ABSTRACT
Thin-ply laminates exhibit a higher degree of freedom in design and altered failure behaviour, and therefore, an increased strength for unnotched laminates in comparison to thick-ply laminates. For notched laminates, the static strength is strongly decreased; this is caused by a lack of stress relaxation through damage, which leads to a higher stress concentration and premature, brittle failure. To overcome this behaviour and to use the advantage of thin-ply laminates in areas with high stress concentrations, we have investigated thin-ply hybrid laminates with different metal volume fractions. Open hole tensile (OHT) and open hole compression (OHC) tests were performed with quasi-isotropic carbon fibre reinforced plastic (CFRP) specimens. In the area of stress concentration, 90° layers were locally substituted by stainless steel layers of differing volume fractions, from 12.5% to 25%. The strain field on the specimen surface was evaluated in-situ using a digital image correlation (DIC) system. The embedding of stainless steel foils in thin-ply samples increases the OHT strength up to 60.44% compared to unmodified thin-ply laminates. The density specific OHT strength is increased by 33%. Thick-ply specimens achieve an OHC strength increase up to 45.7%, which corresponds to an increase in density specific strength of 32.4%.
ABSTRACT
A trade-off between enhancement of physical properties of the final part and the processability during manufacturing always exists for the application of nanocarbon materials in thermoset-based composites. For different epoxy resins, this study elaborates the impact of nanocarbon particle type, functionalization, and filler loading on the resulting properties, i.e., rheological, electrical, thermo-mechanical, as well as the fracture toughness in mode I and mode II loading. Therefore, a comprehensive set of carbon nanoparticles, consisting of carbon black (CB), single-walled carbon nanotubes (SWCNT), multi-walled carbon nanotubes (MWCNT), few layer graphene (FLG), and electrochemically expanded graphite (ExG), in purified or functionalized configuration was introduced in various epoxy resins, with different molecular weight distributions. A novel technique to introduce sharp cracks into single-edge notched bending (SENB) fracture toughness specimens led to true values. SWCNT show highest potential for increasing electrical properties without an increase in viscosity. Functionalized MWCNT and planar particles significantly increase the fracture toughness in mode I by a factor of two.