ABSTRACT
Polyanionic Na3V2(PO4)2FO2 has been successfully prepared for the first time by ionothermal reaction in 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (EMIM TFSI) ionic liquid. Its structure and elemental stoichiometry are confirmed by X-ray diffraction, NMR spectroscopy, and ICP-OES, respectively. Furthermore, the scanning electron microscopy reveals that the as-obtained material possesses an original platelet-like morphology. A topochemical reaction mechanism is proposed to explain the formation of the 3D framework of Na3V2(PO4)2FO2 from layered compound α-VOPO4·2H2O. Galvanostatic electrochemical tests indicate a modification of the desodiation and sodiation mechanism of the as-prepared Na3V2(PO4)2FO2 compared to those synthesized by conventional solid-state approaches. Furthermore, the electrochemical performance of Na3V2(PO4)2FO2 obtained at different cycling rates is also discussed.
ABSTRACT
Among the positive electrode materials for Na-ion batteries, Na3V2(PO4)2F3 is considered as one of the most promising and generates high interest. Here, we study the influence of the sol-gel synthesis parameters on the structure and on the electrochemical signature of the partially substituted Na3V2-zAlz(PO4)2(F,O)3 materials. We demonstrate that the acidity of the starting solution influences the vanadium oxidation state of the final product. For the first time we report on the possibility of controlling the double Al/V and O/F substitution that leads to the preparation of the Na3V2-zAlz(PO4)2F1+zO2-z solid solution.
ABSTRACT
We here present the synthesis of a new material, Na3(VO)Fe(PO4)2F2, by the sol-gel method. Its atomic and electronic structural descriptions are determined by a combination of several diffraction and spectroscopy techniques such as synchrotron X-ray powder diffraction and synchrotron X-ray absorption spectroscopy at V and Fe K edges, 57Fe Mössbauer, and 31P solid-state nuclear magnetic resonance spectroscopy. The crystal structure of this newly obtained phase is similar to that of Na3(VO)2(PO4)2F, with a random distribution of Fe3+ ions over vanadium sites. Even though Fe3+ and V4+ ions situate on the same crystallographic position, their local environment can be studied separately using 57Fe Mössbauer and X-ray absorption spectroscopy at Fe and V K edges, respectively. The Fe3+ ion resides in a symmetric octahedral environment, while the octahedral site of V4+ is greatly distorted due to the presence of the vanadyl bond. No electrochemical activity of the Fe4+/Fe3+ redox couple is detected, at least up to 5 V, whereas the reduction of Fe3+ to Fe2+ has been observed at â¼1.5 V versus Na+/Na through the insertion of 0.5 Na+ into Na3(VO)Fe(PO4)2F2. Comparing to Na3(VO)2(PO4)2F, the electrochemical profile of Na3(VO)Fe(PO4)2F2 in the same cycling condition shows a smaller polarization which could be due to a slight improvement in Na+ diffusion process thanks to the presence of Fe3+ in the framework. Furthermore, the desodiation mechanism occurring upon charging is investigated by operando synchrotron X-ray diffraction and operando synchrotron X-ray absorption at V K edge.