ABSTRACT
The observation of inverted magnetic hysteresis loops and negative magnetic remanence (NRM) in a 7.6 nm thin film of La0.7Sr0.3MnO3 grown on SrTiO3 substrates is reported. The film was grown employing pulsed laser deposition and characterized by reflection high-energy electron diffraction during growth and using x-ray reflectivity measurements post-growth. Magnetic properties of the film were measured from 5 K to 400 K under both the field-cooled (FC) and zero-field-cooled (ZFC) conditions. The observed results of inverted magnetic hysteresis loops and NRM are interpreted in terms of the co-existence of a magnetically inhomogeneous region consisting of superparamagnetic spin clusters with a blocking temperature T B = 240 K and the ferromagnetic state with an ordering temperature T C = 290 K. Hysteresis loop inversion is observed in the temperature region of T B < T < T C whereas NRM appears in the mixed superparamagnetic and ferromagnetic states for T < T C down to 5 K. These observations of hysteresis loop inversion and NRM are related to the magneto-static interaction between the superparamagnetic and ferromagnetic phases leading to anti-alignment of spin of both magnetic phases with respect to each other.