Revealing operando surface defect-dependent electrocatalytic performance of Pt at the subparticle level.

Understanding the operando defect-tuning performance of catalysts is critical to establish an accurate structure-activity relationship of a catalyst. Here, with the tool of single-molecule super-resolution fluorescence microscopy, by imaging intermediate CO formation/oxidation during the methanol oxidation reaction process on individual defective Pt nanotubes, we reveal that the fresh Pt ends with more defects are more active and anti-CO poisoning than fresh center areas with less defects, while such difference could be reversed after catalysis-induced step-by-step creation of more defects on the Pt surface. Further experimental results reveal an operando volcano relationship between the catalytic performance (activity and anti-CO ability) and the fine-tuned defect density. Systematic DFT calculations indicate that such an operando volcano relationship could be attributed to the defect-dependent transition state free energy and the accelerated surface reconstructing of defects or Pt-atom moving driven by the adsorption of the CO intermediate. These insights deepen our understanding to the operando defect-driven catalysis at single-molecule and subparticle level, which is able to help the design of highly efficient defect-based catalysts.

Weathered granites and soils harbour microbes with lanthanide-dependent methylotrophic enzymes.

BACKGROUND: Prior to soil formation, phosphate liberated by rock weathering is often sequestered into highly insoluble lanthanide phosphate minerals. Dissolution of these minerals releases phosphate and lanthanides to the biosphere. Currently, the microorganisms involved in phosphate mineral dissolution and the role of lanthanides in microbial metabolism are poorly understood. RESULTS: Although there have been many studies of soil microbiology, very little research has investigated microbiomes of weathered rock. Here, we sampled weathered granite and associated soil to identify the zones of lanthanide phosphate mineral solubilisation and genomically define the organisms implicated in lanthanide utilisation. We reconstructed 136 genomes from 11 bacterial phyla and found that gene clusters implicated in lanthanide-based metabolism of methanol (primarily xoxF3 and xoxF5) are surprisingly common in microbial communities in moderately weathered granite. Notably, xoxF3 systems were found in Verrucomicrobia for the first time, and in Acidobacteria, Gemmatimonadetes and Alphaproteobacteria. The xoxF-containing gene clusters are shared by diverse Acidobacteria and Gemmatimonadetes, and include conserved hypothetical proteins and transporters not associated with the few well studied xoxF systems. Given that siderophore-like molecules that strongly bind lanthanides may be required to solubilise lanthanide phosphates, it is notable that candidate metallophore biosynthesis systems were most prevalent in bacteria in moderately weathered rock, especially in Acidobacteria with lanthanide-based systems. CONCLUSIONS: Phosphate mineral dissolution, putative metallophore production and lanthanide utilisation by enzymes involved in methanol oxidation linked to carbonic acid production co-occur in the zone of moderate granite weathering. In combination, these microbial processes likely accelerate the conversion of granitic rock to soil.

Constructing Asymmetric Charge Polarized NiCo Prussian Blue Analogue for Promoted Electrocatalytic Methanol to Formate Conversion.

The highly selective electrochemical conversion of methanol to formate is of great significance for various clean energy devices, but understanding the structure-to-property relationship remains unclear. Here, the asymmetric charge polarized NiCo prussian blue analogue (NiCo PBA-100) is reported to exhibit remarkable catalytic performance with high current density (210 mA cm-2 @1.65 V vs RHE) and Faraday efficiency (over 90%). Meanwhile, the hybrid water splitting and Zinc-methanol-battery assembled by NiCo PBA-100 display the promoted performance with decent stability. X-ray absorption spectroscopy (XAS) and operando Raman spectroscopy indicate that the asymmetric charge polarization in NiCo PBA leads to more unoccupied states of Ni and occupied states of Co, thereby facilitating the rapid transformation of the high-active catalytic centers. Density functional theory calculations combining operando Fourier transform infrared spectroscopy demonstrate that the final reconstructed catalyst derived by NiCo PBA-100 exhibits rearranged d band properties along with a lowered energy barrier of the rate-determining step and favors the desired formate production.

Colloidal Synthesis of Carbon Dot-ZnSe Nanoplatelet Van der Waals Heterostructures for Boosting Photocatalytic Generation of Methanol-Storable Hydrogen.

