ABSTRACT
A high-throughput sonochemical synthesis and testing strategy was developed to discover covalent organic frameworks (COFs) for photocatalysis. In total, 76 conjugated polymers were synthesized, including 60 crystalline COFs of which 18 were previously unreported. These COFs were then screened for photocatalytic hydrogen peroxide (H2O2) production using water and oxygen. One of these COFs, sonoCOF-F2, was found to be an excellent photocatalyst for photocatalytic H2O2 production even in the absence of sacrificial donors. However, after long-term photocatalytic tests (96 h), the imine sonoCOF-F2 transformed into an amide-linked COF with reduced crystallinity and loss of electronic conjugation, decreasing the photocatalytic activity. When benzyl alcohol was introduced to form a two-phase catalytic system, the photostability of sonoCOF-F2 was greatly enhanced, leading to stable H2O2 production for at least 1 week.
ABSTRACT
The invention of inverse vulcanization provides great opportunities for generating functional polymers directly from elemental sulfur, an industrial by-product. However, unsatisfactory mechanical properties have limited the scope for wider applications of these exciting materials. Here, we report an effective synthesis method that significantly improves mechanical properties of sulfur-polymers and allows control of performance. A linear pre-polymer containing hydroxyl functional group was produced, which could be stored at room temperature for long periods of time. This pre-polymer was then further crosslinked by difunctional isocyanate secondary crosslinker. By adjusting the molar ratio of crosslinking functional groups, the tensile strength was controlled, ranging from 0.14±0.01â MPa to 20.17±2.18â MPa, and strain was varied from 11.85±0.88 % to 51.20±5.75 %. Control of hardness, flexibility, solubility and function of the material were also demonstrated. We were able to produce materials with suitable combination of flexibility and strength, with excellent shape memory function. Combined with the unique dynamic property of S-S bonds, these polymer networks have an attractive, vitrimer-like ability for being reshaped and recycled, despite their crosslinked structures. This new synthesis method could open the door for wider applications of sustainable sulfur-polymers.
ABSTRACT
Inverse vulcanization, a sustainable platform, can transform sulfur, an industrial by-product, into polymers with broad promising applications such as heavy metal capture, electrochemistry and antimicrobials. However, the process usually requires high temperatures (≥159 °C), and the crosslinkers needed to stabilize the sulfur are therefore limited to high-boiling-point monomers only. Here, we report an alternative route for inverse vulcanization-mechanochemical synthesis, with advantages of mild conditions (room temperature), short reaction time (3 h), high atom economy, less H2S, and broader monomer range. Successful generation of polymers using crosslinkers ranging from aromatic, aliphatic to volatile, including renewable monomers, demonstrates this method is powerful and versatile. Compared with thermal synthesis, the mechanochemically synthesized products show enhanced mercury capture. The resulting polymers show thermal and light induced recycling. The speed, ease, versatility, safety, and green nature of this process offers a more potential future for inverse vulcanization, and enables further unexpected discoveries.
Subject(s)
Polymers , Sulfur , Electrochemistry , Recycling , Transition TemperatureABSTRACT
The inverse vulcanization (IV) of elemental sulfur to generate sulfur-rich functional polymers has attracted much recent attention. However, the harsh reaction conditions required, even with metal catalysts, constrains the range of feasible crosslinkers. We report here a photoinduced IV that enables reaction at ambient temperatures, greatly broadening the scope for both substrates and products. These conditions enable volatile and gaseous alkenes and alkynes to be used in IV, leading to sustainable alternatives for environmentally harmful plastics that were hitherto inaccessible. Density functional theory calculations reveal different energy barriers for thermal, catalytic and photoinduced IV processes. This protocol circumvents the long curing times that are common in IV, generates no H2S by-products, and produces high-molecular-weight polymers (up to 460,000 g mol-1) with almost 100% atom economy. This photoinduced IV strategy advances both the fundamental chemistry of IV and its potential industrial application to generate materials from waste feedstocks.
Subject(s)
Polymers , Sulfur , Alkenes , Plastics , CatalysisABSTRACT
Mercury pollution is a significant threat to the environment and health worldwide. Therefore, effective and low-cost absorbents that are easily scalable are needed for real-world applications. Enlarging the surface area of the materials and doping with heteroatoms are two of the most common strategies to cope with this problem. Sulfur-doped activated carbon synthesized from the carbonization of inverse vulcanized thiopolymers makes it possible to combine both large specific surface area and doping of heteroatoms, resulting in outperformance in mercury uptake against commercial activated carbons. Convenient recovery of mercury absorbents after treatment should be beneficial in mercury collecting and recycling. Therefore, magnetic sulfur-doped carbons (MSCs) were prepared by functionalizing sulfur doped carbons through chemical precipitation with magnetic iron oxides. Besides the characterisations of materials, mercury uptake experiments, such as stactic test, capacity test, impact of solution pH, and mixed ions interferences were performed. These MSCs exhibit high specific surface area (1,329 m2/g), high sulfur content (up to 14.8 wt%), porous structure, low cost, and are convenient for retrieval. MSCs are demonstrated high uptake capacity (187 mg g-1) and efficiency in mercury solution and multifunctional absorption in mixed ions solution, showing their potential to be applied in water purification and environmental remediation.