ABSTRACT
As lignin is becoming more and more attractive to industry and the circular economy continues to grow, the utilization of a byproduct that, to date, has been underrated by the wood industry is investigated as an abundantly available source of lignin. Bark from spruce, larch and beech tress is extracted using the organosolv process with and without prior hot water extraction. The influence of the treatment on chemical properties of the lignin was determined by spectrophotometric, chromatographic, and vibrational spectroscopy. It was found that hot water extraction prior to organosolv extraction influences the chemical composition, antioxidative properties and molecular weight distribution of the obtained extracts. While hot water extracts are rich in flavonoids, organosolv fractions can contain high amounts of organic acids depending on whether they are from a hardwood or softwood source. This investigation lays the foundation for further research into the utilization of byproducts to generate high-value resources.
ABSTRACT
Furfuryl alcohol (FA) and lactic acid (LA) are two of the most interesting biomolecules, easily obtainable from sugars and hence extremely attractive for green chemistry solutions. These substances undergo homopolymerization and they have been rarely considered for copolymerization. Typically, FA homopolymerizes exothermically in an acid environment producing inhomogeneous porous materials, but recent studies have shown that this reaction can be controlled and therefore we have implemented this process to trigger the copolymerization with LA. The mechanical tests have shown that the blend containing small amount of FA were rigid and the fracture showed patterns more similar to the one of neat polyfurfuryl alcohol (PFA). This LA-rich blend exhibited higher chloroform and water resistances, while thermal analyses (TG and DSC) also indicated a higher furanic character than expected. These observations suggested an intimate interconnection between precursors which was highlighted by the presence of a small band in the ester region of the solid state 13C-NMR, even if the FT-IR did not evidence any new signal. These studies show that these bioplastics are basically constituted of PLA and PFA homopolymers with some small portion of covalent bonds between the two moieties.