Methanol is not only a promising liquid hydrogen carrier but also an important feedstock chemical for chemical synthesis. Catalyst design is vital for enabling the reactions to occur under ambient conditions. This study reports a new class of van der Waals heterojunction photocatalyst, which is synthesized by hot-injection method, whereby carbon dots (CDs) are grown in situ on ZnSe nanoplatelets (NPLs), i.e., metal chalcogenide quantum wells. The resultant organic-inorganic hybrid nanoparticles, CD-NPLs, are able to perform methanol dehydrogenation through CH splitting. The heterostructure has enabled light-induced charge transfer from the CDs into the NPLs occurring on a sub-nanosecond timescale, with charges remaining separated across the CD-NPLs heterostructure for longer than 500 ns. This resulted in significantly heightened H2 production rate of 107 µmole·g-1·h-1 and enhanced photocurrent density up to 34 µA cm-2 at 1 V bias potential. EPR and NMR analyses confirmed the occurrence of α-CH splitting and CC coupling. The novel CD-based organic-inorganic semiconductor heterojunction is poised to enable the discovery of a host of new nano-hybrid photocatalysts with full tunability in the band structure, charge transfer, and divergent surface chemistry for guiding photoredox pathways and accelerating reaction rates.

Ultrathin NiV Layered Double Hydroxide for Methanol Electrooxidation: Understanding the Proton Detachment Kinetics and Methanol Dehydrogenation Oxidation.

Electrochemical methanol oxidation reaction (MOR) is regarded as a promising pathway to obtain value-added chemicals and drive cathodic H2 production, while the rational design of catalyst and in-depth understanding of the structure-activity relationship remains challenging. Herein, the ultrathin NiV-LDH (u-NiV-LDH) with abundant defects is successfully synthesized, and the defect-enriched structure is finely determined by X-ray adsorption fine structure etc. When applied for MOR, the as-prepared u-NiV-LDH presents a low potential of 1.41 V versus RHE at 100 mA cm-2, which is much lower than that of bulk NiV-LDH (1.75 V vs RHE) at the same current density. The yield of H2 and formate is 98.2% and 88.1% as its initial over five cycles and the ultrathin structure of u-NiV-LDH can be well maintained. Various operando experiments and theoretical calculations prove that the few-layer stacking structure makes u-NiV-LDH free from the interlayer hydrogen diffusion process and the hydrogen can be directly detached from LDH laminate. Moreover, the abundant surface defects upshift the d-band center of u-NiV-LDH and endow a higher local methanol concentration, resulting in an accelerated dehydrogenation kinetics on u-NiV-LDH. The synergy of the proton detachment from the laminate and the methanol dehydrogenation oxidation contributes to the excellent MOR performance of u-NiV-LDH.

Mixed-Dimensional Partial Dealloyed PtCuBi/C as High-Performance Electrocatalysts for Methanol Oxidation with Enhanced CO Tolerance.

Developing efficient electrocatalysts for methanol oxidation reaction (MOR) is crucial in advancing the commercialization of direct methanol fuel cells (DMFCs). Herein, carbon-supported 0D/2D PtCuBi/C (0D/2D PtCuBi/C) catalysts are fabricated through a solvothermal method, followed by a partial electrochemical dealloying process to form a novel mixed-dimensional electrochemically dealloyed PtCuBi/C (0D/2D D-PtCuBi/C) catalysts. Benefiting from distinctive mixed-dimensional structure and composition, the as-obtained 0D/2D D-PtCuBi/C catalysts possess abundant accessible active sites. The introduction of Cu as a water-activating element weakens the COads, and oxophilic metal Bi facilitates the OHads, thereby enhancing its tolerance to CO poisoning and promoting MOR activity. The X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure spectroscopy (XAFS) collectively reveal the electron transfer from Cu and Bi to Pt, the electron-enrichment effect induced by dealloying, and the strong interactions among Pt-M (Cu, Pt, and Bi) multi-active sites, which improve the tuning of the electronic structure and enhancement of electron transfer ability. Impressively, the optimized 0D/2D D-PtCuBi/C catalysts exhibit the superior mass activity (MA) of 17.68 A mgPt -1 for MOR, which is 14.86 times higher than that of commercial Pt/C. This study offers a proposed strategy for Pt-based alloy catalysts, enabling their use as efficient anodic materials in fuel cell applications.

In Situ Pt Migration Enabled Resurrection of Electrocatalyst and Fuel Cell Device.

