Formation of aligned periodic patterns during the crystallization of organic semiconductor thin films.

Self-organizing patterns with micrometre-scale features are promising for the large-area fabrication of photonic devices and scattering layers in optoelectronics. Pattern formation would ideally occur in the active semiconductor to avoid the need for further processing steps. Here, we report an approach to form periodic patterns in single layers of organic semiconductors by a simple annealing process. When heated, a crystallization front propagates across the film, producing a sinusoidal surface structure with wavelengths comparable to that of near-infrared light. These surface features initially form in the amorphous region within a micrometre of the crystal growth front, probably due to competition between crystal growth and surface mass transport. The pattern wavelength can be tuned from 800 nm to 2,400 nm by varying the film thickness and annealing temperature, and millimetre-scale domain sizes are obtained. This phenomenon could be exploited for the self-assembly of microstructured organic optoelectronic devices.

Sub-turn-on exciton quenching due to molecular orientation and polarization in organic light-emitting devices.

The efficiency of organic light-emitting devices (OLEDs) is often limited by roll-off, where efficiency decreases with increasing bias. In most OLEDs, roll-off primarily occurs due to exciton quenching, which is commonly assumed to be active only above device turn-on. Below turn-on, exciton and charge carrier densities are often presumed to be too small to cause quenching. Using lock-in detection of photoluminescence, we find that this assumption is not generally valid; luminescence can be quenched by >20% at biases below turn-on. We show that this low-bias quenching is due to hole accumulation induced by intrinsic polarization of the electron transport layer (ETL). Further, we demonstrate that selection of nonpolar ETLs or heating during deposition minimizes these losses, leading to efficiency enhancements of >15%. These results reveal design rules to optimize efficiency, clarify how ultrastable glasses improve OLED performance, and demonstrate the importance of quantifying exciton quenching at low bias.