the recorded data.
ABSTRACT
We report an unexpected pulse repetition rate effect on ultrafast-laser modification of sodium germanate glass with the composition 22Na2O 78GeO2. While at a lower pulse repetition rate (~≤250 kHz), the inscription of nanogratings possessing form birefringence is observed under series of 105-106 pulses, a higher pulse repetition rate launches peripheral microcrystallization with precipitation of the Na2Ge4O9 phase around the laser-exposed area due to the thermal effect of femtosecond pulses via cumulative heating. Depending on the pulse energy, the repetition rate ranges corresponding to nanograting formation and microcrystallization can overlap or be separated from each other. Regardless of crystallization, the unusual growth of optical retardance in the nanogratings with the pulse repetition rate starting from a certain threshold has been revealed instead of a gradual decrease in retardance with the pulse repetition rate earlier reported for some other glasses. The repetition rate threshold of the retardance growth is shown to be inversely related to the pulse energy and to vary from ~70 to 200 kHz in the studied energy range. This effect can be presumably assigned to the chemical composition shift due to the thermal diffusion of sodium cations occurring at higher pulse repetition rates when the thermal effect of the ultrashort laser pulses becomes noticeable.
ABSTRACT
Space-selective laser-induced crystallization of glass enables direct femtosecond laser writing of crystal-in-glass channel waveguides having nearly single-crystal structure and consisting of functional phases with favorable nonlinear optical or electrooptical properties. They are regarded as promising components for novel integrated optical circuits. However, femtosecond-laser-written continuous crystalline tracks typically have an asymmetric and strongly elongated cross-section, which causes a multimode character of light guiding and substantial coupling losses. Here, we investigated the conditions of partial remelting of laser-written LaBGeO5 crystalline tracks in lanthanum borogermanate glass by the same femtosecond laser beam which had been used for their writing. Exposure to femtosecond laser pulses at 200 kHz repetition rate provided cumulative heating of the sample in the vicinity of the beam waist sufficient to provide space-selective melting of crystalline LaBGeO5. To form a smoother temperature field, the beam waist was moved along the helical or flat sinusoidal path along the track. The sinusoidal path was shown to be favorable for tailoring the improved cross-section of the crystalline lines by partial remelting. At optimized laser processing parameters, most of the track was vitrified, and the residual part of the crystalline cross-section had an aspect ratio of about 1:1. Thermal-induced stress emerging during the tailoring procedure was efficiently eliminated by fine post-annealing. The proposed technique suggests a new way to control the morphology of laser-written crystal-in-glass waveguides by tailoring their cross-section, which is expected to improve the mode structure of the guided light.