In direct methanol fuel cells (DMFCs), the poisoning of noble metals is considered to be a major impediment to their commercial development. Here, it is found that the loss of surface Pt is one main reason for the attenuation of catalyst performance during long-time methanol oxidation reaction (MOR). A strategy to realize in situ resurrection of the deactivated catalyst by migrating Pt atoms inside to the surface is innovatively proposed. A high-activity Pt-SnO2 is designed, whose MOR activity is resurrected to 97.4% of the initial value. Based on this, the multiple resurrection of a DMFC device is also achieved for the first time. This work provides a new approach for the solution of catalyst deactivation and the development of sustainable catalysts as well as fuel cells.

Platinum-Ruthenium Bimetallic Nanoparticle Catalysts Synthesized Via Direct Joule Heating for Methanol Fuel Cells.

Platinum-Ruthenium (PtRu) bimetallic nanoparticles are promising catalysts for methanol oxidation reaction (MOR) required by direct methanol fuel cells. However, existing catalyst synthesis methods have difficulty controlling their composition and structures. Here, a direct Joule heating method to yield highly active and stable PtRu catalysts for MOR is shown. The optimized Joule heating condition at 1000 °C over 50 microseconds produces uniform PtRu nanoparticles (6.32 wt.% Pt and 2.97 wt% Ru) with an average size of 2.0 ± 0.5 nanometers supported on carbon black substrates. They have a large electrochemically active surface area (ECSA) of 239 m2 g-1 and a high ECSA normalized specific activity of 0.295 mA cm-2. They demonstrate a peak mass activity of 705.9 mA mgPt -1 for MOR, 2.8 times that of commercial 20 wt.% platinum/carbon catalysts, and much superior to PtRu catalysts obtained by standard hydrothermal synthesis. Theoretical calculation results indicate that the superior catalytic activity can be attributed to modified Pt sites in PtRu nanoparticles, enabling strong methanol adsorption and weak carbon monoxide binding. Further, the PtRu catalyst demonstrates excellent stability in two-electrode methanol fuel cell tests with 85.3% current density retention and minimum Pt surface oxidation after 24 h.

Confining N-Doped Carbon Dots into PtNi Aerogels Skeleton for Robust Electrocatalytic Methanol Oxidation and Oxygen Reduction.

Noble metallic aerogels with the self-supported hierarchical structure and remarkable activity are promising for methanol fuel cells, but are limited by the severe poisoning and degradation of active sites during electrocatalysis. Herein, the highly stable electrocatalyst of N-doped carbon dots-PtNi (NCDs-PtNi) aerogels is proposed by confining NCDs with alloyed PtNi for methanol oxidation and oxygen reduction reactions. Comprehensive electrocatalytic measurements and theoretical investigations suggest the improvement in structure stability and regulation in electronic structure for better electrocatalytic durability when confining NCDs with PtNi aerogels. Notably, the NCDs-PtNi aerogels perform 12-fold higher activity than that of Pt/C and maintain 52% of their initial activity after 5000 cycles toward acidic methanol oxidation. The enhanced stability and activity of NCDs-PtNi aerogels are also evident for oxygen reduction reactions in different electrolytes. These results highlight the effectiveness of stabilizing metallic aerogels with NCDs, offering a feasible pathway to develop robust electrocatalysts for fuel cells.

Enhanced Activity of Small Pt Nanoparticles Decorated with High-Loading Single Fe─N4 for Methanol Oxidation and Oxygen Reduction via the Assistive Active Sites Strategy.

Decorating platinum (Pt) with a single atom offers a promising approach to tailoring their catalytic activity. In this study, for the first time, an innovative assistive active sites (AAS) strategy is proposed to construct high-loading (3.46wt.%) single Fe─N4 as AAS, which are further hybridized with small Pt nanoparticles to enhance both oxygen reduction reaction (ORR) and methanol oxidation reaction (MOR) activities. For ORR, the target catalyst (Pt/HFeSA-HCS) exhibits a higher mass activity (MA) of 0.98 A mgPt -1 and specific activity (SA) of 1.39 mA cmPt -2 at 0.90 V versus RHE. As for MOR, Pt/HFeSA-HCS shows exceptional MA (3.21 A mgPt -1) and SA (4.27 mA cmPt -2) at peak values, surpassing commercial Pt/C by 15.3 and 11.5 times, respectively. The underlying mechanism behind this AAS strategy is to find that in MOR, Fe─N4 promotes water dissociation, generating more *OH to accelerate the conversion of *CO to CO2. Meanwhile, in ORR, Fe─N4 acts as a competitor to adsorb *OH, weakening Pt─OH bonding and facilitating desorption of *OH on the Pt surface. Constructing AAS that can enhance dual functionality simultaneously can be seen as a successful "kill two birds with one stone" strategy.

Hybrid Acid/Base Electrolytic Cell for Hydrogen Generation and Methanol Conversion Implemented by Bifunctional Ni/MoN Nanorod Electrocatalyst.

Combining the methanol oxidation reaction (MOR) and hydrogen evolution reaction (HER) within an integrated electrolytic system may offer the advantages of enhanced kinetics of the anode, reduced energy consumption, and the production of high-purity hydrogen. Herein, it is reported the construction of Ni─MoN nanorod arrays supported on a nickel foam substrate (Ni─MoN/NF) as a bifunctional electrocatalyst for electrocatalytic hydrogen production and selective methanol oxidation to formate. Remarkably, The optimal Ni─MoN/NF catalyst displays exceptional HER performance with an overpotential of only 49 mV to attain 10 mA cm-2 in acid, and exhibits a high activity for MOR to achieve 100 mA cm-2 at 1.48 V in alkali. A hybrid acid/base electrolytic cell with Ni─MoN/NF electrode as anode and cathode is further developed for an integrated HER-MOR cell, which only requires a voltage of 0.56 V at 10 mA cm-2 , significantly lower than that of the HER-OER system (0.70 V). The density functional theory studies reveal that the incorporation of Ni effectively modulates the electronic structure of MoN, thereby resulting in enhanced catalytic activity. The unique combination of high electrocatalytic activity and excellent stability make the Ni─MoN/NF catalyst a promising candidate for practical applications in electrocatalytic hydrogen production and methanol oxidation.

Recycling the Spent LiNi1- x - yMnxCoyO2 Cathodes for High-Performance Electrocatalysts toward Both the Oxygen Catalytic and Methanol Oxidation Reactions.

The traditional recycling methods of the spent lithium ion batteries (LIBs) involve the intricate and cumbersome steps. This work proposes a facile method of acid leaching followed by the sulfurization treatment to achieve the high Li leaching efficiency, and obtain high-performance multi-function electrocatalysts for oxygen reduction (ORR), oxygen evolution (OER), and methanol oxidation reactions (MOR) from the spent LIB ternary cathodes. By this method, the Li leaching efficiency from the spent LIB ternary cathode can reach 98.3%, and the transition metal sulfide heterostructures (LNMCO-H-450S) consisting MnS, NiS2, and NiCo2S4 phases can be obtained. LNMCO-H-450S shows the superior bifunctional oxygen catalytic activities with ORR half-wave potential of 0.763 V and OER potential at 10 mA cm-2 of 1.561 V, surpassing most of the state-of-the-art electrocatalysts. LNMCO-H-450S also demonstrates the superior MOR catalytic activity with the potential at 100 mA cm-2 being 1.37 V. Using LNMCO-H-450S as the oxygen catalyst, this work can construct the aqueous and solid-state zinc-air batteries with high power density of 309 and 257 mW cm-2, respectively. This work provides a promising strategy for the efficient recovery of Li, and reutilization of Ni, Co, and Mn from the spent LIB ternary cathodes.

A Universal Approach for Controllable Synthesis of Homogeneously Alloyed PtM Nanoflowers toward Enhanced Methanol Oxidation.

Platinum (Pt)-based alloys have received considerable attention due to their compositional variability and unique electrochemical properties. However, homogeneous element distribution at the nanoscale, which is beneficial to various electrocatalytic reactions, is still a great challenge. Herein, a universal approach is proposed to synthesize homogeneously alloyed and size-tunable Pt-based nanoflowers utilizing high gravity technology. Owing to the significant intensification of micro-mixing and mass transfer in unique high gravity shearing surroundings, five typical binary/ternary Pt-based nanoflowers are instantaneously achieved at room temperature. As a proof-of-concept, as-synthesized Platinum-Silver nanoflowers (PtAg NFs) demonstrate excellent catalytic performance and anti-CO poisoning ability for anodic methanol oxidation reaction with high mass activity of 1830 mA mgPt -1, 3.5 and 3.2 times higher than those of conventional beaker products and commercial Pt/C, respectively. The experiment in combination with theory calculations suggest that the enhanced performance is due to additional electronic transmission and optimized d-band center of Pt caused by high alloying degree.

Enhanced Hydroxyl Adsorption in Ultrathin NiO/Cr2 O3 In-Plane Heterostructures for Efficient Alkaline Methanol Oxidation Reaction.

The exploration of advanced nickel-based electrocatalysts for alkaline methanol oxidation reaction (MOR) holds immense promise for value-added organic products coupled with hydrogen production, but still remain challenging. Herein, we construct ultrathin NiO/Cr2 O3 in-plane heterostructures to promote the alkaline MOR process. Experimental and theoretical studies reveal that NiO/Cr2 O3 in-plane heterostructures enable a favorable upshift of the d-band center and enhanced adsorption of hydroxyl species, leading to accelerated generation of active NiO(OH)ads species. Furthermore, ultrathin in-plane heterostructures endow the catalyst with good charge transfer ability and adsorption behavior of methanol molecules onto catalytic sites, contributing to the improvement of alkaline MOR kinetics. As a result, ultrathin NiO/Cr2 O3 in-plane heterostructures exhibit a remarkable MOR activity with a high current density of 221 mA cm-2 at 0.6 V vs Ag/AgCl, which is 7.1-fold larger than that of pure NiO nanosheets and comparable with other highly active catalysts reported so far. This work provides an effectual strategy to optimize the activity of nickel-based catalysts and highlights the dominate efficacy of ultrathin in-plane heterostructures in alkaline MOR.

Catalytic Oxidation of Methanol to Formaldehyde Catalyzed by Iron Complex with N3S3-type Tripodal Ligand.

A Fe3+ complex with N3S3-type tripod ligand, 1, reacts with O2 in CH3OH to generate formaldehyde, which has been studied structurally, spectroscopically, and electrochemically. Complex 1 crystallizes as an octahedral structure with crystallographic C3 symmetry around the metal, with Fe-N=2.2917(17) Å and Fe-S=2.3574(6) Å. UV-vis spectrum of 1 in CH3OH under Ar shows an intense band at 572 nm (ϵ 4,100 M-1cm-1), which shifts to 590 nm (ϵ 2,860 M-1cm-1) by the addition of O2, and a new peak appeared at 781 nm (ϵ 790 M-1cm-1). Such a spectral change is not observed in CH2Cl2. Cyclic voltammogram (CV) of 1 in CH2Cl2 under Ar gives reversible redox waves assigned to Fe2+/Fe3+ and Fe3+/Fe4+ couples at -1.60 V (ΔE=69 mV) and -0.53 V (ΔE=71 mV) vs Fc/Fc+, respectively. In contrast, in CH3OH, the reversible redox waves, albeit accompanied by a positive shift of the Fe2+/Fe3+ couple, are observed at -1.20 V (ΔE=85 mV) and -0.53 V (ΔE=64 mV) vs Fc/Fc+ under Ar. Interestingly, a catalytic current was observed for the CV of 1 in CH3OH in the presence of CH3ONa under Ar, when the sweep rate was slowed down.

Sheet-Isolated MoS2 Used for Dispersing Pt Nanoparticles and its Application in Methanol Fuel Cells.

It is highly challenging to activate the basal plane and minimize the π-π stacking of MoS2 sheets, thus enhancing its catalytic performance. Here, we display an approach for making well-dispersed MoS2 . By using the N-doped multi-walled carbon nanotubes (NMWCNTs) as an isolation unit, the aggregation of MoS2 sheets was effectively reduced, favoring the dispersion of Pt nanoparticles (noted as Pt/NMWCNTs-isolated-MoS2 ). Excellent bifunctional catalytic performance for methanol oxidation and oxygen reduction reaction (MOR/ORR) were demonstrated by the produced Pt/NMWCNTs-isolated-MoS2 . In comparison to Pt nanoparticles supported on MoS2 (Pt/MoS2 ), the MOR activity (2314.14 mA mgpt -1 ) and stability (317.69 mA mgpt -1 after 2 h of operation) on Pt/NMWCNTs-isolatedMoS2 were 24 and 232 times higher, respectively. As for ORR, Pt/NMWCNTs-isolated-MoS2 holds large half-wave potential (0.88 V) and high stability (92.71 % after 22 h of operation). This work presents a tactic for activating the basal planes and reducing the π-π stacking of 2D materials to satisfy their applications in electrocatalysis. In addition, the proposed sheet-isolation method can be used for fabricating other 2D materials to promote the dispersion of nanoparticles, which assist its application in other fields of energy as well as the environment.

In situ Low-Energy Electron Microscopy of Chemical Waves on a Composite V-oxide/Rh(110) Surface.

Chemical wave patterns and V-oxide redistribution in catalytic methanol oxidation on a VOx/Rh(110) surface have been investigated in the 10-4 mbar range with low-energy electron microscopy (LEEM) and micro spot low-energy electron diffraction (micro-LEED) as in situ methods. V coverages of θV=0.2 and 0.4 MLE (monolayer equivalents) were studied. Pulses display a c(2×2) pattern in the reduced part and (1×2) and c(2×8) structures in the oxidized part of the surface. At θV=0.4 MLE (1×2)/(1×4) patterns with streaks along the [001]-direction at the 1/8 positions are present on the oxidized part of the surface. This phase can be assigned to V-oxide. On a tentative basis, an excitation mechanism for pulses is presented, Annealing the surface to 990 K under reaction conditions results in a macroscopic hole pattern in which holes of low VOx coverage are surrounded by a V-oxide layer. Chemical waves propagate inside the holes as well as on the VOx covered parts of the surface. The results demonstrate for the first time that also in supported oxidic overlayers selforganization processes can take place leading to chemical waves and a large scale redistribution of the oxide.

Atomically Dispersed CrOX on Pd Metallene for CO-Resistant Methanol Oxidation.

The effective design and construction of high-performance methanol oxidation reaction (MOR) electrocatalysts are significant for the development of direct methanol fuel cells. But the active sites of the MOR electrocatalysts are susceptible to being poisoned by CO, resulting in poor durability. Herein, we report an atomically dispersed CrOX species anchored on Pd metallene through bridging O atoms. This catalyst shows an outstanding MOR performance with 7 times higher mass activity and 100 mV lower CO electrooxidation potential than commercial Pd/C. The results of operando electrochemical Fourier transform infrared spectroscopy demonstrate the rapid removal of CO* on CrOX-Pd metallene. Theoretical calculations reveal that atomically dispersed CrOX can lower the adsorption energy of CO* on Pd sites and enhance that of OH* through the formation of a hydrogen bond, decreasing the formation energy of COOH*. This work provides a new strategy for improving MOR performance via atomically engineering oxide/metal interfaces.

The Role of Bismuth in Suppressing the CO Poisoning in Alkaline Methanol Electrooxidation: Switching the Reaction from the CO to Formate Pathway.

While tuning the electronic structure of Pt can thermodynamically alleviate CO poisoning in direct methanol fuel cells, the impact of interactions between intermediates on the reaction pathway is seldom studied. Herein, we contrive a PtBi model catalyst and realize a complete inhibition of the CO pathway and concurrent enhancement of the formate pathway in the alkaline methanol electrooxidation. The key role of Bi is enriching OH adsorbates (OHad) on the catalyst surface. The competitive adsorption of CO adsorbates (COad) and OHad at Pt sites, complementing the thermodynamic contribution from alloying Bi with Pt, switches the intermediate from COad to formate that circumvents CO poisoning. Hence, 8% Bi brings an approximately 6-fold increase in activity compared to pure Pt nanoparticles. This notion can be generalized to modify commercially available Pt/C catalysts by a microwave-assisted method, offering opportunities for the design and practical production of CO-tolerance electrocatalysts in an industrial setting.

Periodic Assembly of Diblock Pt-Au Heteronanowires for the Methanol Oxidation Reaction.

Periodic assembly of heterogeneous nanoparticles provides a strategy for integrating distinct nanocatalyst blocks where their synergic effects can be explored for diverse applications. To achieve the synergistic enhancement, an intimate clean interface is preferred which however is usually plagued by the bulky surfactant molecules used in the synthesis and assembly process. Herein, we showed the creation of one-dimensional Pt-Au nanowires (NWs) with periodic alternating Pt and Au nanoblocks, by assembling Pt-Au Janus nanoparticles with the assistance of peptide T7 (Ac-TLTTLTN-CONH2). It is demonstrated that the Pt-Au NWs showed much-improved performance in the methanol oxidation reaction (MOR), exhibiting 5.3 times higher specific activity and 2.5 times higher mass activity than the current state-of-the-art commercial Pt/C catalyst. In addition, the periodic heterostructure also improves the stability of Pt-Au NWs in the MOR, where the Pt-Au NWs retained 93.9% of their initial mass activity much higher than commercial Pt/C (30.6%).